POM共聚，Celcon® GC25T对比POM共聚，Primocon GC25A物性表,价格行情_搜料

牌号信息	Celcon® GC25T 物性表 POM共聚 & 美国塞拉尼斯指导价格：暂无塑料库存：缺货	Primocon GC25A 物性表 POM共聚 & 美国KMI 指导价格：暂无塑料库存：缺货
牌号简介	Celcon® GC25T是一种25%的玻璃纤维偶联缩醛共聚物。它提供比标准Celcon GC25-A更高的强度。Celcon® GC25T是FDA批准的。Celcon® GC25T还特别耐燃油。它对运输燃料，特别是含氧燃料有很好的抵抗力。符合ISO 1043-1的化学缩写：POM Celcon® GC25T is a 25% glass fiber coupled acetal copolymer grade. It offers higher strength than the standard Celcon GC25-A. Celcon GC25T is FDA approved. Celcon GC25T is also exceptionally resistant to fuel. It offers excellent resistance to transportation fuels especially oxygenated fuels. Chemical abbreviation according to ISO 1043-1: POM	Primocon GC25A缩醛共聚物级，是一种含25%增强纤维玻璃的玻璃耦合配方。该等级产品具有优异的强度、刚度和热变形温度，具有较低的模具收缩率、最小的热膨胀、良好的尺寸稳定性和良好的可塑性。 Primocon GC25A Acetal Copolymer grade, is a glass coupled formulation containing 25% reinforced fiber glass. This grade offers excellent strength, stiffness and heat distortion temperature with lower mold shrinkage, minimum thermal expansion, excellent dimensional stability and good moldability.

产品描述
厂家：	美国塞拉尼斯 Celanese	美国KMI
类别：	POM共聚 Copolymer Polyformaldehyde	POM共聚 Copolymer Polyformaldehyde
填料：	玻璃纤维 25	玻璃纤维 25
用途：
性能特点：	机械强度好,化学耦合,耐燃油 Good Rigidity,Chemical coupling,Fuel resistance	机械强度好,易加工,尺寸稳定性好,共聚物 Good Rigidity,Excellent Processability,Good Dimensional Stability,Copolymer
加工条件：

技术参数

物理性能
PHYSICAL Celcon® GC25T Primocon GC25A 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate % ASTM D955

收缩率(TD)
Shrinkage rate % ISO 294-4

机械性能
MECHANICAL Celcon® GC25T Primocon GC25A 单位
UNIT 测试方法
TEST METHOD

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2/1A/5

拉伸强度(断裂)
tensile strength MPa ISO 527-2/1A/5

拉伸强度(断裂，23℃)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-2/1A/1

冲击性能
IMPACT Celcon® GC25T Primocon GC25A 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1e

热性能
THERMAL Celcon® GC25T Primocon GC25A 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

加工方式

注射 Celcon® GC25T Primocon GC25A 单位测试方法

保压 MPa

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

注射速度

背压 MPa

备注

1 一般属性：这些不能被视为规格。

2 10°C/min

1 一般属性：这些不能被视为规格。

2 10°C/min