牌号简介	lnpThermocompd251rc（实验级名称为extc8483）是一种基于循环聚碳酸酯树脂的化合物，含有玻璃纤维、阻燃剂。该材料的附加特性包括：高模量，良好的平整度，良好的延展性，无溴化U0026amp；无氯化阻燃剂。消费后回收（PCR）聚碳酸酯含量高达35%。 LNP* Thermocomp* D251RC (experimental grade name as EXTC8483) is a compound based on Recycle Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: high modulus, good flatness, good ductility, Non-Brominated u0026amp; Non-Chlorinated Flame Retardant. Post-Consumer Recycling (PCR) polycarbonate content up to 35%.	LNPThermocompD151RC（实验级名称为extc8482）是一种基于循环聚碳酸酯树脂的化合物，含有玻璃纤维、阻燃剂。该材料的附加特性包括：高模量、表面良好、平整度好、延展性好、无溴化U0026amp；无氯化阻燃剂。消费后回收（PCR）聚碳酸酯含量高达35%。 LNP* Thermocomp* D151RC (experimental grade name as EXTC8482) is a compound based on Recycle Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: high modulus, good surface, good flatness, good ductility, Non-Brominated u0026amp; Non-Chlorinated Flame Retardant. Post-Consumer Recycling (PCR) polycarbonate content up to 35%.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：	玻璃纤维	玻璃纤维
用途：	电气/电子应用领域	电气/电子应用领域
性能特点：
加工条件：

技术参数

物理性能
PHYSICAL LNP™ THERMOCOMP™ Compound D251RC LNP™ THERMOCOMP™ Compound D151RC 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

收缩率(MD：24 hrs)
Shrinkage rate %

收缩率(TD：24 hrs)
Shrinkage rate %

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min

熔体体积流动速率(300℃，2.16 kg)
Melt Volume Rate cm³/10min

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min

熔体质量流动速率(300℃，2.16kg)
Melt Flow Rate g/10min

机械性能
MECHANICAL LNP™ THERMOCOMP™ Compound D251RC LNP™ THERMOCOMP™ Compound D151RC 单位
UNIT 测试方法
TEST METHOD

弯曲应力(--)
Bending stress MPa ISO 178

弯曲应力(屈服，50.0 mm 跨距)
Bending stress MPa ASTM D790

弯曲应力(断裂，50.0 mm 跨距)
Bending stress MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

抗张强度(断裂)
Tensile strength MPa ASTM D638

抗张强度(断裂)
Tensile strength MPa ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LNP™ THERMOCOMP™ Compound D251RC LNP™ THERMOCOMP™ Compound D151RC 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(23°C，Total Energy)
Dart impact equipped with measuring instruments (23 ° C, Total Energy) J ASTM D3763

热性能
THERMAL LNP™ THERMOCOMP™ Compound D251RC LNP™ THERMOCOMP™ Compound D151RC 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，4.0 mm，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，4.0 mm，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度(--)
Vicat Softening Temp ℃ ISO 306

维卡软化温度(--)
Vicat Softening Temp ℃ ISO 306/B120

电气性能
ELECTRICAL LNP™ THERMOCOMP™ Compound D251RC LNP™ THERMOCOMP™ Compound D151RC 单位
UNIT 测试方法
TEST METHOD

介电常数(1.10 GHz)
Dielectric constant

介电常数(1.9 GHz)
Dielectric constant

介电常数(10.0 GHz)
Dielectric constant

介电常数(5.00 GHz)
Dielectric constant

体积电阻率
Volume resistivity ohms·cm ASTM D257

耗散因数(1.1 GHz)
Dissipation factor

耗散因数(1.9 GHz)
Dissipation factor

耗散因数(10 GHz)
Dissipation factor

耗散因数(5 GHz)
Dissipation factor

表面电阻率
Surface resistivity ohms ASTM D257

阻燃性能
FLAMMABILITY LNP™ THERMOCOMP™ Compound D251RC LNP™ THERMOCOMP™ Compound D151RC 单位
UNIT 测试方法
TEST METHOD

阻燃等级(0.50 mm)
Flame retardant level

阻燃等级(0.60 mm)
Flame retardant level

阻燃等级(0.60 mm)
Flame retardant level UL 94

加工方式

注射 LNP™ THERMOCOMP™ Compound D251RC LNP™ THERMOCOMP™ Compound D151RC 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

2、5.0 mm/min

3、类型 1, 5.0 mm/min

4、1.3 mm/min

5、2.0 mm/min

6、at Yield

7、at Break

8、80*10*4 mm