技术参数
物理性能
PHYSICAL
23APG4
3APG5
单位
UNIT
测试方法
TEST METHOD
吸水率(23℃,24hr)
Water absorption rate
%
ASTM D-570
密度(---)
Density
g/cm³
ASTM D-792
熔体流动速率(230℃,3.8kg)
Melt flow rate
g/10min
ASTM D-1238
线性成型收缩率(Flow,3.2mm)
Linear molding shrinkage rate
%
ASTM D-955
热性能
THERMAL
23APG4
3APG5
单位
UNIT
测试方法
TEST METHOD
注塑成型参考模温(---)
Injection molding reference mold temperature
℃
---
注塑成型温度范围(---)
Injection molding temperature range
℃
---
烘干温度/时间(---)
Drying temperature/time
℃/h
---
烘干温度/时间(---)
Drying temperature/time
℃/hr
---
热变形温度(1.82MPa)
Hot deformation temperature
℃
ASTM D-648
热变形温度(1.82MPa)
Hot deformation temperature
℃
GB 1634
燃烧性能(3.2mm厚)
combustion performance
---
ASTM UL-94
线膨胀系数(-30+30℃)
Linear expansion coefficient
mm/℃
ASTM D696
阻燃性(UL 94)
Flame retardancy
---
1.50mm
机械性能
MECHANICAL
23APG4
3APG5
单位
UNIT
测试方法
TEST METHOD
屈服弯曲强度(6.4mm)
Yield bending strength
MPa
ASTM D-790
弯曲强度(6.4mm)
bending strength
MPa
ASTM D-790
弯曲模量(6.4mm)
Bending modulus
MPa
ASTM D-790
悬臂梁缺口冲击强度(干湿不断裂)
Impact strength of cantilever beam notch
KJ/m²
ASTM D-256
拉伸强度(---)
tensile strength
MPa
ASTM D-638
拉伸强度(23℃,50RH)
tensile strength
MPa
ASTM D-638
断裂伸长率(---)
elongation at break
%
ASTM D-638
断裂伸长率(23℃,50RH)
elongation at break
%
ASTM D-638
简支梁冲击强度
Charpy impact strength
ISO179
缺口
Gap
KJ/m²
3.2mm宽
非缺口
Non gap
KJ/m²
3.2mm宽
电性能
23APG4
3APG5
单位
UNIT
测试方法
TEST METHOD
介电常数(10-6HZ)
Dielectric constant
---
ASTM D150
介电强度(2mm厚)
Dielectric strength
MV/m
ASTM D149
介质损耗角正切(10-6HZ)
Tangent of dielectric loss angle
---
ASTM D150
体积电阻率(---)
Volume resistivity
Ω.m
ASTM D257