PA+PO，NEALID XW400H - 8229对比PA+PO，NEALID XG100物性表,价格行情_搜料

牌号信息	NEALID XW400H - 8229 物性表 PA+PO & 法国AD Majoris 指导价格：暂无塑料库存：缺货	NEALID XG100 物性表 PA+PO & 法国AD Majoris 指导价格：暂无塑料库存：缺货
牌号简介	Nealid XW400H-8229是一种40%玻璃纤维/矿物增强聚酰胺合金黑色，用于注塑成型。应用产品要求在热性能和机械性能之间有良好的结合。 NEALID XW400H-8229 is a 40 % glass fibre/mineral reinforced polyamide alloy black intended for injection moulding. APPLICATIONS Products requiring excellent combination between thermal and mechanical properties.	NEALID XG100是一种10%玻璃纤维增强聚酰胺合金，用于注塑成型。应用程序NEALID XG100已经开发出来，特别是在汽车工业和电气零件的要求非常苛刻的应用。要求热性能和机械性能结合良好的产品。NEALID XG100有黑色（NEALID XG100-8229）和天然色（NEALID XG100）两种颜色，但可根据要求提供其他颜色。 NEALID XG100 is a 10% glass fibre reinforced polyamide alloy intended for Injection moulding. APPLICATIONS NEALID XG100 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. NEALID XG100 is available in both black (NEALID XG100 - 8229) and natural (NEALID XG100) but other colours can be provided on request.

产品描述
厂家：	法国AD Majoris	法国AD Majoris
类别：	PA+PO PA + Olefins	PA+PO PA + Olefins
填料：	玻璃纤维/矿物 40	玻璃纤维 10
用途：		电气元件,汽车领域的应用
性能特点：	可回收,防火阻燃等级HB Renewable resources,HB	可回收,防火阻燃等级HB Renewable resources,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL NEALID XW400H - 8229 NEALID XG100 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

密度
Density g/cm³ ISO 1183

收缩率
Shrinkage rate %

机械性能
MECHANICAL NEALID XW400H - 8229 NEALID XG100 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-2

冲击性能
IMPACT NEALID XW400H - 8229 NEALID XG100 单位
UNIT 测试方法
TEST METHOD

简支梁无缺口冲击强度
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL NEALID XW400H - 8229 NEALID XG100 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度(DSC)
Melting temperature ℃ ISO 3146

阻燃性能
FLAMMABILITY NEALID XW400H - 8229 NEALID XG100 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

灼热丝可燃性指数(2.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

电气性能
ELECTRICAL NEALID XW400H - 8229 NEALID XG100 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm DIN 53482

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V IEC 60112

表面电阻率
Surface resistivity ohms DIN 53482

加工方式

注射 NEALID XW400H - 8229 NEALID XG100 单位测试方法

保压 MPa

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

注射速度

螺杆长径比

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
电气性能
加工方式
注射
备注
返回顶部

PA+PO，NEALID XW400H - 8229对比PA+PO，NEALID XG100对比物性表,价格行情_搜料_soliao