LDPE，DINALEN® 50对比LDPE，DINALEN® 55物性表,价格行情_搜料

牌号信息	DINALEN® 50 物性表 LDPE & 克罗地亚DIOKI 指导价格：暂无塑料库存：缺货	DINALEN® 55 物性表 LDPE & 克罗地亚DIOKI 指导价格：暂无塑料库存：缺货
牌号简介	DINALEN® 50是不含添加剂的低密度聚乙烯。它主要用于吹塑和铸膜挤出，而其他加工技术可用于较小程度。DINALEN® 50具有很好的拉伸性能，拉伸膜的刚度、机械性能和光学性能平衡良好。DINALEN® 50在推荐的熔融温度范围160°C到180°C之间挤压。推荐的膜厚：0.025到0.060 mm。应用高光泽、高透明度、高硬度热收缩薄膜，将物理发泡剂挤出的泡沫与小直径管挤出电线、电缆护套注塑成型的厚壁制品、吹塑包装等浅层物体混合、共挤出，并与西服配套使用。聚烯烃级 DINALEN 50 is low density polyethylene containing no additives. It is primarily intended for blow and cast film extrusion while other processing techniques can be used to a lesser extent. DINALEN 50 exhibits very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film. DINALEN 50 is extruded at recommended melt temperature range between 160°C and 180° C. Recommended film thickness: 0.025 to 0.060 mm. Application Thin non-slippery film of high gloss and transparency Heat shrinkable film with excellent stiffness for industrial bundling Extruded foams with physical blowing agent Small diameter pipe extrusion Wire and cable sheathing Injection moulded thick-walled products Blown packaging and other shallow objects Mixing and co-extrusion with suitable polyolefin grades	DINALEN® 55是低密度聚乙烯，含有防滑和防堵塞添加剂。它主要用于吹塑和铸膜挤出，而其他加工技术可用于较小程度。DINALEN® 55具有很好的拉伸性能，拉伸膜的刚度、机械性能和光学性能平衡良好。DINALEN® 55在推荐的熔融温度范围160°C到180°C之间挤压。推荐的膜厚：0.25到0.05mm。应用高光泽度、高透明度的湿滑薄膜层压生产薄膜，适用于食品、卫生用品等各种初级软包装，适用于机场安检袋、DTK袋、冷藏袋、T恤袋、肩包、布林丁等多种运输袋的化学薄膜生产。g与Dinalen 50混合，以获得不太滑的薄膜混合，并与适当的i-聚丁烯-1级共挤出，以生产用于剥离系统的薄膜，并与适当的聚烯烃级混合和共挤出。 DINALEN® 55 is low density polyethylene containing slip and anti-blocking additives. It is primarily intended for blow and cast film extrusion while other processing techniques can be used to a lesser extent. DINALEN® 55 exhibits very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film. DINALEN® 55 is extruded at recommended melt temperature range between 160°C and 180°C. Recommended film thickness: 0.25 to 0.05mm. Application Thin slippery film of high gloss and transparency Production of film for lamination Production of film for a variety of primary flexible packaging like FFS for foodstuffs, sanitary articles, chemicals Film production for a many kinds of carrier-bags, like airport security bags, DTK bags, cooler-bags, T-shirt-bags, shoulder-bags Blending with DINALEN 50 to obtain a less slippery film Mixing and co-extrusion with suitable i-polybutene-1 grades to produce film for peel systems Mixing and co-extrusion with suitable polyolefin grades

产品描述
厂家：	克罗地亚DIOKI	克罗地亚DIOKI
类别：	LDPE LDPE	LDPE LDPE
填料：
用途：	管道系统,收缩性薄膜,包装,混合,流延薄膜,泡沫	袋子,薄膜,食品包装,混合,层压板
性能特点：	机械强度好,透光性好,表面光泽度好,易剥离,光学性能,热收缩性好 Good Rigidity,Good Clarity,Good surface appearance,Good dissection,Optical performance,Good thermal contraction	透光性好,表面光泽度好,高光滑性,光学性能,抗结块性 Good Clarity,Good surface appearance,Smoothness,Optical performance,High anti-blocking
加工条件：	共挤出成型	薄膜挤出 Film extrusion

技术参数

物理性能
PHYSICAL DINALEN® 50 DINALEN® 55 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

薄膜
DINALEN® 50 DINALEN® 55 单位
UNIT 测试方法
TEST METHOD

拉伸应变(MD，断裂，50 µm)
Tensile strain % ISO 527-3

拉伸应变(TD，断裂，50 µm)
Tensile strain % ISO 527-3

拉伸应变(断裂，模压成型)
Tensile strain % ISO 527-2

拉伸强度(MD，50 µm)
tensile strength MPa ISO 527-3

拉伸强度(TD，50 µm)
tensile strength MPa ISO 527-3

落锤冲击(50 µm)
Drop hammer impact g ISO 7765-1

薄膜厚度
film thickness

薄膜厚度(测试)
film thickness µm

裤型撕裂耐性(MD：50 µm)
Pant tear resistance N/mm ISO 6383-1

裤型撕裂耐性(TD：50 µm)
Pant tear resistance N/mm ISO 6383-1

热性能
THERMAL DINALEN® 50 DINALEN® 55 单位
UNIT 测试方法
TEST METHOD

熔融温度
Melting temperature ℃ ISO 11357-3

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

光学性能
OPTICAL DINALEN® 50 DINALEN® 55 单位
UNIT 测试方法
TEST METHOD

光泽度(20°，50 µm)
gloss ASTM D2457

光泽度(60°，50.0 µm)
gloss ASTM D2457

机械性能
MECHANICAL DINALEN® 50 DINALEN® 55 单位
UNIT 测试方法
TEST METHOD

拉伸强度(屈服，模压成型)
tensile strength MPa ISO 527-2

拉伸强度(断裂，模压成型)
tensile strength MPa ISO 527-2

拉伸模量(模压成型)
Tensile modulus MPa ISO 527-2

摩擦系数(与自身 - 动态)
friction coefficient ISO 8295

摩擦系数(与自身 - 静态)
friction coefficient ISO 8295

邵氏硬度(邵氏 D)
Shore hardness ISO 868

邵氏硬度(邵氏 D，模压成型)
Shore hardness ISO 868

加工方式

挤出 DINALEN® 50 DINALEN® 55 单位测试方法

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 Profile 2

1 一般属性：这些不能被视为规格。

2 Profile 2


相关资讯

牌号简介
产品描述
技术参数
物理性能
薄膜
热性能
光学性能
机械性能
加工方式
挤出
备注
返回顶部

LDPE，DINALEN® 50对比LDPE，DINALEN® 55对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别