PBT，LNP™ FARADEX™ WX94736 compound对比PBT，VALOX™ V3500EX resin物性表,价格行情_搜料

牌号信息	LNP™ FARADEX™ WX94736 compound 物性表 PBT & 沙特沙伯基础指导价格：暂无塑料库存：缺货	VALOX™ V3500EX resin 物性表 PBT & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LNPFaradexWX94736是一种基于含不锈钢的PBT树脂的化合物。这种材料的附加特性包括：EMI/RFI屏蔽、导电。又名：lnpfaradex化合物PDX-W-94736产品再订购名称：WX94736 LNP* FARADEX* WX94736 is a compound based on PBT resin containing Stainless Steel. Added features of this material include: EMI/RFI Shielding, Electrically Conductive.	未填充PBT，阻燃，流动性好，在挤压应用（单丝，绝缘电缆），电气零件和连接器的断裂延伸率高 Unfilled PBT,Flame Retardant, good flow, high elongation at break for Extrusion applications (Monofilaments, Insulation Cables),Electrical Parts and Connectors

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PBT polybutylene terephthalate	PBT polybutylene terephthalate
填料：
用途：		单丝,电线电缆应用,电气元件,连接器
性能特点：	导电,电磁屏蔽,射频屏蔽 Conductive,EMI,RFI	易流动,阻燃,防火阻燃等级V-0 Good liquidity,Flame Characteristics,V-0
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ FARADEX™ WX94736 compound VALOX™ V3500EX resin 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³ ASTM D792, ISO 1183

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate %

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate %

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ISO 294-4

熔体体积流动速率(250℃，2.16 kg)
Melt Volume Rate cm³/10min

熔体体积流动速率(250℃，5 kg)
Melt Volume Rate cm³/10min

熔体体积流动速率(265℃，5 kg)
Melt Volume Rate cm³/10min

熔体表观粘度(260℃，1500 sec^-1)
Apparent viscosity of melt Pa·s ISO 11443

熔体质量流动速率(265℃，5.0kg)
Melt Flow Rate g/10min

熔体质量流动速率(266℃，5.0kg)
Melt Flow Rate g/10min

机械性能
MECHANICAL LNP™ FARADEX™ WX94736 compound VALOX™ V3500EX resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(--)
bending strength MPa ASTM D790

弯曲强度(--)
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

球压硬度(H358/30)
Ball hardness MPa ISO 2039-1

冲击性能
IMPACT LNP™ FARADEX™ WX94736 compound VALOX™ V3500EX resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(0℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(0℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m²

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/2C

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/2C

装有测量仪表的落镖冲击(--)
Dart impact equipped with measuring instruments J ISO 6603-2

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ FARADEX™ WX94736 compound VALOX™ V3500EX resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

球压测试(125℃)
Ball pressure test IEC 60695-10-2

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831，ISO 11359-2

线性热膨胀系数(MD：23~150℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：23~150℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度(A50)
Vicat Softening Temp ℃ ASTM D1525，ISO 306

维卡软化温度(B50)
Vicat Softening Temp ℃ ASTM D1525, ISO 306/B50, ISO 306/B120 17

电气性能
ELECTRICAL LNP™ FARADEX™ WX94736 compound VALOX™ V3500EX resin 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant ASTM D150，IEC 60250

介电强度(0.8 mm，在油中)
Dielectric strength kV/mm IEC 60243-1

介电强度(1.6 mm，在油中)
Dielectric strength kV/mm ASTM D149

介电强度(1.6 mm，在油中)
Dielectric strength kV/mm IEC 60243-1

介电强度(3.2 mm，在油中)
Dielectric strength kV/mm ASTM D149

介电强度(3.2 mm，在油中)
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm ASTM D257

体积电阻率
Volume resistivity ohms·cm ASTM D257，IEC 60093

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

耗散因数(1 MHz)
Dissipation factor ASTM D150，IEC 60250

表面电阻率
Surface resistivity ohms ASTM D257

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY LNP™ FARADEX™ WX94736 compound VALOX™ V3500EX resin 单位
UNIT 测试方法
TEST METHOD

0.80 mm
0.80 mm UL 94

加工方式

注射 LNP™ FARADEX™ WX94736 compound VALOX™ V3500EX resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

2 50 mm/min

3 80*10*4

4 80*10*4 mm

1 一般属性：这些不能被视为规格。

2 Tensile Bar

3 2.0 in/min

4 类型 1, 2.0 in/min

5 0.079 in/min

6 Yield

7 80*10*4 sp=62mm

8 80*10*4

9 80*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)

11 速率 A (50°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注