PA66，TECHNYL® A 218 NATURAL对比PA66，Ultramid® A3W物性表,价格行情_搜料

牌号信息	TECHNYL® A 218 NATURAL 物性表 PA66 & 德国道默指导价格：38850.0元/吨塑料库存： 6000kg	Ultramid® A3W 物性表 PA66 & 德国巴斯夫指导价格：44625.0元/吨塑料库存： 25775kg
牌号简介	Technyl A 218 Natural是一种无增强聚酰胺66，标准粘度，热稳定注塑成型。它有天然颜色。 TECHNYL® A 218 Natural is an unreinforced polyamide 66, standard viscosity, heat stabilized for injection moulding. This grade offers all the primary properties of unreinforced polyamide 66. In addition, it has improved resistance to high temperature, and can be used for components which will withstand long-term temperature stresses	易流动，耐热老化的注塑级，可快速加工。用途包括高应力部件，如轴承，轴承保持架，齿轮，线圈架和电缆连接器 An easy flowing, heat aging resistant injection moulding grade for fast processing. Uses include highly stressed parts such as bearings, bearing cages, gear-wheels, coil formers and cable connectors.

产品描述
厂家：	德国道默 DOMO	德国巴斯夫 BASF
类别：	PA66 PA66	PA66 PA66
填料：
用途：		轴承,齿轮,连接器,车轮
性能特点：	热稳定性好,耐高温,耐化学性,防火阻燃等级V-2 Heat Stabilized,High Heat Resistance,Solvent resistance,V-2	耐老化,易流动,成型周期快,耐油 Good heat aging resistance,Good liquidity,Quick molding cycle,Grease resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL TECHNYL® A 218 NATURAL Ultramid® A3W 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ISO 62

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

密度
Density g/cm³ ISO 1183/A

熔体体积流动速率(270℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

粘度(0.5%，96％H2SO4)
Viscosity (0.5%, 96% H2SO4) cm³/g ISO 307, 1157, 1628

机械性能
MECHANICAL TECHNYL® A 218 NATURAL Ultramid® A3W 单位
UNIT 测试方法
TEST METHOD

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-1/2

拉伸应变(屈服，23℃)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-1/2

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-1-2

拉伸强度(屈服，23℃)
tensile strength MPa ASTM D638

拉伸强度(屈服，23℃)
tensile strength MPa ISO 527-2/1A

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2/1A

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2/1A

拉伸蠕变模量(1000hrs，应变<= 0.5％，23℃)
Tensile creep modulus (1000hs, strain<=0.5%, 23 ℃) MPa ISO 899-1

冲击性能
IMPACT TECHNYL® A 218 NATURAL Ultramid® A3W 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180A

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eU

热性能
THERMAL TECHNYL® A 218 NATURAL Ultramid® A3W 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K DIN 52612-1

最高使用温度(短周期)
Maximum operating temperature (short cycle) ℃

比热容
Specific heat capacity J/(kg·K)

温度指数(20000hrs，50％拉伸强度损失)
Temperature index ℃ IEC 60216

温度指数(5000hrs，50％拉伸强度损失)
Temperature index ℃ IEC 60216

热变形温度(0.45 MPa)
Hot deformation temperature ℃ ISO 75-1/2

热变形温度(1.8 MPa)
Hot deformation temperature ℃ ISO 75-1/2

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Af

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion E-6/K ISO 11359-1/-2

电气性能
ELECTRICAL TECHNYL® A 218 NATURAL Ultramid® A3W 单位
UNIT 测试方法
TEST METHOD

介电强度(2 mm)
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm IEC 60093

体积电阻率
Volume resistivity Ohm·m IEC 62631-3-1

相对电容率
Relative permittivity IEC 60250

相对电容率(1 MHz)
Relative permittivity IEC 62631-2-1

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V IEC 60112

相比漏电起痕指数(解决方案 B)
Compared to the leakage tracing index V IEC 60112

耗散因数
Dissipation factor IEC 60250

耗散因数(1 MHz)
Dissipation factor E-4 IEC 62631-2-1

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY TECHNYL® A 218 NATURAL Ultramid® A3W 单位
UNIT 测试方法
TEST METHOD

极限氧指数
Extreme oxygen index % ISO 4589-2

灼热丝可燃性指数(1.6 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

阻燃等级(0.80 mm)
Flame retardant level UL 94，IEC 60695

阻燃等级(1.60 mm)
Flame retardant level IEC 60695

阻燃等级(1.60 mm)
Flame retardant level UL 94

阻燃等级(3.20 mm)
Flame retardant level UL 94

加工方式

注射 TECHNYL® A 218 NATURAL Ultramid® A3W 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注
返回顶部