牌号信息	Hepla® H7115GF EC 物性表 PA6 & 新孚达指导价格：暂无塑料库存：缺货	LNP™ THERMOCOMP™ PF003 compound 物性表 PA6 & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	HEPLA®H7115GF EC是一种填充15%玻璃纤维的聚酰胺6（尼龙6）产品。特点包括：防静电、导电。 Hepla ® H7115GF EC is a Polyamide 6 (Nylon 6) product filled with 15% glass fiber.Characteristics include:ESD Protection,Electrically Conductive.	lnp thermocomp pf003化合物lnp thermocomppf003是一种基于尼龙6树脂的化合物，含有15%的玻璃纤维。也称为：LNPThermoCompa化合物PF-1003产品再订购名称：PF003LNP ThermoCompa PF003化合物LNP ThermoCompa PF003是一种基于含玻璃纤维的尼龙6树脂的化合物。也称为：lnpThermocomp化合物pf-1003产品再订购名称：pf003 LNP™ THERMOCOMP™ PF003 compound LNP THERMOCOMP PF003 is a compound based on Nylon 6 resin containing 15% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound PF-1003 Product reorder name: PF003 LNP™ THERMOCOMP™ PF003 compound LNP THERMOCOMP PF003 is a compound based on Nylon 6 resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound PF-1003 Product reorder name: PF003

产品描述
厂家：	新孚达 NFD	沙特沙伯基础 SABIC
类别：	PA6 PA6	PA6 PA6
填料：	玻璃纤维 15	玻璃纤维 15
用途：
性能特点：	易加工,冲击性能好,导电,自润滑,耐化学性,耐磨性好,防静电 Excellent Processability,High impact resistance,Conductive,Self-lubricating,Solvent resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Hepla® H7115GF EC LNP™ THERMOCOMP™ PF003 compound 单位
UNIT 测试方法
TEST METHOD

含水量
water content %

密度
Density g/cm³ ASTM D792

收缩率(MD：3.20 mm)
Shrinkage rate % ASTM D955

机械性能
MECHANICAL Hepla® H7115GF EC LNP™ THERMOCOMP™ PF003 compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(23℃)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量(23℃)
Tensile modulus MPa ASTM D638

冲击性能
IMPACT Hepla® H7115GF EC LNP™ THERMOCOMP™ PF003 compound 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(3.20 mm)
Impact strength of cantilever beam notch J/m ASTM D256

电气性能
ELECTRICAL Hepla® H7115GF EC LNP™ THERMOCOMP™ PF003 compound 单位
UNIT 测试方法
TEST METHOD

ohms ASTM D257

ohms ESD STM11.11

体积电阻率
Volume resistivity Ohms∙cm ASTM D257

表面电阻率
Surface resistivity

静态衰减
Static attenuation sec FTMS 101C 4046.1

热性能
THERMAL Hepla® H7115GF EC LNP™ THERMOCOMP™ PF003 compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

阻燃性能
FLAMMABILITY Hepla® H7115GF EC LNP™ THERMOCOMP™ PF003 compound 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.50mm)
Flame retardant level UL-94

阻燃等级(3.00mm)
Flame retardant level UL-94

阻燃等级(6.00mm)
Flame retardant level UL-94

加工方式

加工处理 Hepla® H7115GF EC LNP™ THERMOCOMP™ PF003 compound 单位测试方法

干燥时间 hrs

干燥温度 ℃

模具温度 ℃

注射压力 MPa

熔体温度 ℃

露点温度 ℃

备注

1 MIL-PRF-81705D, 5kV to 50 V, 12% RH

1 一般属性：这些不能被视为规格。

2 2.0 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
电气性能
热性能
阻燃性能
加工方式
加工处理
备注
返回顶部

PA6，Hepla® H7115GF EC对比PA6，LNP™ THERMOCOMP™ PF003 compound对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别