牌号信息	SQ185 UVHV NC001 物性表 PC & 塑擎实业指导价格：暂无塑料库存：缺货	Makrolon® 6717 物性表 PC & 德国科思创指导价格：63000.0元/吨塑料库存： 1000kg
牌号简介	含阻燃剂；UL 94V-0/2.0 mm；高粘度；支链；紫外线稳定；易释放；注射成型-熔融温度280-320°C；挤出；提供透明、半透明和不透明颜色	MVR（300°C/1.2 kg）3.0 cm³/10 min；阻燃剂；UL 94V-0/2.0 mm；高粘度；支链；紫外线稳定；易释放；注射成型-熔融温度280-320°C；挤出；提供透明、半透明和不透明颜色 MVR (300 °C/1.2 kg) 3.0 cm³/10 min; flame retardant; UL 94V-0/2.0 mm; high viscosity; branched; UV stabilized; easy release; injection molding - melt temperature 280 - 320 °C; extrusion; available in transparent, translucent and opaque colors

产品描述
厂家：	塑擎实业 SUQING	德国科思创 Covestro
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：
性能特点：	防火阻燃等级V-0,耐候抗UV,含脱模剂,高粘度 V-0,Weather resistance is good,Good stripping performance,Flame Characteristics,High Viscosity	耐候抗UV,高粘度,含脱模剂,阻燃,防火阻燃等级V-0 Weather resistance is good,High Viscosity,Good stripping performance,Flame Characteristics,V-0
加工条件：	挤出,注射成型 Extrusion,Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL SQ185 UVHV NC001 Makrolon® 6717 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ISO 2577

收缩率(MD：2.0 mm)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate % ISO 2577

收缩率(TD：2.0 mm)
Shrinkage rate % ISO 294-4

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ISO 1133

表观密度
Apparent density g/cm³ ISO 60

薄膜
SQ185 UVHV NC001 Makrolon® 6717 单位
UNIT 测试方法
TEST METHOD

气体渗透(二氧化碳：23℃，100.0 µm)
Gas permeation cm³/m²/bar/24 hr ISO 2556

气体渗透(二氧化碳：23℃，25.4 µm)
Gas permeation cm³/m²/bar/24 hr ISO 2556

气体渗透(氧气：23℃，100.0 µm)
Gas permeation cm³/m²/bar/24 hr ISO 2556

气体渗透(氧气：23℃，25.4 µm)
Gas permeation cm³/m²/bar/24 hr ISO 2556

气体渗透(氮气：23℃，100.0 µm)
Gas permeation cm³/m²/bar/24 hr ISO 2556

气体渗透(氮气：23℃，25.4 µm)
Gas permeation cm³/m²/bar/24 hr ISO 2556

水气透过率(23℃，85% RH，100 µm)
Water vapor transmittance g/m²/24 hr ISO 15106-1

热性能
THERMAL SQ185 UVHV NC001 Makrolon® 6717 单位
UNIT 测试方法
TEST METHOD

导热系数(23℃)
Thermal conductivity coefficient W/m/K ISO 8302

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

玻璃化转变温度
Glass transition temperature ℃ ISO 11357-2

球压测试(139℃)
Ball pressure test IEC 60695-10-2

相对温度指数(冲击机械性能，2.00 mm)
Relative temperature index ℃ UL 746

相对温度指数(强度机械性能，2.00 mm)
Relative temperature index ℃ UL 746

相对温度指数(电气性能，2.00 mm)
Relative temperature index ℃ UL 746

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

电气性能
ELECTRICAL SQ185 UVHV NC001 Makrolon® 6717 单位
UNIT 测试方法
TEST METHOD

介电强度(23 ℃，1 mm)
Dielectric strength kV/mm IEC 60243-1

体积电阻率(23℃)
Volume resistivity ohms·cm IEC 60093

相对电容率(23℃，1 MHz)
Relative permittivity IEC 60250

相对电容率(23℃，100 Hz)
Relative permittivity IEC 60250

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V IEC 60112

相比漏电起痕指数(解决方案 B)
Compared to the leakage tracing index V IEC 60112

耗散因数(23℃，1 MHz)
Dissipation factor IEC 60250

耗散因数(23℃，100 Hz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY SQ185 UVHV NC001 Makrolon® 6717 单位
UNIT 测试方法
TEST METHOD

Flash Ignition Temperature
Flash Ignition Temperature ℃ ASTM D1929

Smoke Toxicity(with flame，CO)
Smoke Toxicity ppm AITM 3.0005

Smoke Toxicity(with flame，HCL)
Smoke Toxicity ppm AITM 3.0005

Smoke Toxicity(with flame，HCN)
Smoke Toxicity AITM 3.0005

Smoke Toxicity(with flame，HF)
Smoke Toxicity ppm AITM 3.0005

Smoke Toxicity(with flame，NO-NO2)
Smoke Toxicity ppm AITM 3.0005

Smoke Toxicity(with flame，SO2-H2O)
Smoke Toxicity ppm AITM 3.0005

Vertical Bunsen Burner Test(12 sec：1.00 mm)
Vertical Bunsen Burner Test FAR 28.853(b)

Vertical Bunsen Burner Test(12 sec：3.00 mm)
Vertical Bunsen Burner Test FAR 28.853(b)

Vertical Bunsen Burner Test(60sec：1.00 mm)
Vertical Bunsen Burner Test FAR 28.853(a)

Vertical Bunsen Burner Test(60sec：3.00 mm)
Vertical Bunsen Burner Test FAR 28.853(a)

小型燃烧器火焰的应用(Method K and F，2.00 mm)
The Application of Small Burner Flames DIN 53438-1, -3

极限氧指数
Extreme oxygen index % ISO 4589-2

灼热丝可燃性指数(0.75 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝可燃性指数(1.5 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝可燃性指数(3.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(0.75 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

灼热丝起燃温度(1.5 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

烟密度(with flame，Ds 4 min)
Smoke density ASTM E662

烟雾毒性(with flame，CO)
Smoke toxicity ppm AITM 3.0005

烟雾毒性(with flame，HCL)
Smoke toxicity ppm AITM 3.0005

烟雾毒性(with flame，HCN)
Smoke toxicity AITM 3.0005

烟雾毒性(with flame，HF)
Smoke toxicity ppm AITM 3.0005

烟雾毒性(with flame，NO-NO2)
Smoke toxicity ppm AITM 3.0005

烟雾毒性(with flame，SO2-H2O)
Smoke toxicity ppm AITM 3.0005

燃烧速率(USFMVSS，> 1.00 mm)
Burning rate ISO 3795

自燃温度
Autoignition temperature ℃ ASTM D1929

针焰测试(Method F：1.50 mm)
Needle flame test min IEC 60695-11-5

针焰测试(Method F：2.00 mm)
Needle flame test min IEC 60695-11-5

针焰测试(Method F：3.00 mm)
Needle flame test min IEC 60695-11-5

针焰测试(Method K：1.50 mm)
Needle flame test min IEC 60695-11-5

针焰测试(Method K：2.00 mm)
Needle flame test min IEC 60695-11-5

针焰测试(Method K：3.00 mm)
Needle flame test min IEC 60695-11-5

阻燃等级(2.00 mm)
Flame retardant level UL 94

光学性能
OPTICAL SQ185 UVHV NC001 Makrolon® 6717 单位
UNIT 测试方法
TEST METHOD

折射率
Refractive index ISO 489

透光率(1000 µm)
Transmittance % ISO 13468-2

透光率(2000 µm)
Transmittance % ISO 13468-2

透光率(3000 µm)
Transmittance % ISO 13468-2

透光率(4000 µm)
Transmittance % ISO 13468-2

冲击性能
IMPACT SQ185 UVHV NC001 Makrolon® 6717 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击力峰值(-30℃)
Multi axial instrumented peak impact force N ISO 6603-2

多轴向仪器化冲击力峰值(23℃)
Multi axial instrumented peak impact force N ISO 6603-2

多轴向仪器化冲击能量(-30℃)
Multi axial instrumented impact energy J ISO 6603-2

多轴向仪器化冲击能量(23℃)
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁缺口冲击强度(-30℃，完全断裂)
Impact strength of cantilever beam notch kJ/m² ISO 7391

悬臂梁缺口冲击强度(23℃，局部断裂)
Impact strength of cantilever beam notch kJ/m² ISO 7391

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁无缺口冲击强度(-60℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁缺口冲击强度(-30℃，完全断裂)
Charpy Notched Impact Strength kJ/m² ISO 7391

简支梁缺口冲击强度(23℃，局部断裂)
Charpy Notched Impact Strength kJ/m² ISO 7391

补充信息
SQ185 UVHV NC001 Makrolon® 6717 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname

机械性能
MECHANICAL SQ185 UVHV NC001 Makrolon® 6717 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Bending strain % ISO 178

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲强度(3.50% 应变，23℃)
bending strength MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(屈服，23℃)
Tensile strain % ISO 527-2/50

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2/50

拉伸强度(屈服，23℃)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2/50

拉伸模量(23℃)
Tensile modulus MPa ISO 527-1-2

标称拉伸断裂应变(23℃)
Nominal tensile fracture strain % ISO 527-2/50

球压硬度
Ball hardness MPa ISO 2039-1

备注

1 一般属性：这些不能被视为规格。

2 Pellets

3 60x60x2 mm, 500 bar

4 0.079 in/min

5 2 mm/min

6 Based on ISO 179-1eA, 3 mm

7 Based on ISO 180-A, 3 mm

8 10°C/min

9 Cross-flow

10 程序 A

11 方法 A


相关资讯

牌号简介
产品描述
技术参数
物理性能
薄膜
热性能
电气性能
阻燃性能
光学性能
冲击性能
补充信息
机械性能
加工方式
备注
返回顶部