牌号简介	暂无	NYCASTCP具有很高的弹性，具有比标准等级更高的拉伸延伸率和冲击强度，已在许多需要额外韧性的应用中得到证明。NYCAST CP是己内酰胺和月桂内酯的共聚物，最初专门开发用于石油和天然气工业中的球阀座。这种耐用的材料在NYCAST 6和NYCAST 12配方之间提供了一个经济、高性能的桥梁。NYCAST CP具有较高的延伸率、优异的尺寸稳定性和安全的黄色，是冷轧钢铁工业中摇摆箱镶块和联结箱以及纸管制造厂中芯轴盖的首选。 Highly resilient, with higher tensile elongation and impact strength than standard grades, NYCAST CP has proven itself in many applications requiring an extra degree of toughness. A copolymer of caprolactam and laurinlactam, NYCAST CP was originally developed specifically for use in ball valve seats in the oil and gas industry. This durable material provides an economical, high-performance bridge between NYCAST 6 and NYCAST 12 formulations. NYCAST CP with its higher elongation, superior dimensional stability and safety yellow color has found itself a superior choice for wobbler box inserts and coupling boxes in the cold rolling steel industry as well as mandrels covers used in paper tube manufacturing plants. High impact resistance High tensile elongation Reduced water absorption Lower hardness Easy to machine

产品描述
厂家：	常州星易迪	美国Cast Nylons
类别：	PA6 PA6	PA6 PA6
填料：
用途：		阀门/阀门部件,滚轴,传送机配件,齿轮,外壳,密封件
性能特点：		韧性好,冲击性能好,尺寸稳定性好,有弹性,拉伸性能好,共聚物,经久耐用 Good flexibility,High impact resistance,Good Dimensional Stability,Elastic,Good Tensile Strength,Copolymer,Durability
加工条件：		浇铸 casting

技术参数

物理性能
PHYSICAL 4BA2 Nycast CP 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water absorption rate % ASTM D570

吸水率(饱和)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

密度(---)
Density g/cm³ ASTM D-792

熔体流动速率(---)
Melt flow rate g/10min ASTMD-1238

线性成型收缩率(23℃)
Linear molding shrinkage rate % ASTM D-955

热性能
THERMAL 4BA2 Nycast CP 单位
UNIT 测试方法
TEST METHOD

使用温度(Intermittent)
Operating temperature ℃

注塑成型参考模温(---)
Injection molding reference mold temperature ℃ ---

注塑成型温度范围(---)
Injection molding temperature range ℃ ---

烘干温度/时间(---)
Drying temperature/time ℃/hr ---

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.80MPa)
Hot deformation temperature ℃ ASTM D-648

熔融温度
Melting temperature ℃

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

连续使用温度
Continuous use temperature ℃ ASTM D794

阻燃性能(UL-94)
FLAME CHARACTERISTICS class 0.8mm

机械性能
MECHANICAL 4BA2 Nycast CP 单位
UNIT 测试方法
TEST METHOD

剪切强度
shear strength MPa ASTM D732

压缩强度
compressive strength MPa ASTM D695

压缩模量
Compression modulus MPa ASTM D695

屈服弯曲强度(6.4mm)
Yield bending strength MPa ASTM D-790

弯曲强度
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(6.4mm)
Bending modulus MPa ASTM D-790

悬臂梁缺口冲击强度(3.2m，23℃)
Impact strength of cantilever beam notch KJ/m² ASTM D-256

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(50mm/min)
tensile strength MPa ASTM D-638

拉伸模量
Tensile modulus MPa ASTM D638

摩擦系数(与自身 - 动态)
friction coefficient ASTM D1894

断裂伸长率(50mm/min)
elongation at break % ASTM D-638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

负载变形
Load deformation % ASTM D621

邵氏硬度(邵氏 D)
Shore hardness ASTM D2240

冲击性能
IMPACT 4BA2 Nycast CP 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

电气性能
ELECTRICAL 4BA2 Nycast CP 单位
UNIT 测试方法
TEST METHOD

介电常数(1 kHz)
Dielectric constant ASTM D150

介电常数(100 kHz)
Dielectric constant ASTM D150

介电常数(60 Hz)
Dielectric constant ASTM D150

介电强度
Dielectric strength kV/mm ASTM D149

备注

1 一般属性：这些不能被视为规格。