PBT，Ultradur® B 4300 G6 LS High Speed BK15045对比PBT，POCAN® B 4235 Z 000000物性表,价格行情_搜料

牌号信息	Ultradur® B 4300 G6 LS High Speed BK15045 物性表 PBT & 德国巴斯夫指导价格：37800.0元/吨塑料库存： 3000kg	POCAN® B 4235 Z 000000 物性表 PBT & 德国朗盛指导价格：暂无塑料库存：缺货
牌号简介	Ultradur® B 4300 G6 LS High Speed BK15045是一种高流量、快速循环、低翘曲、30%玻璃填充、着色黑色、工业零件注射成型PBT、刚性坚固、尺寸稳定的应用。典型应用包括挡风玻璃雨刷器臂、印刷电路板、外壳、控制台、接触架、盖子。 Ultradur B 4300 G6 LS High Speed BK15045 is a high flow, fast cycling with low warpage, 30% glass filled, pigmented black, injection molding PBT for industrial parts, rigid tough and dimensional stable applications. Applications Typical applications include windshield wiper arms, printed circuit boards, housing, consoles, contact carriers, covers.	Pocan B 4235 Z 000000 PBT，30%玻璃纤维，注塑，阻燃，提高冲击强度 POCAN® B4235Z 000000 PBT, 30 % glass fibers, injection molding, flame retardant, improved impact strength POCAN® B4235Z 000000 PBT, 30 % glass fibers, injection molding, flame retardant, improved impact strength POCAN® B4235Z 000000 PBT, 30 % glass fibers, injection molding, flame retardant, improved impact strength

产品描述
厂家：	德国巴斯夫 BASF	德国朗盛 LANXESS
类别：	PBT polybutylene terephthalate	PBT polybutylene terephthalate
填料：	玻璃纤维 30	玻璃纤维 30
用途：	工业部件,汽车领域的应用,外壳,印刷电路板,保护性遮盖物
性能特点：	机械强度好,低翘曲性,韧性好,尺寸稳定性好,流动性高,成型周期快 Good Rigidity,Low warping,Good flexibility,Good Dimensional Stability,High liquidity,Quick molding cycle	冲击性能好,阻燃,防火阻燃等级V-2,防火阻燃等级V-0,防火阻燃等级5VA High impact resistance,Flame Characteristics,V-2,V-0,5VA
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Ultradur® B 4300 G6 LS High Speed BK15045 POCAN® B 4235 Z 000000 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

收缩率(MD：120℃，2.0 mm，2 hrs)
Shrinkage rate % ISO 294-4

收缩率(MD：250℃，2.0 mm)
Shrinkage rate % ISO 294-4

收缩率(TD：120℃，2.0 mm，2 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD：250℃，2.0 mm)
Shrinkage rate % ISO 294-4

熔体体积流动速率(250℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(260℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

粘度值(降低的粘度)
Viscosity value ml/g ISO 1628

表观密度
Apparent density g/cm³ ISO 60

机械性能
MECHANICAL Ultradur® B 4300 G6 LS High Speed BK15045 POCAN® B 4235 Z 000000 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Bending strain %

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178-A

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2/5

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2/5

拉伸模量(23℃)
Tensile modulus MPa ISO 527-1-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

球压硬度
Ball hardness MPa ISO 2039-1

热性能
THERMAL Ultradur® B 4300 G6 LS High Speed BK15045 POCAN® B 4235 Z 000000 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(8.0 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/C

熔融温度
Melting temperature ℃ ISO 11357-3

熔融温度(DSC)
Melting temperature ℃ ISO 3146

球压测试(210℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

冲击性能
IMPACT Ultradur® B 4300 G6 LS High Speed BK15045 POCAN® B 4235 Z 000000 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

电气性能
ELECTRICAL Ultradur® B 4300 G6 LS High Speed BK15045 POCAN® B 4235 Z 000000 单位
UNIT 测试方法
TEST METHOD

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V IEC 60112

阻燃性能
FLAMMABILITY Ultradur® B 4300 G6 LS High Speed BK15045 POCAN® B 4235 Z 000000 单位
UNIT 测试方法
TEST METHOD

灼热丝可燃性指数(2.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

阻燃等级(0.75 mm)
Flame retardant level UL 94

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(3.00 mm)
Flame retardant level UL 94

补充信息
Ultradur® B 4300 G6 LS High Speed BK15045 POCAN® B 4235 Z 000000 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname ISO 7792

加工方式

注射 Ultradur® B 4300 G6 LS High Speed BK15045 POCAN® B 4235 Z 000000 单位测试方法

Residual Moisture Content %

加工熔体温度 °C

干燥时间 hr

干燥时间 - 除湿干燥剂 hr

干燥温度 °C

干燥温度 - 除湿干燥剂 °C

建议的最大水分含量 %

模具温度 °C

注塑压力 MPa

注射速度

背压 MPa

备注

1 一般属性：这些不能被视为规格。

2 60x60x2mm, 80°C MT, 600 bar

3 60x60x2; WZ 80°C; 600 Bar

4 60x60x2

5 60x60x2mm

6 0.079 in/min

7 2 mm/min

8 Pull Rate: 2 mm/min; 50% RH

9 10°C/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
热性能
冲击性能
电气性能
阻燃性能
补充信息
加工方式
注射
备注