技术参数
机械性能 MECHANICAL
LEXAN™ LUX7630C resin
LEXAN® RESIN EXRL0747
单位 UNIT
测试方法 TEST METHOD
弯曲强度
Flexural Strength
MPa
ISO 178
弯曲强度(屈服 yield, 1.3 mm/min)
Flexural Strength
MPa
ASTM D790
弯曲强度(屈服 yield, 2 mm/min)
Flexural Strength
MPa
ISO 178
弯曲强度(屈服,50 mm跨度)
Flexural Strength
MPa
ASTM D790
弯曲模量(1.3 mm/min)
Flexural Modulus
MPa
ASTM D790
弯曲模量(2 mm/min)
Flexural Modulus
MPa
ISO 178
弯曲模量(50 mm跨距)
Flexural Modulus
MPa
ASTM D790
拉伸应力(屈服 yield, 50 mm/min)
Tensile Stress
MPa
ASTM D638
拉伸应力(屈服 yield, 50 mm/min)
Tensile Stress
MPa
ISO 527
拉伸应力(断裂 break, 50 mm/min)
Tensile Stress
MPa
ASTM D638
拉伸应力(断裂 break, 50 mm/min)
Tensile Stress
MPa
ISO 527
拉伸应变(屈服 yield, 50 mm/min)
Tensile strain
%
ASTM D638
拉伸应变(屈服 yield, 50 mm/min)
Tensile strain
%
ISO 527
拉伸应变(屈服)
Tensile strain
%
ASTM D638
拉伸应变(屈服)
Tensile strain
%
ISO 527-2/50
拉伸应变(断裂 break, 50 mm/min)
Tensile strain
%
ASTM D638
拉伸应变(断裂 break, 50 mm/min)
Tensile strain
%
ISO 527
拉伸应变(断裂)
Tensile strain
%
ASTM D638
拉伸应变(断裂)
Tensile strain
%
ISO 527-2/50
拉伸强度(屈服)
tensile strength
MPa
ASTM D638
拉伸强度(屈服)
tensile strength
MPa
ISO 527-2/50
拉伸强度(断裂)
tensile strength
MPa
ASTM D638
拉伸强度(断裂)
tensile strength
MPa
ISO 527-2/50
拉伸模量
Tensile modulus
MPa
ASTM D638
拉伸模量
Tensile modulus
MPa
ISO 527-1-2
拉伸模量(1 mm/min)
Tensile Modulus
MPa
ISO 527
拉伸模量(50 mm/min)
Tensile Modulus
MPa
ASTM D638
冲击性能 IMPACT
LEXAN™ LUX7630C resin
LEXAN® RESIN EXRL0747
单位 UNIT
测试方法 TEST METHOD
多轴向仪器化冲击能量
Multiaxial Impact
J
ISO 6603
悬臂梁无缺口冲击强度(-30℃)
Izod Unnotched Impact strength
ISO 180/1U
悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength
ISO 180/1U
悬臂梁缺口冲击强度( 80*10*3 +23°C )
Izod Notched Impact strength
KJ/m²
ISO 180/1A
悬臂梁缺口冲击强度( 80*10*3 -30°C )
Izod Notched Impact strength
KJ/m²
ISO 180/1A
悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength
J/m
ASTM D256
悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength
ASTM D4812
悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength
ASTM D4812
简支梁无缺口冲击强度(-30℃)
Charpy Unnotched Impact strength
ISO 179/1eU
简支梁无缺口冲击强度(23℃)
Charpy Unnotched Impact strength
ISO 179/1eU
简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(-30℃,80*10*3 sp=62mm )
Charpy notched Impact strength
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(23℃,80*10*3 sp=62mm )
Charpy notched Impact strength
kJ/m²
ISO 179/1eA
装有测量仪表的落镖冲击(23℃,Total Energy)
Dart impact equipped with measuring instruments
J
ASTM D3763
热性能 THERMAL
LEXAN™ LUX7630C resin
LEXAN® RESIN EXRL0747
单位 UNIT
测试方法 TEST METHOD
热变形温度(0.45 MPa)
HDT
℃
ASTM D648
热变形温度(0.45 MPa)
HDT
℃
ISO 75/Be
热变形温度(0.45 MPa,未退火,100 mm跨距)
HDT
℃
ISO 75-2/Be
热变形温度(0.45 MPa,未退火,3.2 mm)
HDT
℃
ASTM D648
热变形温度(1.8 MPa)
HDT
℃
ASTM D648
热变形温度(1.8 MPa,未退火,100 mm跨距)
HDT
℃
ISO 75-2/Ae
热变形温度(1.8 MPa,未退火,3.2 mm)
HDT
℃
ASTM D648
热变形温度(1.82 MPa)
HDT
℃
ISO 75/Ae
相对温度指数(冲击机械性能)
Relative temperature index
℃
UL 746
相对温度指数(强度机械性能)
Relative temperature index
℃
UL 746
相对温度指数(机械冲击 Mech w/impact)
Relative Temperature Index
℃
UL-746B
相对温度指数(电气 Elec)
Relative Temperature Index
℃
UL-746B
相对温度指数(电气性能)
Relative temperature index
℃
UL 746
相对温度指数(非机械冲击 Mech w/o impact)
Relative Temperature Index
℃
UL-746B
线性热膨胀系数(-40℃~40℃,横向 xflow)
Coeff.of linear therm expansion
×10-5/℃
ASTM E831
线性热膨胀系数(-40℃~40℃,横向 xflow)
Coeff.of linear therm expansion
×10-5/℃
ISO 11359-2
线性热膨胀系数(-40℃~40℃,流动 flow)
Coeff.of linear therm expansion
×10-5/℃
ASTM E831
线性热膨胀系数(-40℃~40℃,流动 flow)
Coeff.of linear therm expansion
×10-5/℃
ISO 11359-2
线性热膨胀系数(MD:-40~40℃)
Coeff.of linear therm expansion
1/℃
ASTM E831
线性热膨胀系数(MD:23~80℃)
Coeff.of linear therm expansion
1/℃
ISO 11359-2
线性热膨胀系数(TD:-40~40℃)
Coeff.of linear therm expansion
1/℃
ASTM E831
线性热膨胀系数(TD:23~80℃)
Coeff.of linear therm expansion
1/℃
ISO 11359-2
维卡软化温度
Vicat Softening Temperature
℃
ASTM D1525 10
维卡软化温度(B/120)
Vicat Softening Temperature
℃
ISO 306
维卡软化温度(B/50)
Vicat Softening Temperature
℃
ASTM D1525
维卡软化温度(B/50)
Vicat Softening Temperature
℃
ISO 306
维卡软化温度(B120)
Vicat Softening Temperature
℃
ISO 306/B120
维卡软化温度(B50)
Vicat Softening Temperature
℃
ISO 306
物理性能 PHYSICAL
LEXAN™ LUX7630C resin
LEXAN® RESIN EXRL0747
单位 UNIT
测试方法 TEST METHOD
吸水率(23℃)
Water Absorption
%
ISO 62
吸水率(平衡,23℃,50% RH)
Water Absorption
%
ISO 62
吸水率(饱和,23℃)
Water Absorption
%
ISO 62
吸湿性(23℃。50%r.h.)
Moisture Absorption
%
ISO 62
密度
Density
g/cm³
ASTM D792
密度
Density
g/cm³
ISO 1183
成型收缩率(横向 xflow,3.2 mm)
Molding Shrinkage
%
内部
成型收缩率(流动 flow,3.2 mm)
Molding Shrinkage
%
内部
收缩率(MD:3.2 mm)
Shrinkage
%
内部方法
收缩率(TD:3.2 mm)
Shrinkage
%
内部方法
比重
Specific Gravity
ASTM D792
熔体体积流动速率(300℃,1.2 kg)
Melt Volume Rate
cm³/10min
ISO 1133
熔体质量流动速率( 300°C/1.2 kgf)
Melt Flow Rate
g/10min
ASTM D1238
熔体质量流动速率(300℃,1.20kg)
Melt Flow Rate
g/10min
ASTM D1238
耐候性
Weathering resistance
UL 746C
光学性能 OPTICAL
LEXAN™ LUX7630C resin
LEXAN® RESIN EXRL0747
单位 UNIT
测试方法 TEST METHOD
透光率(2.54 mm)
Light Transmission
%
ASTM D1003
透光率(2540 µm)
Light Transmission
%
ASTM D1003
电气性能 ELECTRICAL
LEXAN™ LUX7630C resin
LEXAN® RESIN EXRL0747
单位 UNIT
测试方法 TEST METHOD
介电常数(1.1 GHz)
Dielectric Constant
ASTM D150
介电常数(1.10 GHz)
Dielectric constant
ASTM ES7-83
介电强度(油 oil,0.8 mm)
Dielectric Strength
kV/mm
IEC 60243-1
介电强度(油 oil,1.6 mm)
Dielectric Strength
kV/mm
IEC 60243-1
介电强度(油 oil,3.2 mm)
Dielectric Strength
kV/mm
IEC 60243-1
体积电阻率
Volume Resistivity
ohm·cm
IEC 60093
热丝引燃(PLC 2)
Hot Wire Ignition
mm
UL 746A
热丝引燃(PLC 3)
Hot Wire Ignition
mm
UL 746A
耗散因数(1 GHz)
Dissipation Factor
ASTM D150
耗散因数(1.1 GHz)
Dissipation factor
ASTM ES7-83
高电压电弧起痕速率(PLC 0)
High Voltage Arc Track Rate
mm
UL 746A
阻燃性能 FLAMMABILITY
LEXAN™ LUX7630C resin
LEXAN® RESIN EXRL0747
单位 UNIT
测试方法 TEST METHOD
极限氧指数
Oxygen Index
%
ISO 4589-2
灼热丝可燃性指数(1.0 mm)
Glow Wire Flammability Index(GWFI)
℃
IEC 60695-2-12
灼热丝可燃性指数(3.0 mm)
Glow Wire Flammability Index(GWFI)
℃
IEC 60695-2-12
灼热丝起燃温度(1 mm)
Glow Wire Ignitability Temperature(GWIT)
℃
IEC 60695-2-13
灼热丝起燃温度(1.0 mm)
Glow Wire Ignitability Temperature(GWIT)
℃
IEC 60695-2-13
灼热丝起燃温度(3.0 mm)
Glow Wire Ignitability Temperature(GWIT)
℃
IEC 60695-2-13
紫外线、水暴露/浸泡 UV-light, water exposure/immersion
UV light, water exposure/immersion
UL 746C
阻燃等级(0.40 mm)
Flame Class Rating
UL 94
阻燃等级(1.00 mm)
Flame Class Rating
UL 94
阻燃等级(3.00 mm)
Flame Class Rating
UL 94
阻燃等级(≥0.4 mm)
Flame Class Rating
UL 94
阻燃等级(≥1 mm)
Flame Class Rating
UL 94
阻燃等级(≥3 mm)
Flame Class Rating
UL 94