PC+ABS，LNP™ STAT-KON™ Compound JK800对比PC+ABS，RTP ESD C 2580物性表,价格行情_搜料

牌号信息	LNP™ STAT-KON™ Compound JK800 物性表 PC+ABS & 沙特沙伯基础指导价格：102921.0元/吨塑料库存： 5000kg	RTP ESD C 2580 物性表 PC+ABS & 美国RTP 指导价格：暂无塑料库存：缺货
牌号简介	LNP-STAT-KON JK800复合材料是一种8%碳纤维增强PC+ABS，静电耗散生态相容性好，水解稳定性好。 LNP™ STAT-KON™ JK800 compound is a 8% carbon fiber reinforced PC+ABS, electrostatic dissipative ECO conforming FR. Good hydrolytic stability.	警告：此材料的状态为“商业：限量发行”。此材料的数据最近尚未验证。在指定此等级之前，请联系RTP公司以获取当前信息。ESD 2580系列材料为聚碳酸酯/ABS合金，导电性添加碳纤维。这些材料具有优良的静态耗散特性，是非脱落，可在各种颜色。ESD A 2580为ST Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. ESD 2580 Series materials are polycarbonate/ABS alloy with carbon fiber added for electrical conductivity. These materials have excellent static dissipation characteristics, are non-sloughing and are available in a wide range of colors. ESD A 2580 is st

产品描述
厂家：	沙特沙伯基础 SABIC	美国RTP
类别：	PC+ABS PC+ABS	PC+ABS PC+ABS
填料：	碳纤维	碳纤维
用途：
性能特点：	耐水解,无卤,阻燃,符合ECO,防火阻燃等级V-0,防火阻燃等级5VB Hydrolysis stability,Halogen free,Flame Characteristics,ECO,V-0,5VB	导电,静电放电保护,抗静电,防火阻燃等级HB Conductive,Electrostatic discharge protection,Antistatic property,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ STAT-KON™ Compound JK800 RTP ESD C 2580 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(MD：3.2 mm)
Shrinkage rate % ASTM D955

收缩率(TD：3.2 mm)
Shrinkage rate %

熔体质量流动速率(260℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL LNP™ STAT-KON™ Compound JK800 RTP ESD C 2580 单位
UNIT 测试方法
TEST METHOD

弯曲应力(--)
Bending stress MPa ISO 178

弯曲应力(断裂，50.0 mm 跨距)
Bending stress MPa ASTM D790

弯曲强度(屈服)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

抗张强度(屈服)
Tensile strength MPa ASTM D638

抗张强度(屈服)
Tensile strength MPa ISO 527-2/5

抗张强度(断裂)
Tensile strength MPa ASTM D638

抗张强度(断裂)
Tensile strength MPa ISO 527-2/5

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LNP™ STAT-KON™ Compound JK800 RTP ESD C 2580 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

装有测量仪表的落镖冲击(23°C，Total Energy)
Dart impact equipped with measuring instruments (23 ° C, Total Energy) J ASTM D3763

热性能
THERMAL LNP™ STAT-KON™ Compound JK800 RTP ESD C 2580 单位
UNIT 测试方法
TEST METHOD

RTI
RTI °C UL 746

RTI Elec
RTI Elec °C UL 746

RTI Imp
RTI Imp °C UL 746

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火，6.4 mm)
Hot deformation temperature ℃

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 7

维卡软化温度(--)
Vicat Softening Temp ℃ ISO 306/B120

电气性能
ELECTRICAL LNP™ STAT-KON™ Compound JK800 RTP ESD C 2580 单位
UNIT 测试方法
TEST METHOD

Static Decay - 5000V to <50V
Static Decay - 5000V to <50V msec FTMS 101B

体积电阻率
Volume resistivity ohms·cm ASTM D257

表面电阻率
Surface resistivity ohms ASTM D257

阻燃性能
FLAMMABILITY LNP™ STAT-KON™ Compound JK800 RTP ESD C 2580 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

阻燃等级(1.00 mm)
Flame retardant level

阻燃等级(1.50 mm)
Flame retardant level

加工方式

注射 LNP™ STAT-KON™ Compound JK800 RTP ESD C 2580 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

背压 MPa

螺杆转速 rpm

备注

1、5.0 mm/min

2、类型 1, 5.0 mm/min

3、1.3 mm/min

4、2.0 mm/min

5、at Yield

6、80*10*4 mm

7、速率 A (50°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注