ABS，POLYLAC® PA-777C对比ABS，Lustran® Elite 1891物性表,价格行情_搜料

牌号信息	POLYLAC® PA-777C 物性表 ABS & 台湾奇美指导价格：暂无塑料库存：缺货	Lustran® Elite 1891 物性表 ABS & 瑞士英力士苯领指导价格：暂无塑料库存：缺货
牌号简介	高温、高冲击 High heat, High impact	Lustran® Elite 1891树脂是一种注射成型级的ABS（丙烯腈-丁二烯-苯乙烯），用于汽车市场的高温应用。它提供了高耐热性，低光泽，韧性，易于加工成型的彩色零件。特点SAE J1685:ABS011高耐热性低光泽易流动UL 94 HB额定应用AB柱门板控制台和控制台装饰灯外壳 Lustran® Elite 1891 resin is an injection molding grade of ABS (acrylonitrile butadiene styrene) for high-heat applications in the automotive market. It provides high heat resistance, low gloss, toughness, and easy flow for processing molded-in color parts. FEATURES SAE J1685: ABS0111 High heat resistance Low gloss Easy flow UL 94 HB rated APPLICATIONS AB pillars Door panels Console and console trim Lamp housings

产品描述
厂家：	台湾奇美 CHI MEI	瑞士英力士苯领 INEOS
类别：	ABS ABS	ABS ABS
填料：
用途：		汽车内部零件,汽车领域的应用
性能特点：	冲击性能好,耐高温,防火阻燃等级HB High impact resistance,High Heat Resistance,HB	韧性好,易流动,耐高温,低光泽,防火阻燃等级HB Good flexibility,Good liquidity,High Heat Resistance,Low Gloss,HB
加工条件：		注射成型 Injection Molding

技术参数

物理性能
PHYSICAL POLYLAC® PA-777C Lustran® Elite 1891 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率
Shrinkage rate % ISO 294-4

收缩率(MD)
Shrinkage rate % ASTM D955

熔体质量流动速率(220℃，10.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(220℃，10.0kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(230℃，3.80kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(230℃，3.80kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL POLYLAC® PA-777C Lustran® Elite 1891 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(5% 应变)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(屈服，23℃)
tensile strength MPa ASTM D638

拉伸强度(屈服，23℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

冲击性能
IMPACT POLYLAC® PA-777C Lustran® Elite 1891 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch kJ/m² ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(Area)
Impact strength of cantilever beam notch ASTM D256

落下冲击阻力(-30℃)
Falling impact resistance J/cm ASTM D4226

落下冲击阻力(23℃)
Falling impact resistance J/cm ASTM D4226

热性能
THERMAL POLYLAC® PA-777C Lustran® Elite 1891 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/A

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 2

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

阻燃性能
FLAMMABILITY POLYLAC® PA-777C Lustran® Elite 1891 单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame retardant level UL 94

阻燃等级(1.50 mm)
Flame retardant level UL 94

加工方式

Injection POLYLAC® PA-777C Lustran® Elite 1891 单位测试方法

干燥时间 hr

干燥温度 °C

模具温度 °C

螺杆压缩比

螺杆长径比

备注

3 2.0 mm/min

1 一般属性：这些不能被视为规格。

2 标准 B (120°C/h), 压力1 (10N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
Injection
备注
返回顶部