PA6，Ultramid® 8272G HS BK-102对比PA6，Nypel® RC6030F BK物性表,价格行情_搜料

牌号信息	Ultramid® 8272G HS BK-102 物性表 PA6 & 德国巴斯夫指导价格：暂无塑料库存：缺货	Nypel® RC6030F BK 物性表 PA6 & 德国巴斯夫指导价格：暂无塑料库存：缺货
牌号简介	Ultramid® 8272G HS BK-102 是一种12%的玻璃纤维增强、黑色颜料、热改性尼龙6吹塑复合材料，具有良好的工程性能和熔体强度的平衡，非常适合吹塑和其他需要超高熔体粘度的应用。与标准吹塑等级相比，它具有更高的强度、刚度和抗蠕变能力。优异的渗透性和对油、碳氢化合物和大多数溶剂的耐化学性，以及优异的刚度和为低成本的金属替代品制造复杂形状的能力。 Ultramid 8272G HS BK102 is a 12% glass fiber reinforced, black pigmented, thermally modified, PA6 blow molding compound offering an excellent balance of engineering properties combined with the melt strength ideally suited for blow molding and other applications requiring ultra high melt viscosity. It exhibits improved strength, stiffness and creep resistance compare to standard blow molding grades. Outstanding permeability and chemical resistance to oils, hydrocarbons and most solvents are other advantages along with excellent stiffness ad the ability to fabricate complex shapes for cost effective metal replacements. Applications Ultramid 8272G HS BK102 is designed for blow molding applications requiring improved short term thermal performance as well as extrusions. It is ideal for air ducts, reservoirs and covers.	Nypel® RC6030F BK是一种热稳定，30%玻璃纤维增强，黑色注塑级生产至少20%回收的PA6原料。本产品仅在北美地区提供。应用Nypel® RC6030F BK通常推荐用于螺栓、机架、汽车发动机罩下部件、压力调节器壳体和盖等应用。 Nypel RC6030F BK is a heat stabilized, 30% glass fiber reinforced, black injection molding grade produced with at least 20% recycled PA6 feedstock. This product is a regional grade available in North America only. Applications Nypel RC6030F BK is generally recommended for applications such as bolts, racks, automotive underhood components, pressure regulator housings and caps.

产品描述
厂家：	德国巴斯夫 BASF	德国巴斯夫 BASF
类别：	PA6 PA6	PA6 PA6
填料：	玻璃纤维 30	玻璃纤维 30
用途：		护罩,螺栓,外壳,支架,汽车的发动机罩下的零件
性能特点：	低翘曲性 Low warping	热稳定性好 Heat Stabilized
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Ultramid® 8272G HS BK-102 Nypel® RC6030F BK 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ISO 62

吸水率(24hr)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(平衡，50% RH)
Water absorption rate % ASTM D570

吸水率(饱和)
Water absorption rate % ASTM D570

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate %

冲击性能
IMPACT Ultramid® 8272G HS BK-102 Nypel® RC6030F BK 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL Ultramid® 8272G HS BK-102 Nypel® RC6030F BK 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融峰值温度
Melting peak temperature ℃ ASTM D3418

熔融温度(DSC)
Melting temperature ℃ ISO 3146

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃

电气性能
ELECTRICAL Ultramid® 8272G HS BK-102 Nypel® RC6030F BK 单位
UNIT 测试方法
TEST METHOD

体积电阻率(1.50 mm)
Volume resistivity ohms·cm ASTM D257

机械性能
MECHANICAL Ultramid® 8272G HS BK-102 Nypel® RC6030F BK 单位
UNIT 测试方法
TEST METHOD

弯曲强度(-40℃)
bending strength MPa ASTM D790

弯曲强度(121℃)
bending strength MPa ASTM D790

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量(-40℃)
Bending modulus MPa ASTM D790

弯曲模量(121℃)
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂，-40℃)
Tensile strain % ASTM D638

拉伸应变(断裂，-40℃)
Tensile strain % ISO 527-2

拉伸应变(断裂，120℃)
Tensile strain % ISO 527-2

拉伸应变(断裂，121℃)
Tensile strain % ASTM D638

拉伸应变(断裂，150℃)
Tensile strain % ISO 527-2

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(断裂，-40℃)
tensile strength MPa ASTM D638

拉伸强度(断裂，-40℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂，120℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂，121℃)
tensile strength MPa ASTM D638

拉伸强度(断裂，150℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂，23℃)
tensile strength MPa ASTM D638

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2

拉伸模量(-40℃)
Tensile modulus MPa ISO 527-2

拉伸模量(120℃)
Tensile modulus MPa ISO 527-2

拉伸模量(150℃)
Tensile modulus MPa ISO 527-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

拉伸模量(80℃)
Tensile modulus MPa ISO 527-2

洛氏硬度(R 级)
Rockwell hardness ASTM D785

加工方式

加工温度 Ultramid® 8272G HS BK-102 Nypel® RC6030F BK 单位测试方法

吹塑含水率 %

吹塑干燥温度干燥时间 hr

吹塑模具温度 ℃

吹塑熔体温度 ℃

注射 Ultramid® 8272G HS BK-102 Nypel® RC6030F BK 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

模具温度 °C

注塑压力 MPa

注射速度

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
机械性能
加工方式
加工温度
注射
备注
返回顶部