PPA，LNP™ LUBRICOMP™ UFL36S compound对比PPA，LNP™ LUBRICOMP™ UFL36SXQ compound物性表,价格行情_搜料

牌号信息	LNP™ LUBRICOMP™ UFL36S compound 物性表 PPA & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LNP™ LUBRICOMP™ UFL36SXQ compound 物性表 PPA & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LNP Lubricomp UFL36S化合物LNP LubricompUFL36S是基于含玻璃纤维、聚四氟乙烯的聚邻苯二甲酰胺树脂的化合物。这种材料的附加特性包括：热稳定。也称为：LNPLubricomp化合物BGU产品再订购名称：UFL36SLNP Lubricomp UFL36S化合物LNP LubricompUFL36S是一种基于聚邻苯二甲酰胺树脂的化合物，含有30%的玻璃纤维、15%的聚四氟乙烯。这种材料的附加特性包括：热稳定，耐磨，轴承等级。又名：lnplubricomp复合BGU产品再订购名称：UFL36S LNP™ LUBRICOMP™ UFL36S compound LNP LUBRICOMP* UFL36S is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound BGU Product reorder name: UFL36S LNP™ LUBRICOMP™ UFL36S compound LNP LUBRICOMP* UFL36S is a compound based on Polyphthalamide resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant, Bearing Grade. Also known as: LNP* LUBRICOMP* Compound BGU Product reorder name: UFL36S	LNP* Lubricomp* UFL36SX是以聚邻苯二甲酰胺为基体，含有玻璃纤维和PETF的树脂。此材料主要优势是具有内部润滑功能和热稳定性好。 LNP* Lubricomp* UFL36SX是以聚邻苯二甲酰胺为基体，含有玻璃纤维和PETF的树脂。此材料主要优势是具有内部润滑功能和热稳定性好。

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PPA PPA	PPA PPA
填料：	PTFE/玻璃纤维 15:30	PTFE/玻璃纤维
用途：	轴承	汽车前灯,电气元件,轴承,皮带材料,燃料管线
性能特点：	润滑性,耐磨,热稳定性好 Lubricating,Good wear resistance,Heat Stabilized	机械强度好,硬度高,耐高温,润滑性,热稳定性好 Good Rigidity,Good Hardness,High Heat Resistance,Lubricating,Heat Stabilized
加工条件：	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ LUBRICOMP™ UFL36S compound LNP™ LUBRICOMP™ UFL36SXQ compound 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr，50% RH )
Water absorption rate % ASTM D570

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

垫圈磨损因素
Factors of gasket wear 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

摩擦系数(动态)
friction coefficient ASTM D3702

摩擦系数(静态)
friction coefficient ASTM D3702

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ISO 294

收缩率(MD：24 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ISO 294-4

机械性能
MECHANICAL LNP™ LUBRICOMP™ UFL36S compound LNP™ LUBRICOMP™ UFL36SXQ compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(1 mm/min)
Tensile modulus MPa ISO 527

拉伸模量(50 mm/min)
Tensile modulus MPa ASTM D638

摩擦系数(动态)
friction coefficient ASTM D3702 Modified

摩擦系数(静态)
friction coefficient ASTM D3702 Modified

磨损因数(Washer)
Wear factor 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified

冲击性能
IMPACT LNP™ LUBRICOMP™ UFL36S compound LNP™ LUBRICOMP™ UFL36SXQ compound 单位
UNIT 测试方法
TEST METHOD

仪表冲击能量峰值(23℃)
Instrument impact energy peak cm-kgf ASTM D 3763

多轴冲击
Multiaxial impact cm-kgf ISO 6603

多轴向仪器化冲击能量
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃，80*10*4)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，80*10*4)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ LUBRICOMP™ UFL36S compound LNP™ LUBRICOMP™ UFL36SXQ compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75/Af

加工方式

注射 LNP™ LUBRICOMP™ UFL36S compound LNP™ LUBRICOMP™ UFL36SXQ compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

注塑成型 LNP™ LUBRICOMP™ UFL36S compound LNP™ LUBRICOMP™ UFL36SXQ compound 单位测试方法

中段温度 ℃

前段温度 ℃

后段温度 ℃

干燥时间 hrs

干燥温度 ℃

最大水含量 %

模具温度 ℃

熔体温度 ℃

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 80*10*4

4 80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
注塑成型
备注
返回顶部

PPA，LNP™ LUBRICOMP™ UFL36S compound对比PPA，LNP™ LUBRICOMP™ UFL36SXQ compound对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别