PC，Infino CF-1070对比PC，LEXAN™ EXL9414T resin物性表,价格行情_搜料

牌号信息	Infino CF-1070 物性表 PC & 韩国乐天尖端指导价格：42000.0元/吨塑料库存： 5000kg	LEXAN™ EXL9414T resin 物性表 PC & 沙特沙伯基础指导价格：76650.0元/吨塑料库存： 2975kg
牌号简介	手机外壳材料用高冲击材料 Infino CF-1070 is a Polycarbonate (PC) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Electrical/Electronic Applications. Primary characteristic: flame rated.	Lexan Exl9414T树脂LEXAN™ EXL9414T resin级是一种无卤阻燃聚碳酸酯，具有透明度、-40°C延展性和UL-94 V0等级，适用于注塑应用。卓越的冲击力、良好的流动性、透明的着色性以及薄壁火焰的可追溯性，使本产品成为薄壁应用的最佳候选产品。 LEXAN EXL9414T resin grade is a halogen-free flame retardant polycarbonate featuring transparency, -40 degree C ductility and UL-94 V0 rating for injection molding applications. Excellent impact combined with good flow, all transparent colorability for aesthetics and thin wall flame retradancy makes this product an excellent candidate for thin wall applications.

产品描述
厂家：	韩国乐天尖端 SAMSUNG	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：	手机	薄壁部件
性能特点：	冲击性能好,防火阻燃等级V-2 High impact resistance,V-2	冲击性能好,机械强度好-延展,易流动,无卤,阻燃,防火阻燃等级V-1,防火阻燃等级V-0 High impact resistance,Ductility,Good liquidity,Halogen free,Flame Characteristics,V-1,V-0
加工条件：		注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Infino CF-1070 LEXAN™ EXL9414T resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³ ASTM D792, ISO 1183

密度(-)
Density g/cm³ ISO 1183

密度()
Density g/cm³ ASTM D792

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(250℃，10.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(250℃，10.0kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL Infino CF-1070 LEXAN™ EXL9414T resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT Infino CF-1070 LEXAN™ EXL9414T resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，6.4mm)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL Infino CF-1070 LEXAN™ EXL9414T resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-40~95℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~95℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temp ℃ ASTM D1525, ISO 306/B120 11 16

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

阻燃性能
FLAMMABILITY Infino CF-1070 LEXAN™ EXL9414T resin 单位
UNIT 测试方法
TEST METHOD

极限氧指数
Extreme oxygen index % ISO 4589-2

阻燃等级(0.80 mm)
Flame retardant level UL 94

阻燃等级(1.50 mm)
Flame retardant level

阻燃等级(2.00 mm)
Flame retardant level

阻燃等级(2.50 mm)
Flame retardant level UL 94

阻燃等级(3.00 mm)
Flame retardant level UL 94

光学性能
OPTICAL Infino CF-1070 LEXAN™ EXL9414T resin 单位
UNIT 测试方法
TEST METHOD

透光率(2000 µm)
Transmittance % 内部方法

雾度(2000 µm)
Haze % 内部方法

加工方式

注射 Infino CF-1070 LEXAN™ EXL9414T resin 单位测试方法

射嘴温度 °C

干燥时间 hr

干燥时间-- hr

干燥时间热风干燥机 hr

干燥时间，最大 hr

干燥温度 °C

干燥温度-- °C

干燥温度热风干燥机 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

背压 MPa

螺杆转速 rpm

建议注射量 Infino CF-1070 LEXAN™ EXL9414T resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.11 in/min

4 0.079 in/min

5 Thickness: 4mm

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*3 sp=62mm

8 80*10*3

9 80*10*4 mm

10 速率 A (50°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
光学性能
加工方式
注射
建议注射量
备注
返回顶部

PC，Infino CF-1070对比PC，LEXAN™ EXL9414T resin对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别