牌号信息	LNP™ THERMOCOMP™ QF006 compound 物性表 PA610 & 沙特沙伯基础指导价格：暂无塑料库存：缺货	TECHNYL® eXten D 219WFC V30 BLACK 物性表 PA610 & 德国道默指导价格：暂无塑料库存： 1000kg
牌号简介	LNP ThermocompQF006是一种基于尼龙6/10树脂的化合物，含有30%的玻璃纤维。又称：lnpThermocomp化合物qf-1006产品再订购名称：qf006 LNP THERMOCOMP QF006 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber.	Technylexten D 219WFC V30黑色是一种聚酰胺6.10，用30%的玻璃纤维增强，有机稳定，用于注塑成型。水和食物接触认证。本产品有黑色可选。 TECHNYL eXten® D 219WFC V30 Black is a polyamide 6.10, reinforced with 30% of glass fibre, heat stabilized with organic stabilizers, for injection moulding. This grade offers lower water uptake, higher dimensional stability and enhanced chlorine resistance versus standard PA 6.6. It offers too an enhanced corrosion resistance, a reduction in lead levels versus standard metal solutions and an increase in ease of processing and part design freedom versus metal solutions and other plastics. It is used for cold and warm water plumbing components including, but not limited to, components in contact with drinking water systems globally where elevated levels of chlorine could be present.

产品描述
厂家：	沙特沙伯基础 SABIC	德国道默 DOMO
类别：	PA610 PA610	PA610 PA610
填料：	玻璃纤维 30	玻璃纤维 30
用途：		管道部件
性能特点：	防火阻燃等级HB HB	防火阻燃等级HB,耐腐蚀,熔体强度好,易加工,尺寸稳定性好,耐氯,食品接触 HB,Corrosion Resistant,Good melt strength,Excellent Processability,Good Dimensional Stability,Chlorine-resistant,Food contact compliance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ THERMOCOMP™ QF006 compound TECHNYL® eXten D 219WFC V30 BLACK 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ISO 62

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

密度
Density g/cm³ ISO 1183/A

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ISO 294-4

机械性能
MECHANICAL LNP™ THERMOCOMP™ QF006 compound TECHNYL® eXten D 219WFC V30 BLACK 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2/1A

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2/1A

冲击性能
IMPACT LNP™ THERMOCOMP™ QF006 compound TECHNYL® eXten D 219WFC V30 BLACK 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ THERMOCOMP™ QF006 compound TECHNYL® eXten D 219WFC V30 BLACK 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Af

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

阻燃性能
FLAMMABILITY LNP™ THERMOCOMP™ QF006 compound TECHNYL® eXten D 219WFC V30 BLACK 单位
UNIT 测试方法
TEST METHOD

灼热丝可燃性指数(1.6 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(1.60 mm)
Flame retardant level UL 94

阻燃等级(3.20 mm)
Flame retardant level UL 94

电气性能
ELECTRICAL LNP™ THERMOCOMP™ QF006 compound TECHNYL® eXten D 219WFC V30 BLACK 单位
UNIT 测试方法
TEST METHOD

介电强度(2 mm)
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm IEC 60093

相对电容率
Relative permittivity IEC 60250

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V IEC 60112

表面电阻率
Surface resistivity ohms IEC 60093

加工方式

注射 LNP™ THERMOCOMP™ QF006 compound TECHNYL® eXten D 219WFC V30 BLACK 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 80*10*4

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
电气性能
加工方式
注射
备注
返回顶部

PA610，LNP™ THERMOCOMP™ QF006 compound对比PA610，TECHNYL® eXten D 219WFC V30 BLACK对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别