PP均聚，PP EP300M对比PP均聚，SABIC® PP PHC26物性表,价格行情_搜料

牌号信息	PP EP300M 物性表 PP均聚 & 惠州中海壳牌指导价格：8505.0元/吨塑料库存： 30000kg	SABIC® PP PHC26 物性表 PP均聚 & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介		这一等级结合了非常高的抗冲击性，也在低温下，具有很高的刚度和良好的流动性能。SABIC® PP PHC26由于其分子量分布窄、翘曲倾向低、表面质量优良，因此通常用于行李箱壳体、板条箱和汽车零部件的注塑成型。本文所述产品尤其未经测试，因此未经验证可用于医药/医疗应用。 This grade combines very high impact resistance, also at low temperatures, with high stiffness and offers good flow properties. Due to its narrow molecular weight distribution, the very low tendency to warp and the excellent surface quality, SABIC® PP PHC26 is typically used in injection moulding of suitcase shells, crates & boxes and automotive parts. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.

产品描述
厂家：	惠州中海壳牌	沙特沙伯基础 SABIC
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：
用途：	家电用具	皮箱,汽车领域的应用,装货箱
性能特点：	冲击性能好,尺寸稳定性好,耐低温强度 High impact resistance,Good Dimensional Stability,Low temperature strength	机械强度好,低翘曲性,表面光泽度好,冲击性能好,易流动,成核的,嵌段共聚物,窄分子量分布,耐低温冲击 Good Rigidity,Low warping,Good surface appearance,High impact resistance,Good liquidity,Nucleation,Block Copolymer,Weight distribution,low-temperature impact resistance
加工条件：		注射成型 Injection Molding

技术参数

机械性能
MECHANICAL PP EP300M SABIC® PP PHC26 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790，ISO 178

弯曲模量
Bending modulus MPa ASTM D790/ISO 178

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ASTM D638，ISO 527

拉伸应变(屈服)
Tensile strain % ISO 527-2/1A/50

拉伸应变(断裂)
Tensile strain % ASTM D638，ISO 527

拉伸强度
tensile strength MPa ASTM D638，ISO 527

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/1A/50

拉伸模量
Tensile modulus MPa ASTM D638，ISO 527

拉伸模量(--)
Tensile modulus MPa ISO 527-2/1A/1

拉伸模量(1% 正割)
Tensile modulus MPa ASTM D638

洛氏硬度
Rockwell hardness ASTM D785

洛氏硬度(R 级)
Rockwell hardness ASTM D785

邵氏硬度(邵氏 D)
Shore hardness ISO 868

冲击性能
IMPACT PP EP300M SABIC® PP PHC26 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch J/m ASTM D256-A

悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(0℃)
Impact strength of cantilever beam notch J/m ASTM D256-A

悬臂梁缺口冲击强度(0℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch ASTM D256A , ISO 180/1A

悬臂梁缺口冲击强度(23℃，6.4mm)
Impact strength of cantilever beam notch J/m ASTM D256，ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength J/m ASTM D256/ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(0℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

物理性能
PHYSICAL PP EP300M SABIC® PP PHC26 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570/ISO 62

密度
Density g/cm³ ASTM D792 , ISO 1183

密度
Density g/cm³ ASTM D792，ISO 1183

收缩率
Shrinkage rate % ASTM D955

熔体质量流动速率(200℃，10.0kg )
Melt Flow Rate g/10min ASTM D1238，ISO 1133

熔体质量流动速率(200℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238，ISO 1133

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238，ISO 1133

热性能
THERMAL PP EP300M SABIC® PP PHC26 单位
UNIT 测试方法
TEST METHOD

可燃性
Flammability UL 94

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Af

熔点
melting point ℃ -

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525/ISO R306

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 5 , ISO 306/A120 5

维卡软化温度(B120)
Vicat Softening Temp ℃ ASTM D1525 6 , ISO 306/B120 6

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 2.0 in/min

4 testbar 80*10*4mm

5 标准 B (120°C/h), 压力1 (10N)

6 标准 B (120°C/h), 载荷2 (50N)