PC，HOPELEX PCN-2004对比PC，LEXAN™ ML6411 resin物性表,价格行情_搜料

牌号信息	HOPELEX PCN-2004 物性表 PC & 韩国乐天指导价格：暂无塑料库存：缺货	LEXAN™ ML6411 resin 物性表 PC & 沙特沙伯基础指导价格：46200.0元/吨塑料库存： 30850kg
牌号简介	易脱模无溴、无氯阻燃剂，仅提供不透明颜色。 Easy mold release Non-brominated, non-chlorinated flame retardant Available in opaque color only	Lexan ML6411树脂Lexan ML6411聚碳酸酯（PC）硅氧烷树脂，是一种高流动性不透明注塑成型（IM）级，具有极低的温度延性特性。该等级提供基于无氯、无溴阻燃系统的UL94V0@1.5mm和5VA@3.0mm阻燃性。与标准PC相比，LEXAN™ ML6411 resin具有出色的加工特性，有机会缩短IM周期。该产品有多种不透明颜色，是广泛电气应用的理想选择。 LEXAN ML6411 polycarbonate (PC) siloxane resin, is a high flow opaque injection molding (IM) grade with very low temperature ductility characteristics. This grade offers UL94 V0 @ 1.5mm and 5VA @ 3.0mm flame retardancy based on non-chlorine, non-bromine FR systems. LEXAN ML6411 resin offers excellent processing characteristics with opportunity for shorter IM cycle times compared to standard PC. This product is available in a wide range of opaque colors and is an excellent candidate for a wide range of electrical applications.

产品描述
厂家：	韩国乐天 LOTTE	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：	电器外壳	电气/电子应用领域
性能特点：	无卤,含脱模剂,阻燃,防火阻燃等级V-0 Halogen free,Good stripping performance,Flame Characteristics,V-0	易加工,流动性高,机械强度好-延展,成型周期快,无卤,阻燃,防火阻燃等级V-0,防火阻燃等级5VA,防火阻燃等级5VB Excellent Processability,High liquidity,Ductility,Quick molding cycle,Halogen free,Flame Characteristics,V-0,5VA,5VB
加工条件：		注射成型 Injection Molding

技术参数

物理性能
PHYSICAL HOPELEX PCN-2004 LEXAN™ ML6411 resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(260℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(260℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(300℃，1.2kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL HOPELEX PCN-2004 LEXAN™ ML6411 resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(屈服)
bending strength MPa ASTM D790

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT HOPELEX PCN-2004 LEXAN™ ML6411 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL HOPELEX PCN-2004 LEXAN™ ML6411 resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Be

热变形温度(0.45 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Ae

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

球压测试(125℃)
Ball pressure test IEC 60695-10-2

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746

相对温度指数(强度机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 9

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

阻燃性能
FLAMMABILITY HOPELEX PCN-2004 LEXAN™ ML6411 resin 单位
UNIT 测试方法
TEST METHOD

灼热丝可燃性指数(1.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(1 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

灼热丝起燃温度(2 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级(1.00 mm)
Flame retardant level UL 94

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(2.00 mm)
Flame retardant level UL 94

阻燃等级(3.00 mm)
Flame retardant level UL 94

电气性能
ELECTRICAL HOPELEX PCN-2004 LEXAN™ ML6411 resin 单位
UNIT 测试方法
TEST METHOD

介电强度(3.2 mm，在油中)
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm IEC 60093

热丝引燃(HWI)
Hot wire ignition UL 746

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

相比漏电起痕指数
Compared to the leakage tracing index UL 746

高电弧燃烧指数(HAI)
High Arc Burning Index (HAI) UL 746

加工方式

注射 HOPELEX PCN-2004 LEXAN™ ML6411 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大回制料比例 %

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.39 in/min

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*3

8 120*10*4 mm

9 标准 B (120°C/h), 载荷2 (50N)