PC，LNP™ THERMOCOMP™ Compound D351RC对比PC，LNP™ THERMOCOMP™ D351 compound物性表,价格行情_搜料

牌号信息	LNP™ THERMOCOMP™ Compound D351RC 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LNP™ THERMOCOMP™ D351 compound 物性表 PC & 沙特沙伯基础指导价格：59108.81元/吨塑料库存： 9720kg
牌号简介	LNPThermocompD351RC化合物是基于含有玻璃纤维和阻燃剂的聚碳酸酯树脂。该材料还具有高模量、平整度好、冲击性能好、无卤阻燃、PCR含量高达35%等特点。 LNP* THERMOCOMP* D351RC compound is based on Polycarbonate resin containing Glass Fiber and Flame Retardant. Added features of this material includes high modulus, good flatness, good impact performance, Non-Halogenated Flame Retardant, PCR content up to 35%.	LNP Thermocomp D351（实验级名称为extc8143）是一种基于聚碳酸酯树脂的化合物，含有玻璃纤维，阻燃剂。该材料的附加特性包括：高模量、良好的平整度、良好的延展性、无溴无氯阻燃剂。 LNP THERMOCOMP D351 (experimental grade name as EXTC8143) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good ductility, Non-Brominated & Non-Chlorinated Flame Retardant.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：	玻璃纤维	玻璃纤维
用途：	电子显示器,电气/电子应用领域
性能特点：		机械强度好-延展,无卤,阻燃 Ductility,Halogen free,Flame Characteristics
加工条件：		注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ THERMOCOMP™ Compound D351RC LNP™ THERMOCOMP™ D351 compound 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate % ASTM D995

收缩率(MD：24 hrs)
Shrinkage rate %

收缩率(TD)
Shrinkage rate % ASTM D995

收缩率(TD：24 hrs)
Shrinkage rate %

熔体质量流动速率(300℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL LNP™ THERMOCOMP™ Compound D351RC LNP™ THERMOCOMP™ D351 compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲强度(断裂，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ASTM D790

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

抗张强度(断裂)
Tensile strength (fracture) MPa ASTM D638

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度(23℃)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量(23℃)
Tensile modulus MPa ASTM D638

冲击性能
IMPACT LNP™ THERMOCOMP™ Compound D351RC LNP™ THERMOCOMP™ D351 compound 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL LNP™ THERMOCOMP™ Compound D351RC LNP™ THERMOCOMP™ D351 compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

阻燃性能
FLAMMABILITY LNP™ THERMOCOMP™ Compound D351RC LNP™ THERMOCOMP™ D351 compound 单位
UNIT 测试方法
TEST METHOD

阻燃等级(0.80 mm)
Flame retardant level UL 94

阻燃等级()
Flame retardant level V-0 UL 94

加工方式

注射 LNP™ THERMOCOMP™ Compound D351RC LNP™ THERMOCOMP™ D351 compound 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥时间 Hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

水份含量 %

注塑温度模具温度 °C

注塑温度模头温度 °C

注塑温度螺筒中部温度 °C

注塑温度螺筒前部温度 °C

注塑温度螺筒后部温度 °C

背压 MPa

螺杆转速 rpm

备注

2、5.0 mm/min

3、类型 1, 5.0 mm/min

4、1.3 mm/min

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*4 sp=62mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
备注