牌号信息	Celcon® GC25A 物性表 POM共聚 & 美国塞拉尼斯指导价格：暂无塑料库存：缺货	Tarnoform® 500 GF5 物性表 POM共聚 & 波兰Grupa 指导价格：暂无塑料库存：缺货
牌号简介	CELCON缩醛共聚物GC25A级是一种含25%增强纤维玻璃的玻璃耦合配方。该等级产品具有优异的强度、刚度和热变形温度，具有较低的模具收缩率、最小的热膨胀、良好的尺寸稳定性和良好的可塑性。符合ISO 1043-1的化学缩写：POM Celcon® acetal copolymer grade GC25A is a glass coupled formulation containing 25% reinforced fiber glass. This grade offers excellent strength, stiffness and heat distortion temperature with lower mold shrinkage, minimum thermal expansion, excellent dimensional stability and good moldability. Chemical abbreviation according to ISO 1043-1: POM	玻璃纤维增强注塑等级为25%，强度和刚度高，收缩率和线热膨胀系数小，成型时流动性高。 Tarnoform® 500 GF5 there is 25% glass fibres reinforced injection-moulding grade with high strength and stiffness and with reduced shrinkage and coefficient of linear thermal expansion, combined with higher flowability during moulding.

产品描述
厂家：	美国塞拉尼斯 Celanese	波兰Grupa
类别：	POM共聚 Copolymer Polyformaldehyde	POM共聚 Copolymer Polyformaldehyde
填料：	玻璃纤维 25	玻璃纤维 25
用途：		电气/电子应用领域,薄壁部件,家用货品,汽车领域的应用
性能特点：	机械强度好,易加工,尺寸稳定性好,收缩性低,化学耦合 Good Rigidity,Excellent Processability,Good Dimensional Stability,Low contractility,Chemical coupling	机械强度好,流动性高,收缩性低,防火阻燃等级HB Good Rigidity,High liquidity,Low contractility,HB
加工条件：		注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Celcon® GC25A Tarnoform® 500 GF5 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(MD：2.0 mm)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate % ASTM D955

收缩率(TD)
Shrinkage rate % ISO 294-4

收缩率(TD：2.0 mm)
Shrinkage rate % ISO 294-4

熔体体积流动速率(190℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL Celcon® GC25A Tarnoform® 500 GF5 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2/1A/5

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ISO 527-2/1A/5

拉伸强度(断裂，-40℃)
tensile strength MPa ASTM D638

拉伸强度(断裂，23℃)
tensile strength MPa ASTM D638

拉伸强度(断裂，71℃)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量
Tensile modulus MPa ISO 527-2/1A/1

球压硬度(H358/30)
Ball hardness MPa ISO 2039-1

冲击性能
IMPACT Celcon® GC25A Tarnoform® 500 GF5 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度
Charpy Notched Impact Strength kJ/m² ISO 179-1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Celcon® GC25A Tarnoform® 500 GF5 单位
UNIT 测试方法
TEST METHOD

Limit of Temperature(a few hours operation)
Limit of Temperature（a few hours operation） ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融峰值温度
Melting peak temperature ℃ ASTM D3418

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度
Vicat Softening Temp ℃ ISO 306/B

电气性能
ELECTRICAL Celcon® GC25A Tarnoform® 500 GF5 单位
UNIT 测试方法
TEST METHOD

介电常数(1 Hz)
Dielectric constant IEC 60250

介电强度(2 mm)
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm ASTM D257

体积电阻率
Volume resistivity ohms·cm IEC 60093

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V IEC 60112

耗散因数(1 Hz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Celcon® GC25A Tarnoform® 500 GF5 单位
UNIT 测试方法
TEST METHOD

燃烧速率
Burning rate mm/min FMVSS 302

阻燃等级(3.20 mm)
Flame retardant level UL 94

补充信息
Celcon® GC25A Tarnoform® 500 GF5 单位
UNIT 测试方法
TEST METHOD

ISO Type
ISO Type ISO 1874

加工方式

注射 Celcon® GC25A Tarnoform® 500 GF5 单位测试方法

保压 MPa

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大回制料比例 %

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

注射速度

背压 MPa

注射速度 Celcon® GC25A Tarnoform® 500 GF5 单位测试方法

备注

1 一般属性：这些不能被视为规格。

2 10°C/min

1 一般属性：这些不能被视为规格。

2 0.079 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
加工方式
注射
注射速度
备注
返回顶部

POM共聚，Celcon® GC25A对比POM共聚，Tarnoform® 500 GF5对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别