ABS，LNP™ LUBRICOMP™ AI001XXH compound对比ABS，LNP™ LUBRICOMP™ AL0039 compound物性表,价格行情_搜料

牌号信息	LNP™ LUBRICOMP™ AI001XXH compound 物性表 ABS & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LNP™ LUBRICOMP™ AL0039 compound 物性表 ABS & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	硅橡胶、RTV-1粘合和密封、可再生能源湿型垫圈、汽车和运输粘合和密封、粘合剂和密封剂粘合和密封、机械和工厂工程 Silicone Rubber, RTV-1 Bonding & Sealing, Renewable Energies Wet-Type Gaskets, Automotive & Transportation Bonding & Sealing, Adhesives and Sealants Bonding & Sealing, Mechanical and Plant Engineering	推荐应用：6926是一种UL QMTT2认可的组件产品，适用于THHW（以及TW和THW）75°C湿绝缘和105°C干绝缘产品。6926适用于1015型和MTW产品，适用于耐油I和II以及大众-1应用。本产品符合欧盟有害物质限制（RoHS）指令。 Recommended Applications: 6926 is a UL QMTT2 Recognized Component product rated for THHW (as well as TW and THW) 75 °C wet and 105 °C dry insulation products. 6926 is applicable for Style 1015 and MTW products, is rated for Oil Resistant I and II as well as VW-1 applications. This product complies with the European Union Restriction on Hazardous Substances (RoHS) directive

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	ABS ABS	ABS ABS
填料：
用途：	密封剂,粘合剂	电线电缆应用,耐潮湿级绝缘材料,汽车领域的应用
性能特点：
加工条件：		挤出 Extrusion

技术参数

物理性能
PHYSICAL LNP™ LUBRICOMP™ AI001XXH compound LNP™ LUBRICOMP™ AL0039 compound 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，50% RH)
Water absorption rate % ASTM D570

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate % ASTM D995

收缩率(MD：24 hrs)
Shrinkage rate %

收缩率(TD)
Shrinkage rate % ASTM D995

收缩率(TD：24 hrs)
Shrinkage rate %

机械性能
MECHANICAL LNP™ LUBRICOMP™ AI001XXH compound LNP™ LUBRICOMP™ AL0039 compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ASTM D790

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度(23℃)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

拉伸模量(23℃)
Tensile modulus MPa ASTM D638

摩擦系数(与自身 - 动态)
friction coefficient

摩擦系数(与自身 - 静态)
friction coefficient

磨损因数(Ring)
Wear factor 10^-10 in^5-min/ft-lb-hr

磨损因数(Washer)
Wear factor 10^-10 in^5-min/ft-lb-hr

热性能
THERMAL LNP™ LUBRICOMP™ AI001XXH compound LNP™ LUBRICOMP™ AL0039 compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(MD：-30~30℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(TD：-30~30℃)
Linear coefficient of thermal expansion 1/℃

冲击性能
IMPACT LNP™ LUBRICOMP™ AI001XXH compound LNP™ LUBRICOMP™ AL0039 compound 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(--)
Dart impact equipped with measuring instruments J ISO 6603-2

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

加工方式

注射 LNP™ LUBRICOMP™ AI001XXH compound LNP™ LUBRICOMP™ AL0039 compound 单位测试方法

加工熔体温度 °C

干燥时间 Hr

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

水份含量 %

注塑温度模具温度 °C

注塑温度螺筒中部温度 °C

注塑温度螺筒前部温度 °C

注塑温度螺筒后部温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 50% R.H

1 一般属性：这些不能被视为规格。

2 Unaged Dumbbells

3 F50


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
热性能
冲击性能
加工方式
注射
备注
返回顶部

ABS，LNP™ LUBRICOMP™ AI001XXH compound对比ABS，LNP™ LUBRICOMP™ AL0039 compound对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别