PA610，LNP™ THERMOTUF™ QX01581H compound对比PA610，RTP 208B物性表,价格行情_搜料

牌号信息	LNP™ THERMOTUF™ QX01581H compound 物性表 PA610 & 沙特沙伯基础指导价格：暂无塑料库存：缺货	RTP 208B 物性表 PA610 & 美国RTP 指导价格：暂无塑料库存：缺货
牌号简介	LNP Thermotuf QX01581H是一种基于尼龙6/10树脂的含玻璃纤维化合物。这种材料的附加特性包括：高冲击性。又名：lnpThermotuf化合物PDX-Q-01581产品再订购名称：QX01581H LNP THERMOTUF QX01581H is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: High Impact. Also known as: LNP* THERMOTUF* Compound PDX-Q-01581 Product reorder name: QX01581H	警告：此材料的状态为“商业：限量发行”。此材料的数据最近尚未验证。在指定此等级之前，请联系RTP公司以获取当前信息。玻璃纤维增强尼龙6/10材料在强度、模量和挠曲温度方面提供了显著的改善。与其他尼龙材料相比，它们吸水性非常低，并且具有良好的尺寸稳定性和高物理强度。-每个RTP公司的初步产品数据- Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. Glass reinforced nylon 6/10 materials offer significant improvements in strength, moduli, and deflection temperature over the base resin. They have very low water absorption as compared to other nylon materials and exhibit excellent dimensional stability and high physical strengths. -Preliminary Product Data per RTP Co.-

产品描述
厂家：	沙特沙伯基础 SABIC	美国RTP
类别：	PA610 PA610	PA610 PA610
填料：	玻璃纤维	玻璃纤维
用途：
性能特点：	冲击性能好 High impact resistance	防火阻燃等级HB HB
加工条件：		注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ THERMOTUF™ QX01581H compound RTP 208B 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ASTM D792 , ISO 1183

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ISO 294-4

收缩率(MD：3.2 mm)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

机械性能
MECHANICAL LNP™ THERMOTUF™ QX01581H compound RTP 208B 单位
UNIT 测试方法
TEST METHOD

压缩强度
compressive strength MPa ASTM D695

弯曲强度
bending strength MPa ASTM D790

弯曲强度(--)
bending strength MPa ASTM D790

弯曲强度(--)
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

洛氏硬度(R 级)
Rockwell hardness ASTM D785

冲击性能
IMPACT LNP™ THERMOTUF™ QX01581H compound RTP 208B 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

装有测量仪表的落镖冲击(--)
Dart impact equipped with measuring instruments J ISO 6603-2

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ THERMOTUF™ QX01581H compound RTP 208B 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831，ISO 11359-2

电气性能
ELECTRICAL LNP™ THERMOTUF™ QX01581H compound RTP 208B 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant ASTM D150

介电强度
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

耐电弧性
Arc resistance sec ASTM D495

耗散因数(1 MHz)
Dissipation factor ASTM D150

阻燃性能
FLAMMABILITY LNP™ THERMOTUF™ QX01581H compound RTP 208B 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

加工方式

注射 LNP™ THERMOTUF™ QX01581H compound RTP 208B 单位测试方法

干燥时间 hr

干燥温度 °C

建议的最大回制料比例 %

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 80*10*4

4 80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注
返回顶部

PA610，LNP™ THERMOTUF™ QX01581H compound对比PA610，RTP 208B对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别