牌号简介	HEPLA®H2018cm EC是一种18%矿物填充材料。这种材料结合了高硬度和优良的耐温性和导电性，用于静电喷涂。 Hepla® H2018CM EC is a 18% mineral filled material. This material combines high stiffness and excellent temperature resistance with conductivity for electrostatic painting.	HEPLA®H2000 cm树脂是聚苯醚（PPE）和聚酰胺（PA）树脂的混合物，填充矿物，适合注塑成型。导电性水平得到优化，允许无底漆静电喷涂。HEPLA®H2000 cm提高了冲击/延伸率，矿物含量使材料能够用于结构应用，取代金属或热固性树脂。这种材料只有黑色的。 Hepla® H2000 CM Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, and suitable for injection molding. The conductivity level is optimized to allow for primer-less electrostatic painting. Hepla® H2000 CM has improved impact/elongation and the mineral content enables the material to be used in structural applications replacing metal or thermoset resins. The material is only available in black.

产品描述
厂家：	新孚达 NFD	新孚达 NFD
类别：	PPO(PPE) PPO(PPE)	PPO(PPE) PPO(PPE)
填料：
用途：
性能特点：
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Hepla® H2018CM EC Hepla® H2000 CM 单位
UNIT 测试方法
TEST METHOD

Moisture Absorption(Saturation, 23℃)
Moisture Absorption % ISO 62

Moisture Absorption(平衡，23℃, 50% RH)
Moisture Absorption % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：3.20 mm)
Shrinkage rate % NFD Method

熔体体积流动速率(220℃，5.0 kg)
Melt Volume Rate cm3/10min ISO 1133

熔体质量流动速率(280℃，5.0 kg)
Melt Flow Rate g/10 min ASTM D1238

机械性能
MECHANICAL Hepla® H2018CM EC Hepla® H2000 CM 单位
UNIT 测试方法
TEST METHOD

Flexural Modulus, 2.0 mm/min
Flexural Modulus, 2.0 mm/min MPa ISO 178

Flexural Modulus, 50.0 mm Span(1.3 mm/min)
Flexural Modulus, 50.0 mm Span MPa ASTM D790

Flexural Stress, break(50.0 mm Span, 1.3 mm/min)
Flexural Stress, break MPa ASTM D790

Flexural Stress, yield(2.0 mm/min)
Flexural Stress, yield MPa ASTM D790

Flexural Stress, yield(2.0 mm/min)
Flexural Stress, yield MPa ISO 178

Tensile Modulus, 5.0 mm/min
Tensile Modulus, 5.0 mm/min MPa ASTM D638

Tensile Strain, break, Type I(5.0 mm/min)
Tensile Strain, break, Type I % ASTM D638

Tensile Strain, yield, Type I(5.0 mm/min)
Tensile Strain, yield, Type I % ASTM D638

Tensile Stress, break, Type I(5.0 mm/min)
Tensile Stress, break, Type I MPa ASTM D638

Tensile Stress, yield, Type I(5.0 mm/min)
Tensile Stress, yield, Type I MPa ASTM D638

弯曲模量(2.0 mm/min)
Bending modulus MPa ISO 178

弯曲模量(50.0 mm Span, 1.3 mm/min)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ISO 527-2/1

拉伸模量(5.0 mm/min)
Tensile modulus MPa ASTM D638

冲击性能
IMPACT Hepla® H2018CM EC Hepla® H2000 CM 单位
UNIT 测试方法
TEST METHOD

Notched Izod Impact, -30℃
Notched Izod Impact, -30℃ J/m ASTM D256

Unnotched Izod Impact, -30℃
Unnotched Izod Impact, -30℃ J/m ASTM D4812

悬臂梁无缺口冲击强度(80*10*4 ,-30℃)
Notched impact strength of cantilever beam kJ/m2 ISO 180/1A

悬臂梁无缺口冲击强度(80*10*4， -30℃)
Notched impact strength of cantilever beam kJ/m2 ISO 180/1U

悬臂梁无缺口冲击强度(80*10*4， 23℃)
Notched impact strength of cantilever beam kJ/m2 ISO 180/1U

悬臂梁缺口冲击强度, 23℃
Impact strength of cantilever beam notch, 23 ℃ J/m ASTM D256

悬臂梁缺口冲击强度(80*10*4 , 23℃)
Impact strength of cantilever beam notch kJ/m2 ISO 180/1A

悬臂梁缺口冲击强度(80*10*4， -30℃)
Impact strength of cantilever beam notch kJ/m2 ISO 180/1A

悬臂梁缺口冲击强度(80*10*4， 23℃)
Impact strength of cantilever beam notch kJ/m2 ISO 180/1A

简支梁缺口冲击强度(80*10*4, 23℃)
Charpy Notched Impact Strength kJ/m2 ISO 179/1eA

飞镖冲击强度(23℃, Total Energy)
Dart impact strength J ASTM D3763

热性能
THERMAL Hepla® H2018CM EC Hepla® H2000 CM 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，64.0 mm Span, 120*10*4 mm)
Hot deformation temperature ℃ ISO 75-2/Be

热变形温度(0.45MPa，未退火，3.2mm)
Hot deformation temperature ℃

热变形温度(0.45MPa，未退火，3.2mm)
Hot deformation temperature ℃ ISO 75-2/Be

热变形温度(Bf,0.45 MPa Flatw 80*10*4 sp=64mm)
Hot deformation temperature ℃ ISO 75/Bf

线性热膨胀系数(Flow : -40 to 40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831, ISO 11359-2

线性热膨胀系数(Flow : 23 to 60℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(Transverse : -40 to 40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831, ISO 11359-2

线性热膨胀系数(Transverse : 23 to 60℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

维卡软化温度
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度
Vicat Softening Temp ℃ ISO 306/B50

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306

维卡软化温度(B50)
Vicat Softening Temp ℃ ASTM D1525, ISO 306

加工方式

加工工艺 Hepla® H2018CM EC Hepla® H2000 CM 单位测试方法

Drying Time, Maximum hr

Hopper Temperature ℃

Maximum Moisture Content %

Nozzle Temperature ℃

Screw Speed rpm

Suggested Shot Size %

Vent Depth mm

干燥时间 hr

干燥温度 ℃

料筒中部温度 ℃

料筒前部温度 ℃

料筒后部温度 ℃

模具温度 ℃

熔体温度 ℃

背压 MPa

备注


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
加工工艺
备注