PEI，LNP™ THERMOCOMP™ EC008PXQ compound对比PEI，LNP™ THERMOCOMP™ EC008APQ compound物性表,价格行情_搜料

牌号信息	LNP™ THERMOCOMP™ EC008PXQ compound 物性表 PEI & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LNP™ THERMOCOMP™ EC008APQ compound 物性表 PEI & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LNP™ THERMOCOMP™ EC008PXQ是一种基于含40%碳纤维的聚醚酰亚胺的化合物。附加功能包括：导电，特殊处理，符合FAR25.853。也称为：LNP™ THERMOCOMP™ EC008PXQ。产品再订购名称：EC008PXQ LNP* THERMOCOMP* EC008PXQ is a compound based on Polyetherimide containing 40% Carbon FIber. Added features include: Electrically Conductive, Exceptional Processing, FAR25.853 Compliant.	LNPThermocompEC008APQ是一种基于含40%碳纤维的聚醚酰亚胺的化合物。这种材料的附加特性包括：导电、高流量。符合FAR25.853。也称为：lnpThermocomp化合物EC008APQ产品再订购名称：EC008APQ LNP* THERMOCOMP* EC008APQ is a compound based on Polyetherimide containing 40% Carbon Fiber. Added features of this material include: Electrically Conductive, High Flow. FAR25.853 Compliant.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PEI Polyetherimide	PEI Polyetherimide
填料：	碳纤维 40	碳纤维 40
用途：
性能特点：	易加工,导电 Excellent Processability,Conductive	流动性高,导电 High liquidity,Conductive
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ THERMOCOMP™ EC008PXQ compound LNP™ THERMOCOMP™ EC008APQ compound 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

熔体质量流动速率(380℃，6.70kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT LNP™ THERMOCOMP™ EC008PXQ compound LNP™ THERMOCOMP™ EC008APQ compound 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ THERMOCOMP™ EC008PXQ compound LNP™ THERMOCOMP™ EC008APQ compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD：-40~150℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~150℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

电气性能
ELECTRICAL LNP™ THERMOCOMP™ EC008PXQ compound LNP™ THERMOCOMP™ EC008APQ compound 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm ASTM D257

表面电阻率
Surface resistivity ohms ASTM D257

机械性能
MECHANICAL LNP™ THERMOCOMP™ EC008PXQ compound LNP™ THERMOCOMP™ EC008APQ compound 单位
UNIT 测试方法
TEST METHOD

剪切强度
shear strength MPa ASTM C273

剪切模量
shear modulus MPa ASTM C273

压缩强度
compressive strength MPa 内部方法

弯曲强度
bending strength MPa ISO 178

弯曲强度(断裂，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

泊松比
Poisson's ratio ASTM D638

洛氏硬度(M 级)
Rockwell hardness ASTM D785

加工方式

注射 LNP™ THERMOCOMP™ EC008PXQ compound LNP™ THERMOCOMP™ EC008APQ compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 Break

7 80*10*4

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 80*10*4


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
机械性能
加工方式
注射
备注
返回顶部

PEI，LNP™ THERMOCOMP™ EC008PXQ compound对比PEI，LNP™ THERMOCOMP™ EC008APQ compound对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别