PA66，LubriOne™ LB6600-0002对比PA66，RTP 205 TFE 3 SI物性表,价格行情_搜料

牌号信息	LubriOne™ LB6600-0002 物性表 PA66 & 美国普立万指导价格：暂无塑料库存：缺货	RTP 205 TFE 3 SI 物性表 PA66 & 美国RTP 指导价格：暂无塑料库存：缺货
牌号简介	Lubrione润滑和耐磨化合物被专门配制成自润滑材料，提供低摩擦系数和改进的耐磨性能。润滑油化合物已被证明可以减少摩擦、噪音、振动、热积聚并提高产品的耐久性。 LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.	警告：此材料的状态为“商业：限量发行”。此材料的数据最近尚未验证。在指定此等级之前，请联系RTP公司以获取当前信息。-每个RTP公司的初步产品数据- Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.-

产品描述
厂家：	美国普立万 Polyone	美国RTP
类别：	PA66 PA66	PA66 PA66
填料：
用途：	齿轮,工业应用,滑轮,轴承,滚轴,汽车领域的应用,家电部件,消费品应用领域,印刷机零件,商务设备,传送机配件
性能特点：	机械强度好,耐候抗UV,润滑性,耐磨 Good Rigidity,Weather resistance is good,Lubricating,Good wear resistance	润滑性,防火阻燃等级HB Lubricating,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LubriOne™ LB6600-0002 RTP 205 TFE 3 SI 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

吸水率(24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate %

收缩率(MD：3.2 mm)
Shrinkage rate % ASTM D955

收缩率(TD)
Shrinkage rate %

机械性能
MECHANICAL LubriOne™ LB6600-0002 RTP 205 TFE 3 SI 单位
UNIT 测试方法
TEST METHOD

压缩强度
compressive strength MPa ASTM D695

弯曲强度
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

抗张强度(屈服)
Tensile strength (yield) MPa ASTM D638

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

摩擦系数(与金属 - 动态)
friction coefficient ASTM D1894

摩擦系数(与钢 - 动态)
friction coefficient ASTM D1894

摩擦系数(与钢 - 静态)
friction coefficient ASTM D1894

摩擦系数(动态)
friction coefficient ASTM D3702

摩擦系数(静态)
friction coefficient ASTM D3702

洛氏硬度(R 级)
Rockwell hardness ASTM D785

冲击性能
IMPACT LubriOne™ LB6600-0002 RTP 205 TFE 3 SI 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃，3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁缺口冲击强度(23°C，3.2mm，注塑成型)
Impact strength of cantilever beam notch J/m ASTM D256-A

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL LubriOne™ LB6600-0002 RTP 205 TFE 3 SI 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

阻燃性能
FLAMMABILITY LubriOne™ LB6600-0002 RTP 205 TFE 3 SI 单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame retardant level UL 94

加工方式

注射 LubriOne™ LB6600-0002 RTP 205 TFE 3 SI 单位测试方法

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大回制料比例 %

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

备注

2、类型 1, 5.1 mm/min