PC，KOPHOS® KO1989对比PC，CALIBRE™ 303-22物性表,价格行情_搜料

牌号信息	KOPHOS® KO1989 物性表 PC & 韩国可隆指导价格：暂无塑料库存：缺货	CALIBRE™ 303-22 物性表 PC & 美国盛禧奥指导价格：暂无塑料库存：缺货
牌号简介	KOPHOS® KO1989是一种聚碳酸酯（PC）产品,。它可以通过注射成型进行加工,在北美洲、拉丁美洲、欧洲或亚太地区有供货。典型应用领域为:照明设备。特性包括: 阻燃/额定火焰通过 ROHS 认证 KOPHOS® KO1989 is a Polycarbonate (PC) product. It can be processed by injection molding and is available in Asia Pacific, Europe, Latin America, or North America. Typical application: Lighting Applications. Characteristics include: Flame Rated RoHS Compliant	CALIBRE™ 303-22 SC830104乳白色聚碳酸酯树脂为注塑应用提供卓越的抗冲击性、热变形性和乳白色。高熔体流动速率使复杂零件易于成型。该树脂是紫外线稳定，含有脱模剂。政府和行业标准：保险商实验室公司（UL）应用：照明扩散器储物箱 CALIBRE™ 303-22 SC830104 Opalescent Polycarbonate Resin offers exceptional impact resistance, heat distortion resistance, and opalescence for injection molding applications. The high melt flow rate allows complex parts to be easily molded. The resin is UV stabilized and contains mould release agent . Govt. and Industry Standards: Underwriters Laboratory, Inc. (UL) Applications: Lighting diffusers Storage boxes

产品描述
厂家：	韩国可隆 Kolon	美国盛禧奥 Trinseo
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：	照明漫射器	照明应用
性能特点：	防火阻燃等级V-2 V-2	耐候抗UV,冲击性能好,流动性高,防火阻燃等级HB Weather resistance is good,High impact resistance,High liquidity,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL KOPHOS® KO1989 CALIBRE™ 303-22 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ISO 62

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792 , ISO 1183

密度
Density g/cm³ ISO 1183/B

收缩率(MD)
Shrinkage rate % ISO 294-4

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238，ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL KOPHOS® KO1989 CALIBRE™ 303-22 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(--)
bending strength MPa ASTM D790

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(--)
tensile strength MPa ASTM D638

拉伸强度(23℃)
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ISO 527-2/50

泰伯耐磨性
Taber abraser % ASTM D1044

洛氏硬度(M 级)
Rockwell hardness ISO 2039-2

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

冲击性能
IMPACT KOPHOS® KO1989 CALIBRE™ 303-22 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-A

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL KOPHOS® KO1989 CALIBRE™ 303-22 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火，6.35 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/A

球压温度
Ball pressure temperature ℃ IEC 60598-1

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

阻燃性能
FLAMMABILITY KOPHOS® KO1989 CALIBRE™ 303-22 单位
UNIT 测试方法
TEST METHOD

0.8 到 3.2 mm
0.8 to 3.2 mm UL 94

极限氧指数
Extreme oxygen index % ISO 4589-2

灼热丝可燃性指数(1.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝可燃性指数(2.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝可燃性指数(3.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(1 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

灼热丝起燃温度(2 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(3.00 mm)
Flame retardant level UL 94

光学性能
OPTICAL KOPHOS® KO1989 CALIBRE™ 303-22 单位
UNIT 测试方法
TEST METHOD

a*(1.00 mm)
a*

a*(2.00 mm)
a*

a*(3.00 mm)
a*

b*(1.00 mm)
b*

b*(2.00 mm)
b*

b*(3.00 mm)
b*

Diffusivity(1.00 mm)
Diffusivity

Diffusivity(2.00 mm)
Diffusivity

Diffusivity(3.00 mm)
Diffusivity

L*(1.00 mm)
L*

L*(2.00 mm)
L*

L*(3.00 mm)
L*

透光率(1000 µm)
Transmittance %

透光率(2000 µm)
Transmittance %

透光率(3000 µm)
Transmittance %

透光率(总计)
Transmittance % ISO 13468

透光率(总计，1000 µm)
Transmittance % ISO 13468

雾度(--)
Haze % ISO 14782

雾度(1000 µm)
Haze %

雾度(1000 µm)
Haze % ISO 14782

雾度(2000 µm)
Haze %

雾度(3000 µm)
Haze %

黄度指数(1.00 mm)
Yellowness index YI ASTM D1925

黄度指数(2.00 mm)
Yellowness index YI ASTM D1925

黄度指数(3.00 mm)
Yellowness index YI ASTM D1925

电气性能
ELECTRICAL KOPHOS® KO1989 CALIBRE™ 303-22 单位
UNIT 测试方法
TEST METHOD

介电常数(60 Hz)
Dielectric constant IEC 60250

介电强度
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm IEC 60093

相对电容率(1 MHz)
Relative permittivity IEC 60250

相对电容率(100 Hz)
Relative permittivity IEC 60250

相比漏电起痕指数(2.00 mm，解决方案 A)
Compared to the leakage tracing index V IEC 60112

耗散因数(1 MHz)
Dissipation factor IEC 60250

耗散因数(50 Hz)
Dissipation factor IEC 60250

加工方式

注射 KOPHOS® KO1989 CALIBRE™ 303-22 单位测试方法

射嘴温度 °C

干燥时间 - 热风干燥机 hr

干燥温度 - 热风干燥机 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 0.079 in/min

3 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions.


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
光学性能
电气性能
加工方式
注射
备注
返回顶部

PC，KOPHOS® KO1989对比PC，CALIBRE™ 303-22对比物性表,价格行情_搜料_soliao