聚烯烃，共挤薄膜用聚烯烃，PRE-ELEC® CP 1316对比聚烯烃，共挤薄膜用聚烯烃，PRE-ELEC® CP 1515物性表,价格行情_搜料

牌号信息	PRE-ELEC® CP 1316 物性表聚烯烃，共挤薄膜用聚烯烃 & 芬兰普宓斯指导价格：暂无塑料库存：缺货	PRE-ELEC® CP 1515 物性表聚烯烃，共挤薄膜用聚烯烃 & 芬兰普宓斯指导价格：暂无塑料库存：缺货
牌号简介	pre-eleccp 1316是一种基于聚烯烃共聚物的碳黑填充导电热塑性化合物。除了低电阻率。Pre-eleccp 1316具有良好的机械性能平衡，易于挤出或注塑成型。典型的应用包括柔性挤压型材或管与柔性注塑成型零件。pre-eleccp 1316也可以用10-30%的eva或pe-ld稀释。 PRE-ELEC®CP 1316 is a carbon black filled conductive thermoplastic compound based on polyolefin copolymer. In addition to a low electrical resistivity. PRE-ELEC®CP 1316 has an excellent balance of mechanical properties and is easy to extrude or injection mould. Typical applications include flexible extruded profiles or tubes together with flexible injection moulded parts. PRE-ELEC®CP 1316 may also be diluted with 10-30% of EVA or PE-LD.	PRE-ELEC® CP 1515是一种基于聚烯烃共聚物的碳黑填充导电热塑性化合物。除了低电阻率。PRE-ELEC® CP 1515具有良好的机械性能平衡，易于挤压。PRE-ELEC® CP 1515已经开发出来，特别是为块工艺泡沫。 PRE-ELEC® CP 1515 is a carbon black filled conductive thermoplastic compound based on polyolefin copolymer. In addition to a low electrical resistivity. PRE-ELEC® CP 1515 has an excellent balance of mechanical properties and is easy to extrude. PRE-ELEC® CP 1515 has been developed especially for block-process foams.

产品描述
厂家：	芬兰普宓斯 Premix Oy	芬兰普宓斯 Premix Oy
类别：	聚烯烃，共挤薄膜用聚烯烃聚烯烃，共挤薄膜用聚烯烃	聚烯烃，共挤薄膜用聚烯烃聚烯烃，共挤薄膜用聚烯烃
填料：
用途：	管件,型材	泡沫
性能特点：	易加工,导电 Excellent Processability,Conductive	易加工,导电 Excellent Processability,Conductive
加工条件：	挤出 Extrusion	挤出 Extrusion

技术参数

物理性能
PHYSICAL PRE-ELEC® CP 1316 PRE-ELEC® CP 1515 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD)
Shrinkage rate % ISO 294-4

熔体质量流动速率(190℃，21.6kg)
Melt Flow Rate g/10min ASTM D1238，ISO 1133

熔体质量流动速率(190℃，21.6kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(190℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238，ISO 1133

机械性能
MECHANICAL PRE-ELEC® CP 1316 PRE-ELEC® CP 1515 单位
UNIT 测试方法
TEST METHOD

弯曲模量(4 mm)
Bending modulus MPa ASTM D790

弯曲模量(4 mm)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638 , ISO 527-2

拉伸应变(断裂，4 mm)
Tensile strain % ISO 527-2

拉伸强度
tensile strength MPa ASTM D638 , ISO 527-2

拉伸强度(4 mm)
tensile strength MPa ISO 527-2

邵氏硬度(邵氏 A)
Shore hardness ASTM D2240 , ISO 868

邵氏硬度(邵氏 A)
Shore hardness ISO 868

邵氏硬度(邵氏 D)
Shore hardness ASTM D2240 , ISO 868

邵氏硬度(邵氏 D)
Shore hardness ISO 868

冲击性能
IMPACT PRE-ELEC® CP 1316 PRE-ELEC® CP 1515 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-20℃)
Notched impact strength of cantilever beam ISO 180

悬臂梁无缺口冲击强度(-20℃，4 mm)
Notched impact strength of cantilever beam ASTM D256

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ISO 180

悬臂梁无缺口冲击强度(23℃，4 mm)
Notched impact strength of cantilever beam ASTM D256

悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch ISO 180

悬臂梁缺口冲击强度(-20℃，4.00 mm)
Impact strength of cantilever beam notch ASTM D256

悬臂梁缺口冲击强度(-20℃，4mm)
Impact strength of cantilever beam notch ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch ISO 180

悬臂梁缺口冲击强度(23℃，4.00 mm)
Impact strength of cantilever beam notch ASTM D256

悬臂梁缺口冲击强度(23℃，4mm)
Impact strength of cantilever beam notch ASTM D256

悬臂梁缺口冲击强度(Area)
Impact strength of cantilever beam notch ASTM D256

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength ASTM D256

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength ISO 179

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength ISO 179 , ASTM D256

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ASTM D256

简支梁无缺口冲击强度(2℃)
Charpy Unnotch Impact strength ISO 179

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ASTM D256

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ASTM D256，ISO 179

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength ASTM D256

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength ISO 179 , ASTM D256

热性能
THERMAL PRE-ELEC® CP 1316 PRE-ELEC® CP 1515 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648-B

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648，ISO 75-2/B

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Bf

维卡软化温度(A50)
Vicat Softening Temp ℃ ASTM D1525，ISO 306

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

电气性能
ELECTRICAL PRE-ELEC® CP 1316 PRE-ELEC® CP 1515 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm 内部方法

表面电阻率
Surface resistivity ohms ESD STM11.11

表面电阻率
Surface resistivity ohms ESD STM11.11，IEC 61340-2-3

表面电阻率
Surface resistivity ohms IEC 61340-2-3

加工方式

注射 PRE-ELEC® CP 1316 PRE-ELEC® CP 1515 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

注塑压力 MPa

注射速度

挤出 PRE-ELEC® CP 1316 PRE-ELEC® CP 1515 单位测试方法

干燥时间 hr

干燥温度 °C

料筒1区温度 °C

料筒2区温度 °C

料筒3区温度 °C

料筒4区温度 °C

料筒5区温度 °C

备注

1 一般属性：这些不能被视为规格。

2 4 mm thickness

3 4 mm thick

4 速率 A (50°C/h), 载荷2 (50N)

1 一般属性：这些不能被视为规格。

2 4 mm thickness

3 4 mm thick

4 速率 A (50°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
加工方式
注射
挤出
备注
返回顶部