技术参数
物理性能
PHYSICAL
CYCOLAC™ X17 resin
CYCOLAC™ T resin
单位
UNIT
测试方法
TEST METHOD
密度
Density
g/cm³
ASTM D792
收缩率(MD)
Shrinkage rate
收缩率(MD)
Shrinkage rate
%
熔体质量流动速率(200℃，5.0kg)
Melt Flow Rate
g/10min
ASTM D1238
熔体质量流动速率(230℃，3.8kg)
Melt Flow Rate
g/10min
ASTM D1238
粘度(260°C, 1000 sec-1 )
Viscosity (260 ° C, 1000 sec-1)
poise
ASTM D 3825
粘度(260°C, 1000 sec-1)
Viscosity (260 ° C, 1000 sec-1)
poise
ASTM D 3825
机械性能
MECHANICAL
CYCOLAC™ X17 resin
CYCOLAC™ T resin
单位
UNIT
测试方法
TEST METHOD
弯曲强度(屈服)
bending strength
MPa
ASTM D790
弯曲模量
Bending modulus
MPa
ASTM D790
拉伸强度(屈服)
tensile strength
拉伸强度(屈服)
tensile strength
ASTM D638
拉伸模量
Tensile modulus
MPa
ASTM D638
洛氏硬度(R 级)
Rockwell hardness
ASTM D785
热性能
THERMAL
CYCOLAC™ X17 resin
CYCOLAC™ T resin
单位
UNIT
测试方法
TEST METHOD
导热系数
Thermal conductivity coefficient
W/m/℃
ASTM C 177
热变形温度(0.45 MPa，3.2 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(0.45 MPa，6.4 mm)
Hot deformation temperature
ASTM D648
热变形温度(1.8 MPa，3.2 mm)
Hot deformation temperature
ASTM D648
热变形温度(1.8 MPa，3.2 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa，6.4 mm)
Hot deformation temperature
℃
ASTM D648
相对温度指数(冲击机械性能)
Relative temperature index
℃
UL 746B
相对温度指数(电气性能)
Relative temperature index
℃
UL 746B
相对温度指数(非机械冲击性能)
Relative temperature index
℃
UL 746B
线性膨胀系数(-40°C~ 40°C，MD)
Linear expansion coefficient (-40 ° C~40 ° C, MD)
1/°C
ASTM E 831
线性膨胀系数(-40°C~40°C，MD)
Linear expansion coefficient (-40 ° C~40 ° C, MD)
1/℃
ASTM E 831
维卡软化温度
Vicat Softening Temp
℃
冲击性能
IMPACT
CYCOLAC™ X17 resin
CYCOLAC™ T resin
单位
UNIT
测试方法
TEST METHOD
悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
电气性能
ELECTRICAL
CYCOLAC™ X17 resin
CYCOLAC™ T resin
单位
UNIT
测试方法
TEST METHOD
热丝引燃{PLC
PLC Code
UL 746A
热丝引燃{PLC}
PLC Cod
UL 746A
相比漏电起痕指数
Compared to the leakage tracing index
PLC Code
UL 746A
耐电弧性(钨丝)
Arc resistance
PLC Code
ASTM D495
高电压电弧起痕速率 {PLC
High voltage arc marking rate {PLC
PLC Code
UL 746A
高电压电弧起痕速率 {PLC}
High voltage arc marking rate {PLC}
PLC Cod
UL 746A
高电流电弧引燃，表面{PLC
High current arc ignition, surface {PLC
PLC Code
UL 746A
高电流电弧引燃，表面{PLC}
High current arc ignition, surface {PLC}
PLC Cod
UL 746A
阻燃性能
FLAMMABILITY
CYCOLAC™ X17 resin
CYCOLAC™ T resin
单位
UNIT
测试方法
TEST METHOD
CSA
CSA
File No
CSA LISTED
极限氧指数
Extreme oxygen index
%
ASTM D2863
紫外线,水暴露/浸没
UV rays, water exposure/immersion
UL 746C
阻燃等级(1.47 mm)
Flame retardant level
UL 94