PA共聚，NYCOA Polyamide 2277 G30I对比PA共聚，ProPolymers PAA 4000物性表,价格行情_搜料

牌号信息	NYCOA Polyamide 2277 G30I 物性表 PA共聚 & 美国Nycoa 指导价格：暂无塑料库存：缺货	ProPolymers PAA 4000 物性表 PA共聚 & 美国ProPolymers 指导价格：暂无塑料库存：缺货
牌号简介	NYCOA 2277 G30I是一种30%玻璃纤维增强、冲击改性、尼龙共聚物树脂，用于注塑成型。与尼龙6相比，该等级具有优异的强度和刚度、尺寸稳定性和较低的熔点。NYCOA 2277 G30I还提供紫外线稳定等级，以及定制颜色。典型应用包括运动用品、电动工具外壳和草坪和花园设备部件。 NYCOA 2277 G30I is a 30% glass fiber reinforced, impact modified, Nylon Copolymer resin used for injection molding. This grade features excellent strength and stiffness, dimensional stability, and a lower melting point vs. Nylon 6. NYCOA 2277 G30I is also available in UV stable grades, as well as custom colors. Typical applications include sporting goods, power tool housing, and lawn & garden equipment parts.	30%玻璃纤维增强，抗水解，聚对苯二甲酸丁二醇酯 PAA 4000 is a 40% reinforced aromatic nylon copolymer. It has very high stiffness and strength similar to PPA. It can be processed in water heated tools and provides excellent surface finish. It is commonly used in metal and die cast replacement applications.

产品描述
厂家：	美国Nycoa	美国ProPolymers
类别：	PA共聚 PA Copolymer	PA共聚 PA Copolymer
填料：	玻璃纤维 30	玻璃纤维 30
用途：	电机外壳,草坪和园林设备,体育用品
性能特点：	机械强度好,耐候抗UV,冲击性能好,尺寸稳定性好,共聚物 Good Rigidity,Weather resistance is good,High impact resistance,Good Dimensional Stability,Copolymer	耐水解 Hydrolysis stability
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL NYCOA Polyamide 2277 G30I ProPolymers PAA 4000 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(TD)
Shrinkage rate % ASTM D955

冲击性能
IMPACT NYCOA Polyamide 2277 G30I ProPolymers PAA 4000 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-40℃，6.4 mm)
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁无缺口冲击强度(23℃，6.4 mm)
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-40℃，6.4mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，6.4mm)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL NYCOA Polyamide 2277 G30I ProPolymers PAA 4000 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

熔融温度
Melting temperature ℃ DSC

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

机械性能
MECHANICAL NYCOA Polyamide 2277 G30I ProPolymers PAA 4000 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
机械性能
加工方式
备注