PA66，Celstran® PA66-GF20-02P11/12对比PA66，OnForce™ LFT NN-40LGF/000 HS UV Black物性表,价格行情_搜料

牌号信息	Celstran® PA66-GF20-02P11/12 物性表 PA66 & 美国塞拉尼斯指导价格：暂无塑料库存：缺货	OnForce™ LFT NN-40LGF/000 HS UV Black 物性表 PA66 & 美国普立万指导价格：暂无塑料库存：缺货
牌号简介	无铅无光表面轮廓挤压化合物。本产品符合欧盟有害物质限制（RoHS）指令。 Nylon 66 reinforced by 20 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.	普立万的长纤维热塑性（LFT）化合物是为要求高硬度和良好冲击的应用而配制的，如金属替换或其他结构应用。与标准短纤维产品相比，这些产品具有更高的物理和机械性能。LFT化合物的好处包括改善冲击强度、弹性模量和材料强度，范围从亚环境到高度升高。此外，与传统的高填充短纤维产品相比，LFT化合物在蠕变和疲劳性能方面提供了改进的性能，提高了尺寸稳定性，并表现出优异的表面光洁度。 PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. These products exhibit enhanced physical and mechanical properties versus standard short fiber products. Benefits of LFT compounds include improved impact strength, elastic modulus, and material strength across wide temperature ranges from subambient to highly elevated. Furthermore, LFT compounds have been shown to offer improved performance in the areas of creep and fatigue performance, improved dimensional stability, and exhibit an exceptional surface finish when compared to traditional highly filled short fiber products.

产品描述
厂家：	美国塞拉尼斯 Celanese	美国普立万 Polyone
类别：	PA66 PA66	PA66 PA66
填料：	长纤维填料 20	长纤维填料 40
用途：	型材
性能特点：	无铅 Lead content is low to none	耐候抗UV,热稳定性好 Weather resistance is good,Heat Stabilized
加工条件：	型材挤出成型 Profile extrusion

技术参数

物理性能
PHYSICAL Celstran® PA66-GF20-02P11/12 OnForce™ LFT NN-40LGF/000 HS UV Black 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

收缩率(--)
Shrinkage rate % ASTM D955

收缩率(--)
Shrinkage rate % ISO 294-4

机械性能
MECHANICAL Celstran® PA66-GF20-02P11/12 OnForce™ LFT NN-40LGF/000 HS UV Black 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ASTM D790

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲强度(80℃)
bending strength MPa ISO 178

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

弯曲模量(80℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2 , ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/1A/5

拉伸应变(断裂，-40℃)
Tensile strain % ISO 527-2

拉伸应变(断裂，100℃)
Tensile strain % ISO 527-2

拉伸应变(断裂，80℃)
Tensile strain % ISO 527-2/1A

拉伸强度(80℃)
tensile strength MPa ISO 527-2/1A

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/1A/5

拉伸强度(断裂，-40℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂，100℃)
tensile strength MPa ISO 527-2

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-2

拉伸模量(--)
Tensile modulus MPa ISO 527-2/1A/1

拉伸模量(80℃)
Tensile modulus MPa ISO 527-2/1A

冲击性能
IMPACT Celstran® PA66-GF20-02P11/12 OnForce™ LFT NN-40LGF/000 HS UV Black 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

落锤冲击
Drop hammer impact J ASTM D5420

热性能
THERMAL Celstran® PA66-GF20-02P11/12 OnForce™ LFT NN-40LGF/000 HS UV Black 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(8.0 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/C

熔融温度
Melting temperature ℃ ISO 11357-3

加工方式

注射 Celstran® PA66-GF20-02P11/12 OnForce™ LFT NN-40LGF/000 HS UV Black 单位测试方法

保压 MPa

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

注射速度

背压 MPa

注射速度 Celstran® PA66-GF20-02P11/12 OnForce™ LFT NN-40LGF/000 HS UV Black 单位测试方法

背压 MPa

备注

1 一般属性：这些不能被视为规格。

2 Measured on a tensile specimen. Actual mold shrinkage values are highly dependant on part geometry, mold configuration, and processing conditions.


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
注射速度
备注