技术参数
机械性能
MECHANICAL
TPU-2790
Pellethane® 2102-90AE
单位
UNIT
测试方法
TEST METHOD
压缩形变(22hr,25℃)
Compression deformation
%
ASTM D395
压缩形变(22hr,70℃)
Compression deformation
%
ASTM D395
回弹性
Resilience
%
ASTM D2630,ISO 4662
弯曲模量
Bending modulus
MPa
ASTM D790
拉伸应变
Tensile strain
%
ASTM D412
拉伸应变
Tensile strain
%
ASTM D412,ISO 527
拉伸强度
tensile strength
MPa
ASTM D412
拉伸强度
tensile strength
MPa
ASTM D412,ISO 527
拉伸模量(100% 应变)
Tensile modulus
MPa
ASTM D412,ISO 527
拉伸模量(100%应变)
Tensile modulus
MPa
ASTM D412
拉伸模量(300% 应变)
Tensile modulus
MPa
ASTM D412,ISO 527
拉伸模量(300%应变)
Tensile modulus
MPa
ASTM D412
拉伸模量(50%应变)
Tensile modulus
MPa
ASTM D412
撕裂强度
tear strength
KN/m
ASTM D624
撕裂强度
tear strength
N/mm²
ASTM D624,ISO 34
泰伯耐磨性(1000g,1000周期)
Taber abraser
mg
ASTM D1044
邵氏硬度(邵氏 A)
Shore hardness
ASTM D2240
邵氏硬度(邵氏 A)
Shore hardness
ASTM D2240,ISO 868
邵氏硬度(邵氏 D)
Shore hardness
ASTM D2240
物理性能
PHYSICAL
TPU-2790
Pellethane® 2102-90AE
单位
UNIT
测试方法
TEST METHOD
密度
Density
ASTM D792
密度
Density
ASTM D792,ISO 2781,JIS K7311
收缩率(MD)
Shrinkage rate
%
收缩率(TD)
Shrinkage rate
%
熔体质量流动速率(224℃,1.2 kg)
Melt Flow Rate
g/10min
ASTM D1238
热性能
THERMAL
TPU-2790
Pellethane® 2102-90AE
单位
UNIT
测试方法
TEST METHOD
玻璃化转变温度
Glass transition temperature
℃
ASTM D3418,ISO 815
玻璃化转变温度
Glass transition temperature
℃
DSC
线性热膨胀系数
Linear coefficient of thermal expansion
mm/mm/℃
ASTM D696
维卡软化温度
Vicat Softening Temp
℃
ASTM D1525
维卡软化温度
Vicat Softening Temp
℃
ASTM D1525,ISO R306