PP，Multi-Pro® 3010 X对比PP，Polyrocks 5003G15C物性表,价格行情_搜料

牌号信息	Multi-Pro® 3010 X 物性表 PP & 印度Multibase 指导价格：暂无塑料库存：缺货	Polyrocks 5003G15C 物性表 PP & 清远聚石指导价格：暂无塑料库存：缺货
牌号简介	Multi-Pro® 3010 X是一种聚丙烯产品,。它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。主要特性为:耐热。 Multi-Pro® 3010 X is a Polypropylene product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: heat resistant.	5003g（+）是以磷、溴、氮为阻燃剂的阻燃增强聚丙烯。通过固化相和气相机理提高阻燃性能，并通过催化机理加速熔滴，发挥阻燃性能。可燃性可达到UL94-V2（1.5mm和3.0mm），灼热丝试验符合GWIT:775/3.0和GWFI:850/3.0，具有成品密度低、机械性能好、烟度低、对模具腐蚀小等特点。 5003G(+) is flame retardant reinforced polypropylene with phosphorus, bromine and nitrogen as the flame retardant elements. Through solidifying phase and gas-phase mechanism improve flame retardant performance, and accelerating melting and dripping by catalytic mechanism to play flame retardant performance. The flammability can reach UL94-V2 (1.5mm and 3.0mm), glow-wire test meets GWIT:775/3.0 and GWFI:850/3.0, it has the characteristics of low density of finished products, good mechanical properties, low smoke, less corrosion to the mould etc.

产品描述
厂家：	印度Multibase	清远聚石 POLYROCKS
类别：	PP PP not specified	PP PP not specified
填料：
用途：		家电部件,构件,电气元件,电气/电子应用领域,插头,汽车内部零件
性能特点：	耐热性好 Heat Resistance, Good	低烟,阻燃,低密度 Low smoke,Flame Characteristics,Low density
加工条件：

技术参数

物理性能
PHYSICAL Multi-Pro® 3010 X Polyrocks 5003G15C 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL Multi-Pro® 3010 X Polyrocks 5003G15C 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

冲击性能
IMPACT Multi-Pro® 3010 X Polyrocks 5003G15C 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch kJ/m² ISO 180

热性能
THERMAL Multi-Pro® 3010 X Polyrocks 5003G15C 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

阻燃性能
FLAMMABILITY Multi-Pro® 3010 X Polyrocks 5003G15C 单位
UNIT 测试方法
TEST METHOD

灼热丝可燃性指数(3.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级(1.50 mm)
Flame retardant level

阻燃等级(3.00 mm)
Flame retardant level

加工方式

注射 Multi-Pro® 3010 X Polyrocks 5003G15C 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

备注

1 一般属性：这些不能被视为规格。

2、Phosphorus, Bromine and Nitrogen


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
备注
返回顶部