PC+ABS，PPR ABSPC01对比PC+ABS，Jamplast JPPCABSI物性表,价格行情_搜料

牌号信息	PPR ABSPC01 物性表 PC+ABS & 美国Premier Plastic 指导价格：暂无塑料库存：缺货	Jamplast JPPCABSI 物性表 PC+ABS & 美国Jamplast 指导价格：暂无塑料库存：缺货
牌号简介	PPR ABSPC01是一种聚碳酸酯+丙烯腈丁二烯苯乙烯(PC+ABS)产品,。它,在北美洲有供货。 PPR ABSPC01 is a Polycarbonate + ABS (PC+ABS) product. It is available in North America.	JPPCABSI工程树脂旨在提供冲击强度、耐热性和加工性能之间的平衡。它提供了比聚碳酸酯更好的加工性能，同时在室温和低温下提供了比ABS高的冲击强度。JPPCABSI在230°F的负载（264 psi，未调节）下的偏转温度，与ABS相比，还具有较高的耐热性。JPPCABSI工程树脂已用于汽车仪表板和内饰应用。 JPPCABSI engineering resin is designed to offer a balance of properties between impact strength, heat resistance and processability. It offers better processability than polycarbonate while offering high impact strength at both room and low temperatures compared to ABS. With a deflection temperature under load (264 psi, unannealed) of 230°F, JPPCABSI also offers high heat resistance compared to ABS. JPPCABSI engineering resin has been used in automotive instrument panel and interior trim applications.

产品描述
厂家：	美国Premier Plastic	美国Jamplast
类别：	PC+ABS PC+ABS	PC+ABS PC+ABS
填料：
用途：
性能特点：
加工条件：		共挤出成型

技术参数

物理性能
PHYSICAL PPR ABSPC01 Jamplast JPPCABSI 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate % ASTM D955

熔体质量流动速率(230℃，3.80kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL PPR ABSPC01 Jamplast JPPCABSI 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度(屈服)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(正切)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

冲击性能
IMPACT PPR ABSPC01 Jamplast JPPCABSI 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-40℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

装有测量仪表的落镖冲击(-29℃，3.18 mm，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，3.18 mm，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL PPR ABSPC01 Jamplast JPPCABSI 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，退火，3.18 mm)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD：-40~82℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

加工方式

注射 PPR ABSPC01 Jamplast JPPCABSI 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

注射速度 PPR ABSPC01 Jamplast JPPCABSI 单位测试方法

保压 MPa

垫层 mm

背压 MPa

备注

1 一般属性：这些不能被视为规格。

2 类型 1, 2.0 in/min

3 10 mil 缺口深度

4 11.1 ft/sec


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
注射速度
备注
返回顶部