PC，LNP™ LUBRICOMP™ DFL38 compound对比PC，LNP™ LUBRICOMP™ DFL36P compound物性表,价格行情_搜料

牌号信息	LNP™ LUBRICOMP™ DFL38 compound 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LNP™ LUBRICOMP™ DFL36P compound 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LNPLubricompDFL38是一种基于聚碳酸酯树脂的化合物，含有40%的玻璃纤维和15%的聚四氟乙烯。这种材料的附加特征是：耐磨。又名：lnplubricomp化合物DFL-4038产品再订购名称：DFL38 LNP* LUBRICOMP* DFL38 is a compound based on Polycarbonate resin containing 40% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DFL-4038 Product reorder name: DFL38	LNPLubricompDFL36P是一种基于聚碳酸酯的化合物，含有30%的玻璃纤维和15%的聚四氟乙烯。这种材料的附加特性包括：特殊加工。耐磨。也称为：LNPLubricomp化合物DFL-4036 EP产品再订购名称：DFL36P LNP* LUBRICOMP* DFL36P is a compound based on Polycarbonate containing 30% Glass Fiber 15% PTFE. Added features of this material include: Exceptional Processing. Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DFL-4036 EP Product reorder name: DFL36P

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：	PTFE/玻璃纤维 15:40	PTFE/玻璃纤维 15:30
用途：
性能特点：	润滑性,耐磨 Lubricating,Good wear resistance	易加工,润滑性,耐磨 Excellent Processability,Lubricating,Good wear resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ LUBRICOMP™ DFL38 compound LNP™ LUBRICOMP™ DFL36P compound 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

机械性能
MECHANICAL LNP™ LUBRICOMP™ DFL38 compound LNP™ LUBRICOMP™ DFL36P compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲强度(断裂，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

摩擦系数(动态)
friction coefficient ASTM D3702 Modified

摩擦系数(静态)
friction coefficient ASTM D3702 Modified

磨损因数(Ring)
Wear factor 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified

磨损因数(Washer)
Wear factor 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified

冲击性能
IMPACT LNP™ LUBRICOMP™ DFL38 compound LNP™ LUBRICOMP™ DFL36P compound 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ LUBRICOMP™ DFL38 compound LNP™ LUBRICOMP™ DFL36P compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(TD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

加工方式

注射 LNP™ LUBRICOMP™ DFL38 compound LNP™ LUBRICOMP™ DFL36P compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 0,20 in/min

3 类型 1, 0,20 in/min

4 0,051 in/min

5 0,079 in/min

6 80*10*4

7 80*10*4 mm

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 80*10*4

7 80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
备注
返回顶部

PC，LNP™ LUBRICOMP™ DFL38 compound对比PC，LNP™ LUBRICOMP™ DFL36P compound对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别