PPO(PPE)+PS+PA，NORYL GTX™ GTX6203 resin对比PPO(PPE)+PS+PA，NORYL GTX™ GTX4610 resin物性表,价格行情_搜料

牌号信息	NORYL GTX™ GTX6203 resin 物性表 PPO(PPE)+PS+PA & 沙特沙伯基础指导价格：47250.0元/吨塑料库存： 2350kg	NORYL GTX™ GTX4610 resin 物性表 PPO(PPE)+PS+PA & 沙特沙伯基础指导价格：58464.0元/吨塑料库存： 10850kg
牌号简介	Noryl GTX6203是一种20%滑石填充材料，具有优异的尺寸稳定性、良好的加工性能和表面外观。 NORYL GTX6203 is a 20% talc filled material with superior dimensional stability, excellent processability and surface appearance.	NORYL GTX™ GTX4610 resin是一种高性能、10%玻璃填充的PPE/PA混合物，具有良好的非卤化阻燃性、尺寸稳定性、高耐热性、强度和流动性平衡。该材料可用于注射成型，颜色有限。 NORYL GTX GTX4610 resin is a high performance, 10% glass filled blend of PPE/PA that exhibits an excellent balance of non-halogenated flame retardance, dimensional stability, high heat resistance, strength, and flow. The material is available in limited colors for injection molding.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PPO(PPE)+PS+PA PPO(PPE)+PS+PA	PPO(PPE)+PS+PA PPO(PPE)+PS+PA
填料：	滑石粉 20	玻璃纤维 10
用途：
性能特点：	易加工,表面光泽度好,尺寸稳定性好 Excellent Processability,Good surface appearance,Good Dimensional Stability	机械强度好,尺寸稳定性好,流动性高,无卤,阻燃,耐高温,防火阻燃等级V-1 Good Rigidity,Good Dimensional Stability,High liquidity,Halogen free,Flame Characteristics,High Heat Resistance,V-1
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL NORYL GTX™ GTX6203 resin NORYL GTX™ GTX4610 resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792 , ISO 1183

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

收缩率(TD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(280℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(300℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(280℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(300℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL NORYL GTX™ GTX6203 resin NORYL GTX™ GTX4610 resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ISO 527-2/5 , ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT NORYL GTX™ GTX6203 resin NORYL GTX™ GTX4610 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL NORYL GTX™ GTX6203 resin NORYL GTX™ GTX4610 resin 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ISO 8302

热变形温度(0.45 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Be

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

球压测试(125℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831，ISO 11359-2

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831，ISO 11359-2

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 10

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ASTM D1525 11 , ISO 306/B50 11

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306/B50 , ISO 306/B120

电气性能
ELECTRICAL NORYL GTX™ GTX6203 resin NORYL GTX™ GTX4610 resin 单位
UNIT 测试方法
TEST METHOD

介电强度(1.6 mm，在油中)
Dielectric strength kV/mm ASTM D149

介电强度(1.6 mm，在空气中)
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

相比漏电起痕指数
Compared to the leakage tracing index UL 746

高电弧燃烧指数(HAI)
High Arc Burning Index (HAI) UL 746

阻燃性能
FLAMMABILITY NORYL GTX™ GTX6203 resin NORYL GTX™ GTX4610 resin 单位
UNIT 测试方法
TEST METHOD

灼热丝可燃性指数(2.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(1 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级(0.80 mm)
Flame retardant level UL 94

阻燃等级(2.00 mm)
Flame retardant level UL 94

加工方式

注射 NORYL GTX™ GTX6203 resin NORYL GTX™ GTX4610 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

建议注射量 NORYL GTX™ GTX6203 resin NORYL GTX™ GTX4610 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

2 5.0 mm/min

3 类型 1, 5.0 mm/min

4 1.3 mm/min

5 2.0 mm/min

6 Yield

7 80*10*4 sp=62mm

8 80*10*4

9 120*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)

3 5.0 mm/min

4 类型 1, 5.0 mm/min

5 1.3 mm/min

6 2.0 mm/min

7 Yield

8 80*10*4 sp=62mm

9 80*10*4

10 80*10*4 mm

11 标准 B (120°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
建议注射量
备注
返回顶部