PA66，RTP 200 AR 15 TFE 5对比PA66，RTP 200 AR 10 HS物性表,价格行情_搜料

牌号信息	RTP 200 AR 15 TFE 5 物性表 PA66 & 美国RTP 指导价格：暂无塑料库存：缺货	RTP 200 AR 10 HS 物性表 PA66 & 美国RTP 指导价格：暂无塑料库存：缺货
牌号简介	警告：此材料的状态为“商业：限量发行”。此材料的数据最近尚未验证。在指定此等级之前，请联系RTP公司以获取当前信息。 Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade.	警告：此材料的状态为“商业：限量发行”。此材料的数据最近尚未验证。在指定此等级之前，请联系RTP公司以获取当前信息。RTP200AR系列是芳纶纤维增强尼龙6/6复合材料，具有优异的耐磨性和各向同性。 Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. The RTP 200 AR series are aramid fiber reinforced nylon 6/6 composites designed for exceptional wear and abrasion resistance along with isotropic properties.

产品描述
厂家：	美国RTP	美国RTP
类别：	PA66 PA66	PA66 PA66
填料：
用途：
性能特点：	润滑性,耐磨,防火阻燃等级HB Lubricating,Good wear resistance,HB	热稳定性好,防火阻燃等级HB Heat Stabilized,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL RTP 200 AR 15 TFE 5 RTP 200 AR 10 HS 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD：3.2 mm)
Shrinkage rate % ASTM D955

机械性能
MECHANICAL RTP 200 AR 15 TFE 5 RTP 200 AR 10 HS 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

摩擦系数(与金属 - 动态)
friction coefficient ASTM D1894

洛氏硬度(R 级)
Rockwell hardness ASTM D785

冲击性能
IMPACT RTP 200 AR 15 TFE 5 RTP 200 AR 10 HS 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL RTP 200 AR 15 TFE 5 RTP 200 AR 10 HS 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

电气性能
ELECTRICAL RTP 200 AR 15 TFE 5 RTP 200 AR 10 HS 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm ASTM D257

阻燃性能
FLAMMABILITY RTP 200 AR 15 TFE 5 RTP 200 AR 10 HS 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

加工方式

注射 RTP 200 AR 15 TFE 5 RTP 200 AR 10 HS 单位测试方法

干燥时间 hr

干燥温度 °C

建议的最大回制料比例 %

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

备注


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注
返回顶部

PA66，RTP 200 AR 15 TFE 5对比PA66，RTP 200 AR 10 HS对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别