PC+ABS，PULSE™ EXT 100对比PC+ABS，Iupilon® MB2212R物性表,价格行情_搜料

牌号信息	PULSE™ EXT 100 物性表 PC+ABS & 美国盛禧奥指导价格：暂无塑料库存：缺货	Iupilon® MB2212R 物性表 PC+ABS & 日本三菱指导价格：暂无塑料库存：缺货
牌号简介	PULSE EXT 100 工程树脂拥有优秀的加工性能，在室温和低温下的高耐热和高抗冲击性能。 PULSE EXT 100 工程树脂应用于汽车外饰件。 PULSE™ EXT 100 engineering resin has been designed to provide excellent processability, high heat resistance, and high impact strength at room and low temperatures. PULSE EXT 100 engineering resin has been used in automotive plated and painted exterior trim applications. Applications: Front Grilles Wheel Covers and Center Caps Decorative Trim Name Plates and Badges	Iupilon® MB2212R是一种聚碳酸酯+丙烯腈丁二烯苯乙烯(PC+ABS)材料,。该产品在北美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 Iupilon® MB2212R的主要特性有: 阻燃/额定火焰高流动性 Iupilon® MB2212R is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupilon® MB2212R are: Flame Rated High Flow

产品描述
厂家：	美国盛禧奥 Trinseo	日本三菱 Mitsubishi
类别：	PC+ABS PC+ABS	PC+ABS PC+ABS
填料：
用途：	汽车外部零件,汽车领域的应用
性能特点：	易加工,冲击性能好,耐高温,耐低温冲击 Excellent Processability,High impact resistance,High Heat Resistance,low-temperature impact resistance	流动性高,防火阻燃等级HB High liquidity,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

机械性能
MECHANICAL PULSE™ EXT 100 Iupilon® MB2212R 单位
UNIT 测试方法
TEST METHOD

Nominal strain at break
Nominal strain at break % ISO 527-2 2

弯曲强度
bending strength MPa ISO 178

弯曲强度(屈服)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(屈服)
Tensile strain % ISO 527-2 2

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-2 2

拉伸模量
Tensile modulus MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-2 2

标称拉伸断裂应变
Nominal tensile fracture strain % ISO 527-2

冲击性能
IMPACT PULSE™ EXT 100 Iupilon® MB2212R 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁冲击强度(-30℃)
Charpy impact strength ISO 179/1eU 2

简支梁冲击强度(23℃)
Charpy impact strength ISO 179/1eU 2

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA 2

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA 2

装有测量仪表的落镖冲击(-29℃，3.20 mm，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，3.20 mm，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL PULSE™ EXT 100 Iupilon® MB2212R 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa)
Hot deformation temperature ℃ ISO 75-2 2

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa)
Hot deformation temperature ℃ ISO 75-2 2

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2 2

线性热膨胀系数(MD：-40~82℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306 2

物理性能
PHYSICAL PULSE™ EXT 100 Iupilon® MB2212R 单位
UNIT 测试方法
TEST METHOD

Melt Specific Heat
Melt Specific Heat J/kg/℃ ASTM C351

No Flow Temperature
No Flow Temperature ℃

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

密度
Density g/cm³ ISO 1183-2

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(TD：3.2 mm)
Shrinkage rate %

熔体体积流动速率(250℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(265℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体密度
Melt density g/cm³

熔体导热性
Melt thermal conductivity W/m/K ASTM C177

熔体质量流动速率(230℃，3.80kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(250℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

顶出温度
Ejection temperature ℃

阻燃性能
FLAMMABILITY PULSE™ EXT 100 Iupilon® MB2212R 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.50 mm)
Flame retardant level UL 94

加工方式

注射 PULSE™ EXT 100 Iupilon® MB2212R 单位测试方法

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 ??????,?? ISO 10350 ??? 23°C/50%r.h. ???

3 类型 1, 2.0 in/min

4 10 mil 缺口深度

5 11.1 ft/sec

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
机械性能
冲击性能
热性能
物理性能
阻燃性能
加工方式
注射
备注
返回顶部

PC+ABS，PULSE™ EXT 100对比PC+ABS，Iupilon® MB2212R对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别