PA66，TECHNYL® A R 218 V30 BLACK对比PA66，Durethan® AKV30GH2.0 900051 SR1物性表,价格行情_搜料

牌号信息	TECHNYL® A R 218 V30 BLACK 物性表 PA66 & 德国道默指导价格：暂无塑料库存： 1000kg	Durethan® AKV30GH2.0 900051 SR1 物性表 PA66 & 德国恩骅力指导价格：暂无塑料库存：缺货
牌号简介	Technyl AR 218 V30黑色是一种聚酰胺66，用30%的玻璃纤维增强，热稳定，用于注塑成型。它含有回收材料。本产品有黑色可选。 TECHNYL® AR 218 V30 Black is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection moulding. It contains recycled materials. This grade offers a good combination between thermal and mechanical properties.	PA 66，30%玻璃纤维，注塑成型，热老化稳定，改善表面光洁度 Durethan® AKV30GH2.0 900051 SR1 (Dry) PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, improved surface finish Durethan® AKV30GH2.0 900051 SR1 PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, improved surface finish Durethan® AKV30GH2.0 900051 SR1 PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, improved surface finish

产品描述
厂家：	德国道默 DOMO	德国恩骅力 Envalior
类别：	PA66 PA66	PA66 PA66
填料：	玻璃纤维 30	玻璃纤维 30
用途：	汽车领域的应用,汽车的发动机罩下的零件
性能特点：	防火阻燃等级HB,热稳定性好 HB,Heat Stabilized	表面光泽度好,热稳定性好 Good surface appearance,Heat Stabilized
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL TECHNYL® A R 218 V30 BLACK Durethan® AKV30GH2.0 900051 SR1 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ISO 62

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³

密度
Density g/cm³ ISO 1183/A

收缩率(MD：120℃，3.0 mm)
Shrinkage rate %

收缩率(MD：290℃，3.0 mm)
Shrinkage rate %

收缩率(TD：120℃，3.0 mm)
Shrinkage rate %

收缩率(TD：290℃，3.0 mm)
Shrinkage rate %

表观密度
Apparent density g/cm³

机械性能
MECHANICAL TECHNYL® A R 218 V30 BLACK Durethan® AKV30GH2.0 900051 SR1 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Bending strain %

弯曲强度(23℃)
bending strength MPa

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲强度(3.50% 应变，23℃)
bending strength MPa

弯曲模量(23℃)
Bending modulus MPa

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂，23℃)
Tensile strain %

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(断裂，23℃)
tensile strength MPa

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2/1A

拉伸模量(23℃)
Tensile modulus MPa

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2/1A

球压硬度
Ball hardness MPa

冲击性能
IMPACT TECHNYL® A R 218 V30 BLACK Durethan® AKV30GH2.0 900051 SR1 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击力峰值(-30℃)
Multi axial instrumented peak impact force N

多轴向仪器化冲击力峰值(23℃)
Multi axial instrumented peak impact force N

多轴向仪器化冲击能量(-30℃，冲击总贯穿能量)
Multi axial instrumented impact energy J

多轴向仪器化冲击能量(23℃，冲击总贯穿能量)
Multi axial instrumented impact energy J

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m²

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m²

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(-40℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL TECHNYL® A R 218 V30 BLACK Durethan® AKV30GH2.0 900051 SR1 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Af

热变形温度(8.0 MPa，未退火)
Hot deformation temperature ℃

熔融温度
Melting temperature ℃

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度
Vicat Softening Temp ℃

阻燃性能
FLAMMABILITY TECHNYL® A R 218 V30 BLACK Durethan® AKV30GH2.0 900051 SR1 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

US FMVSS302
US FMVSS302

极限氧指数
Extreme oxygen index %

极限氧指数
Extreme oxygen index % ISO 4589-2

灼热丝可燃性指数(1.6 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝可燃性指数(2.0 mm)
Glowing wire flammability index ℃

阻燃等级(1.50 mm)
Flame retardant level

电气性能
ELECTRICAL TECHNYL® A R 218 V30 BLACK Durethan® AKV30GH2.0 900051 SR1 单位
UNIT 测试方法
TEST METHOD

介电强度(23 ℃，1 mm)
Dielectric strength kV/mm

体积电阻率(23℃)
Volume resistivity ohms·cm

相对电容率(23℃，1 MHz)
Relative permittivity

相对电容率(23℃，100 Hz)
Relative permittivity

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V

耗散因数(23℃，1 MHz)
Dissipation factor

耗散因数(23℃，100 Hz)
Dissipation factor

表面电阻率
Surface resistivity ohms

补充信息
TECHNYL® A R 218 V30 BLACK Durethan® AKV30GH2.0 900051 SR1 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname

加工方式

注射 TECHNYL® A R 218 V30 BLACK Durethan® AKV30GH2.0 900051 SR1 单位测试方法

Residual Moisture Content % Karl Fisher

加工熔体温度 °C

干燥时间 - Dry Air Dryer hr

干燥温度 °C

干燥温度 - Dry Air Dryer °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2. 150x105x3mm, 4 hr

3. 150x105x3mm, 80°C MT, 500 bar

4. 2.0 mm/min

5. 2 mm/min

6. 10°C/min

7. 程序 A


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
电气性能
补充信息
加工方式
注射
备注
返回顶部