技术参数
物理性能
PHYSICAL
CYCOLAC™ MGX53GP resin
LG ABS XR404
单位
UNIT
测试方法
TEST METHOD
密度
Density
ASTM D792
密度
Density
g/cm³
ASTM D792
密度
Density
g/cm³
ISO 1183
收缩率(MD)
Shrinkage rate
收缩率(MD)
Shrinkage rate
%
收缩率(MD：3.2 mm)
Shrinkage rate
%
ASTM D955
收缩率(MD：3.2 mm)
Shrinkage rate
%
ISO 294-4
熔体体积流动速率(220℃，10 kg)
Melt Volume Rate
cm³/10min
ISO 1133
熔体质量流动速率(220℃，10.0kg)
Melt Flow Rate
g/10min
ASTM D1238
熔体质量流动速率(230℃，3.8kg)
Melt Flow Rate
g/10min
ASTM D792
机械性能
MECHANICAL
CYCOLAC™ MGX53GP resin
LG ABS XR404
单位
UNIT
测试方法
TEST METHOD
弯曲强度(3.20 mm)
bending strength
MPa
ASTM D790
弯曲强度(屈服)
bending strength
MPa
ASTM D790
弯曲模量
Bending modulus
MPa
ASTM D790
弯曲模量(3.20 mm)
Bending modulus
MPa
ASTM D790
拉伸应变(屈服)
Tensile strain
%
ASTM D638
拉伸应变(断裂)
Tensile strain
%
ASTM D638
拉伸应变(断裂，3.20 mm)
Tensile strain
%
ASTM D638
拉伸强度(屈服)
tensile strength
MPa
ASTM D638
拉伸强度(屈服)
tensile strength
MPa
ISO 527-2/50
拉伸强度(屈服，3.20 mm)
tensile strength
MPa
ASTM D638
拉伸强度(断裂)
tensile strength
MPa
ASTM D638
拉伸模量
Tensile modulus
MPa
ASTM D638
拉伸模量
Tensile modulus
MPa
ISO 527-1-2
洛氏硬度(R 级)
Rockwell hardness
ASTM D785
热性能
THERMAL
CYCOLAC™ MGX53GP resin
LG ABS XR404
单位
UNIT
测试方法
TEST METHOD
热变形温度(0.45 MPa，3.2 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(0.45 MPa，未退火，4.0 mm)
Hot deformation temperature
℃
ISO 75-2/Be
热变形温度(0.45 MPa，未退火，6.4 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa，3.2 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa，未退火，4.0 mm)
Hot deformation temperature
℃
ISO 75-2/Ae
热变形温度(1.8 MPa，未退火，6.4 mm)
Hot deformation temperature
℃
ASTM D648
相对温度指数(冲击机械性能)
Relative temperature index
℃
UL 746
相对温度指数(冲击机械性能)
Relative temperature index
℃
UL 746B
相对温度指数(强度机械性能)
Relative temperature index
℃
UL 746
相对温度指数(电气性能)
Relative temperature index
℃
UL 746
相对温度指数(电气性能)
Relative temperature index
℃
UL 746B
相对温度指数(非机械冲击性能)
Relative temperature index
℃
UL 746B
线性热膨胀系数(MD：23~60℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(TD：23~60℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性膨胀系数(-40°C~40°C)(MD)
Linear expansion coefficient (-40 ° C~40 ° C)
1/℃
ASTM E 831
线性膨胀系数(-40°C~40°C)(TD)
Linear expansion coefficient (-40 ° C~40 ° C)
1/℃
ASTM E 831
维卡软化温度
Vicat Softening Temp
℃
ASTM D1525
维卡软化温度(B50)
Vicat Softening Temp
℃
ISO 306
冲击性能
IMPACT
CYCOLAC™ MGX53GP resin
LG ABS XR404
单位
UNIT
测试方法
TEST METHOD
仪器冲击能量峰值(23°C)
Instrument impact energy peak (23 ° C)
J
ASTM D 3763
悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(-30℃，3.2mm)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(-30℃，6.4mm)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃，6.4mm)
Impact strength of cantilever beam notch
J/m
ASTM D256
简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
电气性能
ELECTRICAL
CYCOLAC™ MGX53GP resin
LG ABS XR404
单位
UNIT
测试方法
TEST METHOD
介电强度(23 ℃，1 mm)
Dielectric strength
kV/mm
ASTM D149
体积电阻率(23℃)
Volume resistivity
ohms·cm
ASTM D257
热丝引燃{PLC}
PLC Code
UL 746A
相比漏电起痕指数
Compared to the leakage tracing index
PLC Code
UL 746A
耐电弧性
Arc resistance
ASTM D495
高电流电弧引燃，表面{PLC}
High current arc ignition, surface {PLC}
PLC Code
UL 746A
阻燃性能
FLAMMABILITY
CYCOLAC™ MGX53GP resin
LG ABS XR404
单位
UNIT
测试方法
TEST METHOD
阻燃等级
Flame retardant level
UL 94
阻燃等级(1.49 mm)
Flame retardant level
UL 94
高亮区别
隐藏相同