PPO(PPE)+PS，NORYL™ RN0611 resin对比PPO(PPE)+PS，NORYL™ Resin FP5140物性表,价格行情_搜料

牌号信息	NORYL™ RN0611 resin 物性表 PPO(PPE)+PS & 沙特沙伯基础指导价格：暂无塑料库存：缺货	NORYL™ Resin FP5140 物性表 PPO(PPE)+PS & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	Noryl RN0611是一种基于消费后循环（PCR）的可注射成型改性聚苯醚树脂，包含至少30%的PCR苯乙烯系列树脂含量。该树脂具有良好的尺寸稳定性和高流动性，还使用了非氯化、非溴化的FR添加剂，比密度为1.1 g/cm^3。Noryl RN0611可能是平板电视外壳应用的优秀材料候选，要求具有良好的流变性能、耐热性、抗水解性和低密度。 NORYL RN0611 is an unfilled Post Consumer recycle (PCR) based injection moldable modified polyphenylene ether resin comprising at least 30% PCR styrenic series resin content. Designed for good dimensional stability and high flow, this resin also uses non-chlorinated, non-brominated FR additives with a specific density of 1.1 g/cm^3. NORYL RN0611 may be an excellent material candidate for flat panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance and low density.	Norylfp5140是一种未填充、注射成型的改性聚苯醚树脂，具有100摄氏度的ISO306 VICAT B/120。该树脂设计具有良好的尺寸稳定性和高流动性，该树脂还使用无氯化、无溴FR添加剂，在1.5毫米时达到v1-ul94额定值，比密度为1.1克/立方厘米。Noryl FP5140可能是平板电视外壳应用的优良材料，需要良好的流变性能、耐热性、抗水解性、低密度和薄的全阻燃性。 NORYLFP5140 is an unfilled, injection moldable modified polyphenylene ether resin with an ISO306 Vicat B/120 of 100 deg C. Designed for good dimensional stability and high flow, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating at 1.5mm with a specific density of 1.1g/cm3. NORYL FP5140 may be an excellent material for Flat Panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance, low density and thin all flame resistance

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PPO(PPE)+PS PPO(PPE)+PS	PPO(PPE)+PS PPO(PPE)+PS
填料：
用途：	电视外壳	电子显示器
性能特点：	尺寸稳定性好,流动性高,耐水解,无卤,阻燃,耐高温,低密度,防火阻燃等级V-1 Good Dimensional Stability,High liquidity,Hydrolysis stability,Halogen free,Flame Characteristics,High Heat Resistance,Low density,V-1
加工条件：	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL NORYL™ RN0611 resin NORYL™ Resin FP5140 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ASTM D792, ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(280℃，2.16 kg)
Melt Volume Rate cm³/10min

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min

机械性能
MECHANICAL NORYL™ RN0611 resin NORYL™ Resin FP5140 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain %

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain %

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT NORYL™ RN0611 resin NORYL™ Resin FP5140 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL NORYL™ RN0611 resin NORYL™ Resin FP5140 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，4.0 mm，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

热变形温度(1.8 MPa，退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 8

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ASTM D1525, ISO 306/B50 10 14

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

电气性能
ELECTRICAL NORYL™ RN0611 resin NORYL™ Resin FP5140 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant ASTM D150，IEC 60250

介电常数(1 MHz)
Dielectric constant ASTM D150

介电常数(1 MHz)
Dielectric constant IEC 60250

介电强度(1.6 mm，在油中)
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm ASTM D257

热丝引燃(HWI)
Hot wire ignition UL 746

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

相比漏电起痕指数
Compared to the leakage tracing index UL 746

耗散因数(1 MHz)
Dissipation factor ASTM D150，IEC 60250

耗散因数(1 MHz)
Dissipation factor ASTM D150

表面电阻率(--)
Surface resistivity ohms ASTM D257

表面电阻率(--)
Surface resistivity ohms IEC 60093

高电弧燃烧指数(HAI)
High Arc Burning Index (HAI) UL 746

阻燃性能
FLAMMABILITY NORYL™ RN0611 resin NORYL™ Resin FP5140 单位
UNIT 测试方法
TEST METHOD

极限氧指数
Extreme oxygen index % ISO 4589-2

灼热丝可燃性指数(3.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(1 mm)
Igniting temperature of the hot wire ℃

灼热丝起燃温度(2 mm)
Igniting temperature of the hot wire ℃

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃

阻燃等级(1.50 mm)
Flame retardant level UL 94

加工方式

注射 NORYL™ RN0611 resin NORYL™ Resin FP5140 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 2,0 in/min

3 0,051 in/min

4 0,079 in/min

5 Yield

6 80*10*4 sp=62mm

7 80*10*4

8 80*10*4 mm

9 标准 B (120°C/h), 载荷2 (50N)

3. 50 mm/min

4. 2.0 mm/min

5. at Yield

6. 80*10*4 sp=62mm

7. 80*10*4 mm

8. 速率 A (50°C/h), 载荷2 (50N)

9. Surface


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注