PC，LEXAN™ 915AU resin对比PC，LEXAN™ Homopolymer 915AU物性表,价格行情_搜料

牌号信息	LEXAN™ 915AU resin 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LEXAN™ Homopolymer 915AU 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	聚碳酸酯915AU级树脂是一种阻燃聚碳酸酯，具有无溴化和无氯阻燃体系，具有良好的流动性和良好的紫外线稳定性。可提供透明色，以满足各种应用的WEEE/RoHS要求。 LEXAN resin grade 915AU is a flame retardant polycarbonate featuring non brominated and non chlorinated FR systems, with good flow, and good UV stability. It is available in transparent colors, intended to meet WEEE/RoHS requirements for various applications	聚碳酸酯915AU级树脂是一种阻燃聚碳酸酯，具有无溴化和无氯阻燃体系，具有良好的流动性和良好的紫外线稳定性。可提供透明色，以满足各种应用的WEEE/RoHS要求。 LEXAN resin grade 915AU is a flame retardant polycarbonate featuring non brominated and non chlorinated FR systems, with good flow, and good UV stability. It is available in transparent colors, intended to meet WEEE/RoHS requirements for various applications

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：		电器用具,电子显示器,电气/电子应用领域,非特定食品应用
性能特点：	耐候抗UV,易流动,无卤,阻燃,防火阻燃等级V-2,防火阻燃等级V-0 Weather resistance is good,Good liquidity,Halogen free,Flame Characteristics,V-2,V-0	耐候抗UV,易流动,无卤,阻燃 Weather resistance is good,Good liquidity,Halogen free,Flame Characteristics
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LEXAN™ 915AU resin LEXAN™ Homopolymer 915AU 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ASTM D792, ISO 1183

收缩率(MD)
Shrinkage rate %

收缩率(MD：3.2 mm)
Shrinkage rate %

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL LEXAN™ 915AU resin LEXAN™ Homopolymer 915AU 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LEXAN™ 915AU resin LEXAN™ Homopolymer 915AU 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/2C

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LEXAN™ 915AU resin LEXAN™ Homopolymer 915AU 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Be

热变形温度(1.8 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Ae

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831，ISO 11359-2

线性热膨胀系数(TD：-40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 12

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ASTM D1525, ISO 306/B50 12 19

阻燃性能
FLAMMABILITY LEXAN™ 915AU resin LEXAN™ Homopolymer 915AU 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.50 mm)
Flame retardant level

阻燃等级(3.00 mm)
Flame retardant level

光学性能
OPTICAL LEXAN™ 915AU resin LEXAN™ Homopolymer 915AU 单位
UNIT 测试方法
TEST METHOD

折射率
Refractive index ISO 489

透光率(2540 µm)
Transmittance % ASTM D1003

加工方式

注射 LEXAN™ 915AU resin LEXAN™ Homopolymer 915AU 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 Tensile Bar

3 0.20 in/min

4 类型 1, 2.0 in/min

5 0.051 in/min

6 0.079 in/min

7 Yield

8 80*10*3 sp=62mm

9 80*10*3

10 120*10*4 mm

11 标准 B (120°C/h), 载荷2 (50N)

3. Tensile Bar

4. 5.0 mm/min

5. 类型 1, 50 mm/min

6. 1.3 mm/min

7. 2.0 mm/min

8. at Yield

9. 80*10*3 sp=62mm

10. 80*10*3 mm

11. 120*10*4 mm

12. 速率 A (50°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
光学性能
加工方式
注射
备注
返回顶部

PC，LEXAN™ 915AU resin对比PC，LEXAN™ Homopolymer 915AU对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别