PPO(PPE)+PS+PA，NORYL GTX™ GTX679 resin对比PPO(PPE)+PS+PA，NORYL GTX™ GTX985 resin物性表,价格行情_搜料

牌号信息	NORYL GTX™ GTX679 resin 物性表 PPO(PPE)+PS+PA & 沙特沙伯基础指导价格：暂无塑料库存：缺货	NORYL GTX™ GTX985 resin 物性表 PPO(PPE)+PS+PA & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	Noryl GTX GTX679树脂是聚苯醚（PPE）+聚酰胺（PA）树脂的混合物，填充矿物，导电，适用于注塑成型。导电率水平进行了优化，以减少底漆静电喷涂。GTX679提高了冲击/延伸率，矿物质含量使材料能够用于结构应用，取代金属或热固性树脂。这种材料只有黑色才有。 NORYL GTX GTX679 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to allow for primer-less electrostatic painting. GTX679 has improved impact/elongation and the mineral content enables the material to be used in structural applications replacing metal or thermoset resins. The material is only available in black.	NORYL GTX™ GTX985是一种18%的矿物填充材料。这种材料结合了高硬度和良好的耐温性和导电性的静电绘画。 NORYL GTX985 is a 18% mineral filled material. This material combines high stiffness and excellent temperature resistance with conductivity for electrostatic painting.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PPO(PPE)+PS+PA PPO(PPE)+PS+PA	PPO(PPE)+PS+PA PPO(PPE)+PS+PA
填料：	矿物	矿物 18
用途：	构件,金属取代
性能特点：	冲击性能好,导电,可表面喷涂 High impact resistance,Conductive,Sprayable	机械强度好,导电,可表面喷涂,耐高温 Good Rigidity,Conductive,Sprayable,High Heat Resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL NORYL GTX™ GTX679 resin NORYL GTX™ GTX985 resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792 , ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(220℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(280℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(280℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL NORYL GTX™ GTX679 resin NORYL GTX™ GTX985 resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲强度(断裂，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT NORYL GTX™ GTX679 resin NORYL GTX™ GTX985 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL NORYL GTX™ GTX679 resin NORYL GTX™ GTX985 resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831，ISO 11359-2

线性热膨胀系数(MD：23~60℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831，ISO 11359-2

线性热膨胀系数(TD：23~60℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ASTM D1525 10 , ISO 306/B50 10

维卡软化温度(B50)
Vicat Softening Temp ℃ ASTM D1525 11 , ISO 306/B50 11

电气性能
ELECTRICAL NORYL GTX™ GTX679 resin NORYL GTX™ GTX985 resin 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm 内部方法

加工方式

注射 NORYL GTX™ GTX679 resin NORYL GTX™ GTX985 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

建议注射量 NORYL GTX™ GTX679 resin NORYL GTX™ GTX985 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

2 5.0 mm/min

3 类型 1, 5.0 mm/min

4 1.3 mm/min

5 2.0 mm/min

6 Yield

7 80*10*4 sp=62mm

8 80*10*4

9 80*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)

2 5.0 mm/min

3 类型 1, 5.0 mm/min

4 1.3 mm/min

5 2.0 mm/min

6 Yield

7 80*10*4 sp=62mm

8 80*10*4

9 80*10*3

10 80*10*4 mm

11 标准 B (120°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
加工方式
注射
建议注射量
备注
返回顶部