PEI，LNP™ LUBRICOMP™ EX00548C compound对比PEI，LNP™ STAT-KON™ EX11402 compound物性表,价格行情_搜料

牌号信息	LNP™ LUBRICOMP™ EX00548C compound 物性表 PEI & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LNP™ STAT-KON™ EX11402 compound 物性表 PEI & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LNP™ LUBRICOMP™ EX00548C是一种基于含专有填料的聚醚酰亚胺树脂的化合物。这种材料的附加功能包括：清洁的复合系统，耐磨性。又名：lnplubricomp化合物PDX-E-00548 ccs产品再订购名称：ex00548c LNP* LUBRICOMP* EX00548C is a compound based on Polyetherimide resin containing Proprietary Fillers. Added features of this material include: Clean Compounding System, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PDX-E-00548 CCS Product reorder name: EX00548C	LNP stat-kon ex11402是一种基于含专用填料的聚醚酰亚胺树脂的化合物。这种材料的另一个特点是：导电。也称为：lnpstat-kon化合物ex11402产品再订购名称：ex11402 LNP STAT-KON EX11402 is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PEI Polyetherimide	PEI Polyetherimide
填料：	其他	其他
用途：
性能特点：	低离子含量,耐磨 Low (to None) Ion Content,Good wear resistance	导电 Conductive
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ LUBRICOMP™ EX00548C compound LNP™ STAT-KON™ EX11402 compound 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ISO 294-4

机械性能
MECHANICAL LNP™ LUBRICOMP™ EX00548C compound LNP™ STAT-KON™ EX11402 compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲强度(断裂，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LNP™ LUBRICOMP™ EX00548C compound LNP™ STAT-KON™ EX11402 compound 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ LUBRICOMP™ EX00548C compound LNP™ STAT-KON™ EX11402 compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(TD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

电气性能
ELECTRICAL LNP™ LUBRICOMP™ EX00548C compound LNP™ STAT-KON™ EX11402 compound 单位
UNIT 测试方法
TEST METHOD

表面电阻率
Surface resistivity ohms ASTM D257

加工方式

注射 LNP™ LUBRICOMP™ EX00548C compound LNP™ STAT-KON™ EX11402 compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 80*10*4

4 80*10*4 mm

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 80*10*4

7 80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
加工方式
注射
备注
返回顶部

PEI，LNP™ LUBRICOMP™ EX00548C compound对比PEI，LNP™ STAT-KON™ EX11402 compound对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别