PA9T，Genestar™ G1300H对比PA9T，Genestar™ G1302物性表,价格行情_搜料

牌号信息	Genestar™ G1300H 物性表 PA9T & 日本可乐丽指导价格：110250.0元/吨塑料库存： 50kg	Genestar™ G1302 物性表 PA9T & 日本可乐丽指导价格：暂无塑料库存：缺货
牌号简介	G1300H和G1350H适用于广泛的电气和电子元件，如UL94 HB可燃性等级，而G1302等级提供低摩擦。HB级不含含卤素阻燃剂。GW1458HF具有低翘曲和高流动性。‘无卤’遵循Br小于900ppm，Cl小于900ppm，卤素总量（Br和Cl）小于1500ppm的标准。 The G1300H and G1350H are suitable for use in a wide range of electrical and electronics components as UL94 HB flammability rating, while the G1302 grade delivers low friction. HB grades do not contain halogen-containing flame-retardants. The GW1458HF offers low warpage and high flow-ability. 'Halogen free' follows the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm.	G1300H和G1350H适用于广泛的电气和电子元件，如UL94 HB可燃性等级，而G1302等级提供低摩擦。HB级不含含卤素阻燃剂。GW1458HF具有低翘曲和高流动性。‘无卤’遵循Br小于900ppm，Cl小于900ppm，卤素总量（Br和Cl）小于1500ppm的标准。 The G1300H and G1350H are suitable for use in a wide range of electrical and electronics components as UL94 HB flammability rating, while the G1302 grade delivers low friction. HB grades do not contain halogen-containing flame-retardants. The GW1458HF offers low warpage and high flow-ability. 'Halogen free' follows the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm.

产品描述
厂家：	日本可乐丽 Kuraray	日本可乐丽 Kuraray
类别：	PA9T PA 9T	PA9T PA 9T
填料：	玻璃纤维 30	玻璃纤维 30
用途：	电气/电子应用领域,电气元件	电气/电子应用领域
性能特点：	无卤,防火阻燃等级HB Halogen free,HB	低摩擦系数,无卤,耐磨,防火阻燃等级HB Low coefficient of friction,Halogen free,Good wear resistance,HB
加工条件：

技术参数

物理性能
PHYSICAL Genestar™ G1300H Genestar™ G1302 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，40℃，95% RH)
Water absorption rate %

密度
Density g/cm³

收缩率(MD：1.0 mm)
Shrinkage rate %

收缩率(TD：1.00 mm)
Shrinkage rate %

熔体质量流动速率(320℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL Genestar™ G1300H Genestar™ G1302 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

冲击性能
IMPACT Genestar™ G1300H Genestar™ G1302 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL Genestar™ G1300H Genestar™ G1302 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

熔融温度
Melting temperature ℃

玻璃化转变温度
Glass transition temperature ℃

电气性能
ELECTRICAL Genestar™ G1300H Genestar™ G1302 单位
UNIT 测试方法
TEST METHOD

介电常数(10.0 GHz)
Dielectric constant ASTM D150

介电强度
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

相比漏电起痕指数
Compared to the leakage tracing index UL 746

耗散因数(10 GHz)
Dissipation factor ASTM D150

阻燃性能
FLAMMABILITY Genestar™ G1300H Genestar™ G1302 单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame retardant level UL 94

补充信息
Genestar™ G1300H Genestar™ G1302 单位
UNIT 测试方法
TEST METHOD

Weld Elongation
Weld Elongation % ASTM D638

Weld Strength
Weld Strength MPa ASTM D638

棒流动长度(320℃，500.0 µm)
Rod flow length cm

备注

1 一般属性：这些不能被视为规格。

2 96 hrs

3 750kgf

1 一般属性：这些不能被视为规格。

2 96 hrs

3 750kgf


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
加工方式
备注
返回顶部