PP共聚，PROTEQ™ C15ST4对比PP共聚，PROTEQ™ C15ST4L物性表,价格行情_搜料

牌号信息	PROTEQ™ C15ST4 物性表 PP共聚 & 澳大利亚凯诺斯指导价格：暂无塑料库存：缺货	PROTEQ™ C15ST4L 物性表 PP共聚 & 澳大利亚凯诺斯指导价格：暂无塑料库存：缺货
牌号简介	PROTEQ™ C15ST4是一种中流量20%滑石填充热稳定级聚丙烯共聚物。它适用于使用温度升高且需要热老化稳定性的应用场合。注：字母“U”表示已添加紫外线稳定[即：Proteq C15UST4]。 PROTEQ™ C15ST4 is a medium flow 20% talc filled heat stabilised grade of polypropylene copolymer. It is intended for use in applications where elevated use temperatures occur and heat age stability is required. Note: The letter "U" indicate UV stabilisation has been added [ie: PROTEQ™ C15UST4].	PROTEQ™ C15ST4L是一种中等流量、冲击改性、20%滑石填充、热稳定级的聚丙烯共聚物。它适用于需要较高抗冲击性和热老化稳定性的应用场合。注：字母“U”表示已添加紫外线稳定[即：Proteq C15UST4]。 PROTEQ™ C15ST4L is a medium flow, impact modified, 20% talc filled, heat stabilised grade of polypropylene copolymer. It is intended for use in applications where relatively higher impact resistance and heat age stability is required. Note: The letter "U" indicate UV stabilisation has been added [ ie: PROTEQ™ C15UST4 ].

产品描述
厂家：	澳大利亚凯诺斯 Qenos	澳大利亚凯诺斯 Qenos
类别：	PP共聚 PP copolymer	PP共聚 PP copolymer
填料：	滑石粉 20	滑石粉 20
用途：
性能特点：	耐候抗UV,流动性中等,共聚物,热稳定性好,防火阻燃等级HB Weather resistance is good,Moderate liquidity,Copolymer,Heat Stabilized,HB	耐候抗UV,耐老化,冲击性能好,流动性中等,共聚物,热稳定性好,防火阻燃等级HB Weather resistance is good,Good heat aging resistance,High impact resistance,Moderate liquidity,Copolymer,Heat Stabilized,HB
加工条件：

技术参数

物理性能
PHYSICAL PROTEQ™ C15ST4 PROTEQ™ C15ST4L 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

收缩率(MD：3.0 mm)
Shrinkage rate % ASTM D955

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT PROTEQ™ C15ST4 PROTEQ™ C15ST4L 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL PROTEQ™ C15ST4 PROTEQ™ C15ST4L 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

阻燃性能
FLAMMABILITY PROTEQ™ C15ST4 PROTEQ™ C15ST4L 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

灼热丝起燃温度(1.6 mm)
Igniting temperature of the hot wire ℃ AS/NZS 60695

灼热丝起燃温度(1.6 mm)
Igniting temperature of the hot wire ℃ AS/NZS 60695.2.12

机械性能
MECHANICAL PROTEQ™ C15ST4 PROTEQ™ C15ST4L 单位
UNIT 测试方法
TEST METHOD

弯曲强度(3.20 mm)
bending strength MPa ASTM D790

弯曲模量(3.20 mm)
Bending modulus MPa ASTM D790

拉伸应变(断裂，3.20 mm)
Tensile strain % ASTM D638

拉伸强度(3.20 mm)
tensile strength MPa ASTM D638

邵氏硬度(邵氏 D)
Shore hardness ISO 868

邵氏硬度(邵氏 D，15 秒)
Shore hardness ISO 868

加工方式

注射 PROTEQ™ C15ST4 PROTEQ™ C15ST4L 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

注射速度

背压 MPa

螺杆转速 rpm

锁模力 kN/cm²

注射速度 PROTEQ™ C15ST4 PROTEQ™ C15ST4L 单位测试方法

背压 MPa

螺杆转速 rpm

锁模力 kN/cm²

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.39 in/min

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.39 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
阻燃性能
机械性能
加工方式
注射
注射速度
备注
返回顶部

PP共聚，PROTEQ™ C15ST4对比PP共聚，PROTEQ™ C15ST4L对比物性表,价格行情_搜料_soliao