PPO(PPE)+TPE，NORYL™ WCP921A resin对比PPO(PPE)+TPE，FLEX NORYL™ Resin WCP921A物性表,价格行情_搜料

牌号信息	NORYL™ WCP921A resin 物性表 PPO(PPE)+TPE & 沙特沙伯基础指导价格：暂无塑料库存：缺货	FLEX NORYL™ Resin WCP921A 物性表 PPO(PPE)+TPE & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	柔性Noryl注塑级。比重低，无卤阻燃性能好。开发用于二次成型应用，如插头、应变消除和连接器。UL 94 V-0性能，加工性好。绿色屏幕已批准。 Flexible NORYL injection molding grade. Low specific gravity with good non-halogenated flame retardant performance. Developed for overmolding applications such as plugs, strain reliefs, and connectors. UL 94 V-0 performance with good processability. GreenScreen Approved.	柔性Noryl注塑级。比重低，无卤阻燃性能好。开发用于二次成型应用，如插头、应变消除和连接器。UL 94 V-0性能，加工性好。绿色屏幕已批准。 Flexible NORYL injection molding grade. Low specific gravity with good non-halogenated flame retardant performance. Developed for overmolding applications such as plugs, strain reliefs, and connectors. UL 94 V-0 performance with good processability. GreenScreen Approved.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PPO(PPE)+TPE PPO(PPE)+TPE	PPO(PPE)+TPE PPO(PPE)+TPE
填料：
用途：	插头,包覆成型,疲劳消除用品,连接器	电气/电子应用领域
性能特点：	易加工,韧性好,无卤,阻燃,低密度,防火阻燃等级V-0 Excellent Processability,Good flexibility,Halogen free,Flame Characteristics,Low density,V-0	易加工,韧性好,无卤,阻燃,低密度 Excellent Processability,Good flexibility,Halogen free,Flame Characteristics,Low density
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL NORYL™ WCP921A resin FLEX NORYL™ Resin WCP921A 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

吸水率(23℃，48hr )
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD：24 hrs)
Shrinkage rate %

收缩率(TD：24 hrs)
Shrinkage rate %

熔体质量流动速率(210℃，5.0kg)
Melt Flow Rate g/10min

熔体质量流动速率(250℃，2.16kg)
Melt Flow Rate g/10min

热性能
THERMAL NORYL™ WCP921A resin FLEX NORYL™ Resin WCP921A 单位
UNIT 测试方法
TEST METHOD

脆化温度
Embrittlement temperature ℃ ASTM D746

电气性能
ELECTRICAL NORYL™ WCP921A resin FLEX NORYL™ Resin WCP921A 单位
UNIT 测试方法
TEST METHOD

介电强度(2 mm，在油中)
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm ASTM D257

相对电容率(1 MHz)
Relative permittivity IEC 60250

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

耗散因数(1 MHz)
Dissipation factor IEC 60250

阻燃性能
FLAMMABILITY NORYL™ WCP921A resin FLEX NORYL™ Resin WCP921A 单位
UNIT 测试方法
TEST METHOD

6.00 mm
6.00 mm UL 94

极限氧指数
Extreme oxygen index % ISO 4589-2

灼热丝可燃性指数(3.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

机械性能
MECHANICAL NORYL™ WCP921A resin FLEX NORYL™ Resin WCP921A 单位
UNIT 测试方法
TEST METHOD

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(100 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

邵氏硬度(邵氏 A，30 秒)
Shore hardness ASTM D2240

加工方式

注射 NORYL™ WCP921A resin FLEX NORYL™ Resin WCP921A 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

注射说明 NORYL™ WCP921A resin FLEX NORYL™ Resin WCP921A 单位测试方法

备注

1 一般属性：这些不能被视为规格。

2 Results measured at 48 hrs

3 类型 1, 2,0 in/min

4 0,49 in/min

2. 类型 1, 50 mm/min

3. 13 mm/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
热性能
电气性能
阻燃性能
机械性能
加工方式
注射
注射说明
备注
返回顶部