ABS，MAGNUM™ 342 EZ对比ABS，CYCOLAC™ MG34LG resin物性表,价格行情_搜料

牌号信息	MAGNUM™ 342 EZ 物性表 ABS & 美国盛禧奥指导价格：暂无塑料库存：缺货	CYCOLAC™ MG34LG resin 物性表 ABS & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	概述：Magnum 342ez是标准的热ABS。它是一个可靠的和具有成本效益的解决方案，适用于一般覆盖的汽车内部应用。Magnum 342ez具有高流量特性，支持零件设计自由度。好处：批量到批量的一致性，允许从一开始就进行最佳的机器参数设置低VOC，允许更好的室内空气质量，面临越来越多的法规和原始设备制造商的限制。宽加工温度范围内的热稳定性：增强的零件设计自由度应用：通用覆盖的汽车内部应用中控台车门内衬座椅装饰件 Overview: MAGNUM 342EZ is a standard heat ABS. It is a reliable and cost effective solution for general covered interior automotive applications. MAGNUM 342EZ has high flow characteristics supporting part design freedom. Benefits: Lot to lot consistency allowing for optimal machine parameters settings from the start Low VOC allowing a better interior air quality facing increasing regulatory and OEMs constraints. Heat stability during wide range of processing temperatures: enhanced part design freedom Applications: General purpose covered interior automotive applications Mid-consoles Door liners Seat trims	汽车，低光泽ABS。 Automotive, low gloss ABS.

产品描述
厂家：	美国盛禧奥 Trinseo	沙特沙伯基础 SABIC
类别：	ABS ABS	ABS ABS
填料：
用途：	汽车领域的应用,汽车内部装备,构件,汽车外部装饰	汽车领域的应用
性能特点：	冲击性能好,流动性高,低光泽 High impact resistance,High liquidity,Low Gloss	低光泽 Low Gloss
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL MAGNUM™ 342 EZ CYCOLAC™ MG34LG resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

密度
Density g/cm³ ISO 1183-2

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

收缩率(TD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(220℃，10 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(200℃，3.80kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(230℃，3.80kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL MAGNUM™ 342 EZ CYCOLAC™ MG34LG resin 单位
UNIT 测试方法
TEST METHOD

Nominal strain at break
Nominal strain at break % ISO 527-2 2

弯曲强度
bending strength MPa ISO 178

弯曲强度(3.20 mm，注塑成型)
bending strength MPa ASTM D790

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(3.20 mm，注塑成型)
Bending modulus MPa ASTM D790

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2 2

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(屈服，3.20 mm，注塑成型)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2 2

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(屈服，3.20 mm，注塑成型)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(3.20 mm，注塑成型)
Tensile modulus MPa ASTM D638

冲击性能
IMPACT MAGNUM™ 342 EZ CYCOLAC™ MG34LG resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-18℃，3.2mm，注塑成型)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，3.2mm，注塑成型)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁冲击强度(-30℃)
Charpy impact strength ISO 179/1eU 2

简支梁冲击强度(23℃)
Charpy impact strength ISO 179/1eU 2

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA 2

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA 2

装有测量仪表的落镖冲击(23℃，3.20 mm，注塑成型，Peak Energy)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，3.20 mm，注塑成型，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL MAGNUM™ 342 EZ CYCOLAC™ MG34LG resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa)
Hot deformation temperature ℃ ISO 75-2 2

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa)
Hot deformation temperature ℃ ISO 75-2 2

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

球压测试(75℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2 2

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 10

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306 2

加工方式

注射 MAGNUM™ 342 EZ CYCOLAC™ MG34LG resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆压缩比

螺杆转速 rpm

螺杆长径比

锁模力 kN/cm²

备注

1 一般属性：这些不能被视为规格。

2 ??????,?? ISO 10350 ??? 23°C/50%r.h. ???

3 0.039 in/min

4 方法 I (三点负荷), 0.079 in/min

5 标准 B (120°C/h), 压力1 (10N)

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*4 sp=62mm

8 80*10*4

9 80*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
备注
返回顶部

ABS，MAGNUM™ 342 EZ对比ABS，CYCOLAC™ MG34LG resin对比物性表,价格行情_搜料_soliao