ABS，Hepla® H1100 H FR对比ABS，POLYLAC® PA-763物性表,价格行情_搜料

牌号信息	Hepla® H1100 H FR 物性表 ABS & 新孚达指导价格：暂无塑料库存：缺货	POLYLAC® PA-763 物性表 ABS & 台湾奇美指导价格：25830.0元/吨塑料库存： 4000kg
牌号简介	HEPLA®H1100 H FR是一种无增强丙烯腈-丁二烯-苯乙烯（ABS）产品。特性包括：特性包括：阻燃、耐热、耐候。 Hepla ® H1100 H FR is a unreinforced Acrylonitrile Butadiene Styrene (ABS) product.Characteristics include:Characteristics include: Flame Rated,Heat Resistant,Weather Resistant.	POLYLAC® PA-763是一种丙烯腈丁二烯苯乙烯(ABS)产品,。它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。特性包括: 阻燃/额定火焰通过 ROHS 认证耐候性好耐热 POLYLAC® PA-763 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include: Flame Rated RoHS Compliant Heat Resistant Weather Resistant

产品描述
厂家：	新孚达 NFD	台湾奇美 CHI MEI
类别：	ABS ABS	ABS ABS
填料：
用途：
性能特点：	冲击性能好,尺寸稳定性好,流动性高,吸水率低,阻燃,耐高温,抗静电,加工性能 High impact resistance,Good Dimensional Stability,High liquidity,Low or no water absorption,Flame Characteristics,High Heat Resistance,Antistatic property	耐候抗UV,耐高温,防火阻燃等级V-0,防火阻燃等级5VA Weather resistance is good,High Heat Resistance,V-0,5VA
加工条件：	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Hepla® H1100 H FR POLYLAC® PA-763 单位
UNIT 测试方法
TEST METHOD

密度(--)
Density g/cm³ ASTM D792

密度(23℃)
Density g/cm³ ASTM D792

密度(23℃)
Density g/cm³ ISO 1183

收缩率
Shrinkage rate % ISO 294-4

熔体体积流动速率(220℃/10.0 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(220℃，10 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(200℃/5.0 kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(200℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT Hepla® H1100 H FR POLYLAC® PA-763 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180/1A

悬臂梁缺口冲击强度(23℃, 3.20 mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180/1A

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，6.4mm)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

阻燃性能
FLAMMABILITY Hepla® H1100 H FR POLYLAC® PA-763 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(1.5mm)
Flame retardant level UL 94

阻燃等级(2.50 mm)
Flame retardant level UL 94

阻燃等级(2.5mm)
Flame retardant level UL 94

热性能
THERMAL Hepla® H1100 H FR POLYLAC® PA-763 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa, 退火)
Hot deformation temperature ISO 75-2/A

热变形温度(1.8 MPa, 退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ASTM D648，ISO 75-2/A

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD)
Linear coefficient of thermal expansion cm/cm/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 7

维卡软化温度(103)
Vicat Softening Temp ISO 306/A50

维卡软化温度(104)
Vicat Softening Temp ASTM D1525

维卡软化温度(96)
Vicat Softening Temp ISO 306/B50

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

机械性能
MECHANICAL Hepla® H1100 H FR POLYLAC® PA-763 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ASTM D790

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(2.0 mm/min)
bending strength MPa ISO 178

弯曲强度(2.8 mm/min)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(2.0 mm/min)
Bending modulus MPa ISO 178

弯曲模量(2.8 mm/min)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸应变(断裂，6.0 mm/min)
Tensile strain % ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(屈服，6.0 mm/min)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

洛氏硬度(R 级)
Rockwell hardness ASTM D785

加工方式

加工工艺 Hepla® H1100 H FR POLYLAC® PA-763 单位测试方法

保压压力 MPa

干燥时间 hr

干燥温度 ℃

料筒中部温度 ℃

料筒前部温度 ℃

料筒后部温度 ℃

模具温度 ℃

注射压力 MPa

背压 MPa

注射 Hepla® H1100 H FR POLYLAC® PA-763 单位测试方法

保压 MPa

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

背压 MPa

备注

1 ℃

Rate A (50 /h), Loading 1 (10 N)

3 23°C

4 6.0 mm/min

5 2.8 mm/min

6 2.0 mm/min

7 速率 A (50°C/h), 压力1 (10N)